Variation in Wear Rate with change in Coating thickness is shown in graph 4.1.
Graph 4.1 Wear Rate Vs Coating thickness
Load and Temperature are set aside as constants and Coating thickness changed between 50 to 70µm. Studied Graph 4.1, it has been observed that as Coating thickness increases from 50 to 70µm wear decreases, also it has been observed that, most affected area and the rate of change of Wear Rate is drastic in therange of 55 to 65 µm since selected same level of factor.