Electrodes Welding Wire
WELDING DUCTIL - ELECTRODES FOR THE WELDING OF CARBON STEEL AND LOW-ALLOY STEEL
DUCTIL SUPERBAZ Basic electrodes with >50% carbonates coating and iron dust add-on for a good yield. Ensures a reduced content of hydrogen diffused in the metal, thus conferring a good cold crack strength. Recommended for high-quality steel welding, for metal structures subjected to dynamic and static stress. Steadily burning arc, low spattering, the slag covers well the welding line and it is easy-to-clean after the solidification and the cooling of the welding line, fine aspect - specific to the base-coated electrodes welding, respectively, slightly scaly. Code
Product name
540004 540005 540006 540009 540016 540019 540030
DUCTIL Superbaz 2.5x350mm DUCTIL Superbaz 3.25x450mm DUCTIL Superbaz 4x450mm DUCTIL Superbaz 3.25x350mm DUCTIL Superbaz 2x300mm DUCTIL Superbaz 4x350mm DUCTIL Superbaz 5x450mm
SO SO SO
Content
Boxes/carton
4.0 kg 5.5 kg 5.5 kg 4.0 kg 3.5 kg 4.0 kg 5.5 kg
3 3 3 3 3 3 3
Standards and classifications: SR EN 499
AWS A 5.1
EN ISO 2560-A
E 42 4 B 42 H5
E 7018
E 42 4 B 42 H5
Welding positions: Welding in all positions, except for vertical downward Current type: DC (+); AC Chemical composition of the welding seam: C%
Mn %
Si %
P%
S%
S%+P%
0.05-0.9
0.80-1.20
0.25-0.60
max. 0.025
max. 0.015
max. 0.04
Mechanical features of the deposited metal: Flow limit N/mm2
Breaking strength N/mm2
Elongation A 5d %
>430
510-640
min. 24
SO = VALID BY SPECIAL ORDER
196
www.temad.ro
Kv J +20°C
0°C
-20°C
-40°C
min. 140
min. 100
min. 80
min. 47
DUCTIL - FULL WIRE FOR THE WELDING OF CARBON STEEL
FINE RUTILE DUCTIL SUPERTIT
DUCTIL FILCORD C
Rutile-coated electrodes, comprising >50% titanium dioxide, of medium thickness. Recommended for the welding of light metal structures, subjected to static stress, of thin metal sheets, of the root layer. Very good energizing and easy re-energizing, steady arc, very low spattering both with direct current as well as with alternating current, aesthetic aspect of the weld line, very good slag chipping. Code
Product name
540000 540001 540002 540008 540017 540021 540036 540039
Fine Rutile DUCTIL Supertit 2.5x350mm Fine Rutile DUCTIL Supertit 3.25x350mm Fine Rutile DUCTIL Supertit 4x450mm Fine Rutile DUCTIL Supertit 3.25x350mm Fine Rutile DUCTIL Supertit 2x350mm Fine Rutile DUCTIL Supertit 2x300mm Fine Rutile DUCTIL Supertit 4x350mm Fine Rutile DUCTIL Supertit 2.5x300mm
SO
SO SO SO SO
Content
Boxes/carton
4.5 kg 5.8 kg 5.8 kg 4.5 kg 4.5 kg 3.8 kg 4.5 kg 3.8 kg
3 3 3 3 3 3 3 3
Standards and classifications: SR EN 499
AWS A 5.1
E 38 0 R 12
E 6013
Full copper wire for welding in shielding gas environment. Recommended for the welding in one or in several strikes of non-alloy steel, with tensile breaking strength up to 560N/m². Steady electric arc, low spattering, aesthetical line. Used for welding in shipbuilding, boilers, in the petrochemical industry, automotive industry, railroad constructions, manufacturing of pipes and in household applications. Code
Product name Content Boxes/carton 540053 DUCTIL FILCORD-C K300SS 0.8mm code 2601938 SO 16 kg 1 540054 DUCTIL FILCORD K300SS 1.0mm code 2601946 SO 16 kg 1 540059 DUCTIL FILCORD-C K300SS 1.2mm code 2601963 SO 16 kg 1
Standards and classifications: AWS A 5.18-93
EN ISO 14341-A
EN ISO 14341-A
ER70S-6
G423 C G3Si1
G424 M G3Si1
Welding positions: Welding in all positions, except for vertical downward Current type: DC +
Welding positions: Welding in all positions, except for vertical downward
Gas: Ar / CO2 - Ar / CO2 / O2 - CO2
Current type: DC (-); AC
Chemical Analysis of Wire:
Idle running tension = min. 50V
Chemical composition of the welding seam: C%
Mn %
Si %
P%
S%
0.06-0.10
0.30-0.60
0.20-0.50
max. 0.03
max. 0.03
Mechanical features of the deposited metal: Flow limit N/mm2
Breaking strength N/mm2
Elongation A 5d %
430-470
490-600
min. 24
Kv J
M2, M3, C1 (EN439)
C%
Mn %
Si %
S%
P%
Cu %
0.06-0.13
1.3-1.6
0.70-1.00
≤ 0.025
≤ 0.025
0.25
Mechanical features: GAS
Thermal treatment
Rn N/mm2
Rs N/mm2
E % 5d
Kv J -30°C
Kv J -40°C
Ar/CO2 (M21)
Welded state
510-560
≤ 430
≤ 24
≤ 70
≤ 47
CO2
Welded state
510-560
≤ 430
≤ 24
≤ 47
+0°C min. 47
email: office@temad.ro
197
WELDING DUCTIL - ELECTRODES FOR THE WELDING OF STAINLESS STEEL
DUCTIL STARINOX 308L
RUTILE CEMONT SPEEDARC
Semi-basic coating electrodes. Designed for the welding of austenitic stainless steel, type AISI 302, 304, 304L. Good resistance to inter-crystalline corrosion. Very good welding behaviour, non-spattering, easy-to-remove slag. Code
Product name
540007 540010
DUCTIL Starinox 308L 3.25x350mm DUCTIL Starinox 308L 2.5x300mm
SO
Rutile coating electrodes of medium thickness, specially recommended for the welding of light metal structures, of thin carbon steel sheets. Recommended for the welding of non-alloy steel with a maximum carbon content of 0.25% for light structures, used for temperatures of down to 0˚C.
Content
Boxes/carton
4.5 kg 3.7 kg
3 3
Standards and classifications: SR EN 1600
AWS A 5.4
E 19 9 L R 1 2
E 308L - 16
CEMONT - ELECTRODES FOR THE WELDING OF CARBON STEEL AND LOW-ALLOY STEEL
Code
Product name
542000 542001 542002 542003 542004 542005
Rutile CEMONT Speedarc 2.5x350mm Rutile CEMONT Speedarc 3.25x450mm Rutile CEMONT Speedarc 3.25x350mm SO Rutile CEMONT Speedarc 2x300mm SO Rutile CEMONT Speedarc 4x450mm SO Rutile CEMONT Speedarc 5x450mm
Content
Boxes/carton
4.5 kg 5.8 kg 4.5 kg 3.8 kg 5.8 kg 5.8 kg
3 3 3 3 3 3
Welding positions: Welding in all positions, except for vertical downward. Current type: DC (+); AC Chemical composition of the welding seam: C% max 0.04
Mn %
Si %
0.50-1.00 0.60-0.90
Cr %
Ni %
P%
S%
FN (WRC-92)
18.0-21.0
9.0-11.0
max. 0.030
max. 0.020
5-10
Mechanical features of the deposited metal: Flow limit N/mm2
Breaking strength N/mm2
Elongation A 4d %
min. 350
min. 520
min. 35
Kv J +20°C min. 60
BASIC CEMONT RESISTARC Basic coating electrodes containing iron dust, designed for the structures strongly subjected to static and dynamic tension and for the thick sections of low-alloy steel, at temperatures of down to -40˚C. Recommended for the welding of pressurized containers, inclusively for the chemical and petrochemical industry, shipbuilding, welding of pipes, building of marine platforms.
198
www.temad.ro
Code
Product name
542100 542101 542102 542103
Basic CEMONT Resistarc 2.5x350mm Basic CEMONT Resistarc 3.25x450mm Basic CEMONT Resistarc 4x450mm Basic CEMONT Resistarc 3.25x350mm
SO
Content
Boxes/carton
4.0 kg 5.5 kg 5.5 kg 4.0 kg
3 3 3 3
Electrodes
WELDING ZIKA - ELECTRODES FOR THE WELDING OF CARBON STEEL AND LOW-ALLOY STEEL
Standards and classifications:
RUTILE ZIKA11
AWS/ASME SFA A5.1
DIN 1913
BS 639
EN 499
E 6013
E 43 22 RR6
E 43 22 RR 22
E 42 0 RR 12
Welding positions:
Rutile electrodes with dense coating, suitable for the welding of multiple surfaces: badly prepared surfaces, covered in old paint, rust, as well as for welding metal sheets of different thickness. Recommended for non-alloy steel in constructions, for steel pipes and for cast steel. Code
Product name
545000 545001 545002
RUTILE ZIKA11 2.5x350mm Z11-25E RUTILE ZIKA11 3.25x350mm Z11-32E RUTILE ZIKA11 3.25x450mm Z11-32-8E
Content
Boxes/carton
5.0 kg 5.0 kg 6.0 kg
3 3 3
Current type:
=–
~ (Uo: 50 V)
Chemical composition of the welding seam: C%
Mn %
Si %
0.08
0.50
0.25
Mechanical features of the deposited metal: Flow limit 0.2 [MPa]
Breaking strength [MPa]
Elongation %
Force [ISO-V]
440
520
26
70 J at 0°C
Standards and classifications:
BASIC ZIKA4 Basic electrodes with low content of hydrogen and high ductility. Suitable for the welding of construction steel. Good aspect of welding line. Good impact resistance at -30˚C temperatures. Suitable for the welding of steel structures, boilers or pressurized containers, steel pipes, high-temperature steel, fine-grained steel and shipbuilding steel.
AWS/ASME SFA A5.1
DIN 1913
BS 639
EN 499
E 7018
E 51 44 B10 H5
E 51 44 B 26 H
E 46 3 B 32 H5
Welding positions:
Current type:
=+
~ (Uo: 70 V)
Chemical composition of the welding seam: C%
Mn %
Si %
0.08
1.00
0.60
Mechanical features of the deposited metal: Code
Product name
545050 545051 545052
BASIC ZIKA4 2.5x350mm Z4-25E BASIC ZIKA4 3.25x350mm Z4-32E-6E BASIC ZIKA4 3.25x450mm Z4-32E
Content
Boxes/carton
4.5 kg 4.5 kg 6.0 kg
3 3 3
SO SO SO
SO = VALID BY SPECIAL ORDER
200
www.temad.ro
Flow limit 0.2 [MPa]
Breaking strength [MPa]
Elongation %
Force [ISO-V]
480
570
26
130 J at -20°C 100 J at -30°C