SCHEDA TECNICA - TECHNICAL INFORMATION - TECHNISCHE INFORMATIONEN - INFORMATIONS TECHNIQUES
292 AIR DRYING 2:1 CLEAR COAT FAST AIR DRYING CLEAR COAT
Compatible with all standard bases available. Suitable for all double-layer, metallic, pearl and pastel coatings formulated for the automotive industry. Suitable both for painting of 3-4 panels and small areas (spot repairs). For extended surfaces use FULL CAR retardant additive. Before the application of 292 AIR DRYING CLEAR COAT, opacify the old finishes that must be covered and degrease them using a water based silicone-remover degreaser. As with all paint systems, best results are obtained if the clear coat is sprayed at a temperature of 20-25°C. It is also recommended to bring the surface to at least 15°C before proceeding to the application of the product. Low temperatures make application, absorption and levelling very difficult. It is very important to carefully follow the application procedure to avoid too thick layers and consequent delays in drying process. Is particularly important to ensure that opaque basecoat is completely dry, that is does not contain traces of moisture, water or solvent before applying the clear coat.
292.1000.12 293.0500.12
VOC
Codice prodotto Code - Codigo
292.1000.12 Prodotto 293.0500.12 Catalizzatore/Hard.
NUMERO MANI Number of coats Passes
NATURA PRODOTTO Nature of product Nature du produit Naturaleza de producto Contenuto solido Solid content
Resina Specifica Modified specific resin
SPESSORE FILM SECCO 55 microns Dry film thickness APPASSIMENTO Flash time Evaporation
3‘-6‘ minutes (2’-4’ mins. summer time) Tra una mano e l'altra Between the first and second coat
FUORI POLVERE (20°C) Dust free (20°C)
15‘-20‘
V.O.C. PRODOTTO CH Product V.O.C. CH
SECCO AL TATTO(20°C) Tack free (20°C)
2-4 h
Colore Trasparente Colour • Coleur • Color Transparent • Transparent • Transparente
PRONTO AL MONTAGGIO 2-4 h Dry to assemble
V.O.C. PRODOTTO Pronto all'uso Product V.O.C. Ready to use
Peso Specifico Specific Gravity Poid specific Peso specifigo RAPPORTO MISCELA Mixing ratio A B C Proportion de melange
g/L
PRODOTTO Product Produit Producto CATALIZZATORE Hardener Durcisseur Endurecedor DILUENTE Thinner Diluant Disolvente
A B C
POT-LIFE Pot-life (20°C)
VOC (2004/42/CE IIB) ------------------------------------(e-840 g/L max) cont. 578 g/L
TEMPO ESSICAZIONE Through drying • Evaporation (68°F)(20°C) Aria (140°F)(60°C) Forno CONSERVABILITA' Ageing Stockage
992 ± 50 g / l
Ratio = 2:1 Asta graduata
292 Clear Trasparente 293 Hardener Catalizzatore 898 AD Thinner Diluente
VOLUME% PESO (g) Volume Weight 100
100
50
50
0
Roto orbitale secco Flat bed sander dry Ponceuse vibrante à sec Cart. manuale bagnato Sanding by hand wet Ponçage à la main eau
0
ADDITIVI Additives
2-2,5 h
PISTOLA A CADUTA
1,2 - 1,4 mm.
PISTOLA AD ASPIRAZIONE
-
PRESSIONE ARIA (Bar)
3 - 3,5
Gravity feed spray gun Pistolet à gravité Suction feed spray gun Pistolet à godet suspendu Air pressure (Bar) Pression
60' Air 10' Spray Booth 12 mesi in luogo fresco e asciutto 12 months in a cool and dry place 12 mons dans un endroit frais et sec
Roto orbitale bagnato Flat bed sander wet Ponceuse vibrante à l'eau
Pezzi Cartone Pieces/carton box No. par carton Envases por caja Cartoni Pallet Carton box / Pallet Eur 80 x 120 cm
VISCOSITA' APPLICAZIONE 18±2" Coppa Ford Ø 4 a 20°C Spraying viscosity Viscosité d'application
ATM
2 mani piene 2 full coat
!
1 L clear 500ml Hardener
12 pezzi/pieces/boîtes 12 Cat. / hard./durcis.
1 L 60 cartoni / carton boxes
We do not recommend drying tunnel with infrared. Respect the drying times between each coat. Polishing after 2 hours of air drying at 20°C or after 30’ with oven drying after 10’ at 60°C.
we assume no responsibility for results obtained, as conditions and usage are beyond our control.
Data Sheet Pag. 141 PRODOTTI CHIMICI PER LA CARROZZERIA, L'INDUSTRIA E LA NAUTICA ALLCHEM S.r.l. Via Azzano S. Paolo, 32/C - 24050 GRASSOBBIO (BG) ITALY - Tel. +39-035 525 616 - Fax +39-035 526 199 - www.allchem.it - info@
I dati contenuti nella presente scheda si basano sulle nostre conoscenze ed esperienze. Questi non sono impegnativi poiché a causa della diversità dei materiali presenti sul mercato ed al fatto che le condizioni di applicazione sfuggono al nostro