Chromium Flux-Cored Wire Designed to Combat Both Grinding and Gouging Wear
5306 FW- HIGH CHROM
WIRE • Superior resistance to grinding and gouging abrasion with light impact at elevated temperatures • Open-Arc wire for convenient, gas-free use in the field or shop • High chomium Open-Arc wire for defect-free weldability in adverse conditions • Optimal High chromium content imparts excellent oxidation resistance • Small diameter wires excellent for use with 110v welding machine
TYPICAL APPLICATIONS:
DESCRIPTION: Formulated to combat grinding and gouging abrasion from two- and three-body sliding abrasion, 5306 FW HighChromium forms precise, smooth deposits easily achieved with conventional low-voltage machines. The chromium content takes a duel role in forming carbides to combat wear while protecting the weld metal from high temperature oxidation. The ability to be applied with or without shielding gas makes 5306 FW versatile as well as an outstanding performer in any number of field and shop applications.
TECHNICAL DATA: Typical Hardness: 56-60 HRC Service temperature: 1100°F max Finishing: Grind Only Number of passes: 3-pass maximum Recommended Polarity: DCEP (+)
• Earthmoving / Civil Engineering Industries: Ripper shanks, rock rakes, bucket lips and adapters, dragline clevises • Crushing & Grinding: Rotor and impeller bars, stripper bars grizzly bars, cone crusher rolls • Cement Industry: Drag chain links, cement chutes, crusher hammers and bowls • Steel Industry: Coke pusher shoes, clinker belt links, skip car lips, ore discharge chutes
PACKAGING & SIZES: 0.035” (0.9mm) 10 lbs. (4.5kg) 8” Spool 0.045” (1.2mm) 33 lbs. (15kg) 12” Spool 1/16” (1.6mm) 33 lbs. (15kg) 12” Spool
PARAMETERS AMPS
VOLTS
STICK OUT
.035" (.9mm)
90-150
17-22
1/2"-3/4"
.045" (1.2mm)
180-200
24-28
1/2"-3/4"
1/16" (1.6mm)
190-250
25-28
5/8"-7/8"
EUTECTIC FINE WIRE ECONO-LINE FW-Manganese Steel 5022FW
A high manganese wire for combating impact plus abrasion and high compression loading. Deposits have excellent work-hardening properties.
HRC (WH 45-50)
* Latch bars * Crusher points * Rail frogs
FW-Chromium Iron 5716FW
A specially formulated hardfacing wire for combating abrasion, particularly when accompanied by moderate to heavy impact.
HRC 45-50
* Bucket lips * Dozer blades * Cage Crushers
FW-High Chromium 5306FW
Formulated to combat both grinding and gouging abrasion. Deposits can tolerate light impact but are best for two-body sliding abrasion.
HRC 56-60
* Cone crusher rolls * Drag chain links * Ripper Shanks
FW-Mixed Carbide 5256FW
A hardfacing wire with enhanced abrasion and high temperature wear resistance. Properties are maintained up to 1200 °F.
HRC 55-60
* Kiln flights * Feeder screws * Coke pusher shoes
FW-Tung Carbide M56FW
A hardfacing wire with a high volume of tungsten carbides. The weld deposit offers maximum wear resistance to abrasion and erosion.
HRC 59-62
* Rock drill bits * Screw conveyers * Mixers
YOUR RESOURCE FOR PROTECTION, REPAIR AND JOINING SOLUTIONS Eutectic Corporation N94 W14355 Garwin Mace Drive Menomonee Falls, WI 53051 USA P 800-558-8524 • F 262-255-5542 www.eutectic.com
Eutectic Services 12300 Carmen Avenue Milwaukee, WI 53225 USA P 800-558-8524 • F 262-255-5542
Statement of Liability: Due to variations inherent in specific applications, the technical information contained herein, including any information as to suggested product applications or results, is presented without representation or warranty, expressed or implied. Without limitation, there are no warranties of merchantability or of fitness for a particular purpose. Each process and application must be fully evaluated by the user in all respects, including suitability, compliance with applicable law and non-infringement of the rights of others, and Eutectic Corporation and its affiliates shall have no liability in respect thereof. 5306 07-15 © 2008, Eutectic Corporation, ® Reg. T.M., Printed in the U.S.A.