Type 2 Dental Stones

HIRO PLASTER® Type 2 natural dental plaster.

Type 2 natural dental plaster for fixed and mobile restorations, study models for consultations and orthodontics. • Low expansion; • Quick setting; • Pleasant mixing; • Creamy consistency.

Compressive Strength after 1 hr: • Compressive Strength [MPa; N/mm2] - 16 MPa (2320psi) Compressive Strength Dry: • Compressive Strength [MPa; N/mm2] - 29 MPa (4205psi) ISO 6873, Data referred to 45ml/100g

Packaging: 20kg

• Water/Powder Ratio: 45÷50ml/100g • Setting Time: max.15 min. • Expansion after 2 h: ≤0.20 %

Color: White

HIRO ARTI®

Type 2 articulating dental stone. Type 2 articulating dental stone. Used for mounting of models for articulation and bite registration. • Very short setting time; • Perfect adhesion to all dental stones; • Excellent stacking properties; • Extremely low expansion to maintain the occlusion unaltered; • Smooth and creamy mix; • Also excellent for bite registration. Compressive Strength after 1 hr: • Compressive Strength [MPa; N/mm2] - 19 MPa (2755psi) Compressive Strength Dry: • Compressive Strength [MPa; N/mm2] - 31 MPa (4495psi) • ISO 6873, Data for 45ml/100g

Packaging: 4.5kg | 20kg

www.mutsumidental.eu

• Water/Powder Ratio: 45ml/100g • Setting Time: 3-4 min. • Expansion after 2 h: ≤ 0.05%

Color: White

3


Type 3 Dental Stones

HIRO STONE® Type 3 natural dental stone.

Type 3 natural dental stone. Used for study and working models. • Low expansion; • Quick setting; • Fast removal from the mould; • Smooth and creamy mix; • Increased hardness even after one hour.

Compressive Strength after 1 hr: • Compressive Strength [MPa; N/mm2] - 31 MPa (5946psi) Compressive Strength Dry: • Compressive Strength [MPa; N/mm2] - 55 MPa (7105psi) ISO 6873, Data referred to 30ml/100g

Packaging: 4.5kg | 20kg

• Water/Powder Ratio: 30÷32ml/100g • Setting Time: 10 - 13 min. • Expansion after 2 h: ≤ 0.18%

Color:

Sunglow Yellow White Sky Blue

HIRO STONE PLUS® Type 3 enhanced synthetic dental stone.

Type 3 enhanced synthetic dental stone with an excellent detail reproduction, ideal choice for study models, working models and flasking procedures. Ideally suited for use with Hiro Hard Rock®, Hiro Rock®, EdoRock Implant®, Edo Premium Stone®, EdoRock Max®. • High strength, reduces breakage and chipping; • Quick setting; • Fast removal from the mould; • Compatible with a wide range of impression materials; • Dense and homogenous consistency; • Smooth consistency and pleasant mixing; • Medium expansion. Compressive Strength after 1 hr: • Compressive Strength [MPa; N/mm2] - 41 MPa (5946psi) Compressive Strength Dry: • Compressive Strength [MPa; N/mm2] - 79 MPa (11457psi) ISO 6873, Data referred to 24ml/100g

Packaging:

2.5kg | 5kg | 10kg | 20kg

4

• Water/Powder Ratio: 23-24ml/100g • Setting Time: 10 - 13 min. • Expansion after 2 h: ≤ 0.16%

Color:

Pistachio GreenSky Blue Sunglow YellowCocktail Pink

www.mutsumidental.eu


Type 3 Dental Stones

HIRO ARTI PLUS® Type 3 articulating dental stone.

Type 3 articulating dental stone. Used for mounting of models for articulation and bite registration. • THIXOTROPIC • Perfect adhesion to all dental stones; • Excellent stacking properties; • Extremely low expansion to maintain the occlusion unaltered; • Smooth and creamy mix; • Also excellent for bite registration; • Dimensional stability • Optimal setting time Compressive Strength after 1 hr: • Compressive Strength [MPa; N/mm2] - 34 MPa (4931psi) Compressive Strength Dry: • Compressive Strength [MPa; N/mm2] - 64 MPa (9282psi) ISO 6873, Data referred to 24ml/100g

Packaging:

2.5kg | 5kg | 10kg | 20kg

• Water/Powder Ratio: 23-24ml/100g • Setting Time: 5-6 min. • Expansion after 2 h: ≤ 0.05%

Color: White

HIRO ORTHO® Type 3 synthetic dental stone.

Type 3 synthetic dental stone of super white color for orthodontics, denture repairs - study models, working models and antagonist models. Made especially with the orthodontist in mind. • Short setting time; • Fast removal from the mould; • Compatible with a wide range of impression materials; • Dense and homogenous consistency; • Smooth and creamy mix.

Compressive Strength after 1 hr: • Compressive Strength [MPa; N/mm2] - 40 MPa (5800psi) Compressive Strength Dry: • Compressive Strength [MPa; N/mm2] - 77 MPa (11165psi) ISO 6873, Data referred to 23ml/100g

Packaging:

2.5kg | 5kg | 10kg | 20kg

www.mutsumidental.eu

• Water/Powder Ratio: 23ml/100g • Setting Time: 10 - 13 min. • Expansion after 2 h: ≤ 0.11%

Color: White

5


Type 4 Dental Stones

HIRO DIE STONE® Type 4 modified synthetic dental stone.

Type 4 modified synthetic dental stone with high strength, consisting of a blend of refined alpha hemihydrates and special resin. · Top price-performance ratio; · Thixotropic; · Exceptional hardness; · Extreme easy processing, smooth and creamy mixing; · Dimensional stability; · Glossy surface; · Low expansion.

Compressive Strength after 1 hr: • Compressive Strength [MPa; N/mm2] - 46MPa (6670psi) Compressive Strength Dry: • Compressive Strength [MPa; N/mm2] - 83MPa (12035psi) ISO 6873, Data referred to 23ml/100 gr.

Packaging:

• Water/Powder Ratio: 22 - 23ml/100g • Setting Time: 10-13 min. • Expansion after 2h/24h: ≤ 0.11% / ≤ 0.15%

Color:

2.5kg | 5kg | 10kg | 20kg

Sunglow Yellow Golden Brown

HIRO BASE STONE® Hiro Base Stone® has a water-like flow

Hiro Base Stone® has a water-like flow with only 25ml of water for free-flow around model pins without air bubbles. The stable & low expansion is perfectly matched to be the optimal support to EdoRock Max®, Edo Premium Stone®, Hiro Hard Rock®, Hiro Rock®, EdoRock Implant®, Hiro Die Stone®. • Short setting time; • Fast removal from the mould. FLOWABLE > Compressive Strength after 1 hr: • Compressive Strength [MPa; N/mm2] - 37 MPa (5366psi) Compressive Strength Dry: • Compressive Strength [MPa; N/mm2] - 71 MPa (10297psi) ISO 6873, Data referred to 24ml/100g

FLOWABLE • Water/Powder Ratio: 23-24 ml/100g • Setting Time: 10 - 13 min. • Expansion after 2h/24h: ≤ 0.06% / ≤ 0.08%

THIXOTROPIC > Compressive Strength after 1 hr: • Compressive Strength [MPa; N/mm2] - 41 MPa (5945psi) Compressive Strength Dry: • Compressive Strength [MPa; N/mm2] - 79 MPa (11455psi) ISO 6873, Data referred to 24ml/100g

THIXOTROPIC • Water/Powder Ratio: 19-20 ml/100g • Setting Time: 10 - 13 min. • Expansion after 2h/24h: ≤ 0.08% / ≤ 0.1%

Packaging:

2.5kg | 5kg | 10kg | 20kg

6

Color:

Denim BluePlum PurpleForest Green Fuchsia.

www.mutsumidental.eu


Type 4 Dental Stones

HIRO ROCK®

Type 4 modified synthetic dental die stone with high strength. Type 4 modified synthetic dental die stone with high strength, consisting of a blend of refined selected alpha hemihydrates and special resin, for implant work, sectioned, master and static models, all kinds of prosthetics with high precision etc. • Top price-performance ratio; • Thixotropic • Exceptional hardness; • Extreme easy processing, smooth and creamy mixing; • Dimensional stability; • It can be scanned with several scanning systems; • Glossy surface • Low expansion. Compressive Strength after 1 hr: • Compressive Strength [MPa; N/mm2] - 50MPa (7251psi) Compressive Strength Dry: • Compressive Strength [MPa; N/mm2] - 89MPa (12908psi) ISO 6873, Data referred to 21ml/100g

Packaging:

2.5kg | 5kg | 10kg | 20kg

• Water/Powder Ratio: 21ml/100g • Setting Time: 10 - 13 min. • Expansion after 2h / 24h: ≤ 0.1% / ≤ 0.12%

Color:

Sunglow YellowGolden Brown Pistachio Green

HIRO HARD ROCK®

Type 4 modified synthetic dental die stone with high strength. Type 4 modified synthetic dental die stone with high strength, consisting of a blend of refined selected alpha hemihydrates and special resin, perfect for implant work, sectioned and master models, all kinds of prosthetics with high precision, inlay onlay etc. • Thixotropic • High innitial compression strength, resists chipping and splintering • Low expansion • Can be scanned with several scanning systems • Dimensional stability and glossy surface • Smooth and creamy mix • Glossy surface • Ideal also for plastic basing systems • Ideal for CAD/CAM or other accuracy required purposes Compressive Strength after 1 hr: • Compressive Strength [MPa; N/mm2] - 55MPa (=7977psi) Compressive Strength Dry: • Compressive Strength [MPa; N/mm2] - 99MPa (14358psi) ISO 6873, Data referred to 20ml/100g

Packaging:

2.5kg | 5kg | 10kg | 20kg

www.mutsumidental.eu

• Water/Powder Ratio: 20ml/100g • Setting Time: 10 - 13 min. • Expansion after 2h/24h: ≤ 0.08 % / ≤ 0.1

Color:

Golden BrownVanilla Yellow Pistachio Green

7


Type 4 Dental Stones

EdoRock IMPLANT®

Type 4 Synthetic modified dental hard stone for implant work and all working models by DT Gabriel Gherman EdoRock Implant produces exact and detailed models with superior strength, high dimensional stability and remarkable precision. • Minimized, uniform and steady expansion. • Chipping during the trimming process does NOT occur. • Superior compatibility with impression materials. • Immediate setting. Easy mixing and excellent thixotropy Easier mixing, better thixotropy and a wider water/ powder ratio range are achieved by applying the best particle distribution. Superior quality performance lasts for a long time.

Accurate reproduction of details Expansion rate (%)

Expansion Rate v.s. Time 0,1

Mounted

0,06 0,05 0,02 0

1

2

3

4

5

6

7

Elapsed Time (hours)

8

24

Smooth works after setting With the high strength of the dental models after setting, you can now work more smoothly on them. Less shaving when waxing up is also attained.

Compressive Strength after 1 hr: • Compressive Strength [MPa; N/mm2] - 59MPa (8555psi) Compressive Strength Dry: • Compressive Strength [MPa; N/mm2] - 107MPa (15515psi) • ISO 6873, Data referred to 22ml/100g

Packaging:

• 3kg (Box, Aluminium Bag 2 x 1.5kg)

8

Vibrated

• Water/Powder Ratio: 22ml/100g • Setting Time:10 - 13 min. • Setting Expansion after 2 h: ≤ 0.06% • Setting Expansion after 24 h: ≤ 0.06%

Color:

Ivory Silver Gray

www.mutsumidental.eu


Type 4 Dental Stones

EdoRock MAX®

Type 4 Synthetic Modified Dental Hard Stone, ideal for all working models.

Harder but easier! Pursuing the Finest Quality! Type 4 Synthetic Modified Dental Hard Stone, ideal for all working models for full/partial dentures, inlays, onlays, crowns &bridges on implants, Konuskrone, orthodontic devices, CAD/CAM or other accuracy-required purposes. EdoRock Max is a blend of refined selected alpha hemihydrate and special resin. • Excellently high strength and remarcable workability • High thixotropy-makes thickening of the model easier • Superior compatibility with impression materials • Very accurate reproduction of details • Uniform and steady expansion • Chipping during the trimming process does NOT occur!

Expansion Rate v.s. Time

Surface Roughness Edo RockMax® Average roughness 1,0 �m RaFS 10 POINTS ROUGHNESS 3,6 �m

Competitor A

0,15 0,1

EDO ROCKMAX

200 �m

0,05 1

2

3

48 (2)

24 (1)

72 (3)

10 �m

Superior compatibility with impression materials

Expansion rate (%)

Accurate reproduction of details

96 (4)

120 (5)

144 (6)

Competitor A Average roughness 1,8 �m RaFS 10 POINTS ROUGHNESS 5,9 �m

Elapsed Time (Day)

Uniform and steady expansion enables production of models with high dimensional stability and remarkable precision.

Competitor B Average roughness 3,1 �m RaFS 10 POINTS ROUGHNESS 9,3 �m

Compressive Strength after 1 hr: • Compressive Strength [MPa; N/mm2] - 64MPa (9282psi) Compressive Strength Dry: • Compressive Strength [MPa; N/mm2] - 118MPa (17114psi) • ISO 6873, Data referred to 20ml/100g

Packaging: • 5kg (Bucket)

www.mutsumidental.eu

• Water/Powder Ratio: 20ml/100g • Setting Time: 10 min. • Setting Expansion 2h/24h: ≤0.08% / ≤0.08%

Color:

Golden BrownPolar WhiteVanilla Yellow

9


Type 5 Dental Stones

EDO PREMIUM STONE® Synthetic Type 5 Modified Hard Dental Stone.

Synthetic Type 5 Modified Hard Dental Stone, with high setting expansion to compensate the high contraction of some impression materials, ideal for all working models, master and sectioned models, for orthodontic devices, full/partial dentures, inlays, onlays, crowns, bridges on implants, including models for CAD/CAM. • High thixotropy; • High initial strength; • High Dimensional stability • Short mixing, short setting time; • Remarcable precision, smooth surfaces; • Uniform and steady expansion; • Suitable for long term storage; • Proper fluidity gives excellent workability.

Accurate reproduction of details and smooth surface Immediate setting and increased quality of hyperfine powder allows of accurate detail reproductions and smooth surface when used with alginate, agar, silicon and other impression materials

Edo Premium Stone® Average roughness 1,4 �m RaFS 10 POINTS ROUGHNESS 4,5 �m

200 �m

High dimensional stability Uniform and steady setting expansion enables production of models with high dimensional stability and remarkable precision. Expansion Rate v.s. Time

50 40

Expansion rate (%)

Compressive strength (Mpa)

Creamy mixing and high initial strength The product’s superior hydrophilic property enables easy mixing. Moreover, the immediate setting is initiated soon after pouring, leading to the high initial strength.

30 20 10 0

10

2.5kg | 5kg

10

0,22

0,2

20 30 40 50 60 Elapsed time (Min.)

Compressive Strength after 1 hr: • Compressive Strength [MPa; N/mm2] - 59MPa (8555psi) Compressive Strength Dry: • Compressive Strength [MPa; N/mm2] - 112MPa (16240psi) • ISO 6873, Data referred to 20ml/100g

Packaging:

10 �m

Surface Roughness

1 Variation per hour (Hrs.)

2

24

• Water/Powder Ratio: 20 ml/100g • Setting Time: 10 min. • Setting Expansion after 2h: 0.22%

Color:

Vanilla Yellow Polar White

www.mutsumidental.eu


Phosphate Bonded Investment

HIRO VEST CF 30®

Universal carbon free phosphate bonded investment material SUPERFINE! ONE FOR ALL! • For shock heat process and for the conventional slow heating process • For inlays, crowns, partial and total bridges, partial dentures and combination technique, processed in the gel duplication technique or in duplication with silicone, etc. • Suitable for all precious and non-precious alloys including Co-Cr; - For wax patterns, three-dimensional printed plastic patterns, resin patterns; - UNIFORM and steady expansion, which stops after 30 min; - Easy de-vesting; - Very fine consistence, smooth surfaces; very accurate reproduction of details.

Crowns and bridges non-precious alloys

Precious alloys Technical Data Mixing Liquid

HiroSol®

Processing time at 22°C

approx. 5-6 min.

Characteristic values according to DIN EN ISO 15912

Partial dentures

Setting time (Vicat)

aprox. 10 min.

Compression Strength after 2 hours [MPa]

9 - 10

Linear thermal expansion [%]

0,8

Packaging

3-D printed patterns

HiroVest® CF 30, 25 bags x 160 g

4 kg.

HiroVest® CF 30, 32 bags x 160 g

5,12 kg.

HiroVest® CF 30, 125 bags x 160 g

20 kg.

HiroVest® CF 30 Intro Kit 2 bags x 160g + 80ml HiroSol® Accessories: HiroSol® Mixing Liquid

Bottle 1 liter

HiroSol® Mixing Liquid

Canister 5 liters

HiroSol 130 Mixing Liquid

Bottle 1 liter

®

www.mutsumidental.eu

11


Gypsum bonded investment

Carbon-free phosphate bonded investment for pressable ceramics. • Superfine, produces smooth and detailed pressings; • Suitable for the quick heating as well as for the conventional slow heating process; • High thermal stability; • Uniform and steady expansion; • Creamy consistency ensures easy and accurate investing; • Easy devesting.

Lithium Monosilicate pressed ceramic veneers

Pressed Ceramic Bridges

Lithium Disilicate pressed ceramic veneers

Pressed Ceramic Crowns

Tehnical Data Mixing Liquid

HiroSol P®

Processing time at 22°C

approx. 6-7 min.

Characteristic values according to DIN EN ISO 15912:2016 Setting time (Vicat)

approx. 10 min. Packaging:

Hiro PressVEST® Kit 10 bags x 100 g + 250 ml HiroSol P® Hiro PressVEST® Kit 40 bags x 100 g + 1.000 ml HiroSol P®

12

www.mutsumidental.eu


Polish & Shine

BELL COAT

Ultraviolet cured surface glaze hardening agent. A hard film with a beautiful, smooth lustre. Smooth lustre can be achieved simply by applying the glaze to a resin base, acrylic denture or hard resin and exposing it to UV rays for a short period of time. When applied after morphological corrections, filling of gaps between resin base and dentures, or restoration of hard resin that has lost its lustre, it maintains the lustre for longer time than that of a finishing polish. It can be used also with a Xenon Lamp.

Packaging:

• Bottle of 50ml - Surface Glaze Hardening Agent • Bottle of 6ml - Thinner

GLAZING PASTE

Water soluble glazing paste that contains silicon nitride particle ceramic Water soluble glazing paste that contains silicon nitride particle ceramic (Si3N4), which is the hardest next to diamond, as base ingredient. Resin rich lustre can be obtained very easily. Universal, applicable to hard resin products from all manufacturers.

Packaging: • 15g Jar

www.mutsumidental.eu

13


Hybrid Composite Resin (For Crowns & Bridges)

HIRO SIGHT VEST CF 20® EYE

Hybrid Composite Resin. Quick casting gypsum-bonded investment material.

Eye Sight Introductory Set A3. Content: •1 Bottle Opaque Primer 9ml •1 Syringe Flow Opaque 3ml (FO) •1 Syringe Opaque A3 3ml (OA3) •1 Syringe Cervical C1 6g (C1) •1 Syringe Dentine A3 6g (DA3) •1 Syringe Enamel E2 6g (E2) •1 Syringe Transparent 6g (T) •1 Flat Brush

Shades Guide Body Resin - Dentine EYE SIGHT DENTINE

The New Economic Standard: 50%

Increased content - 6g Syringes

A New Concept for Efficiency Excess paste can be preserved inside the syringe cap until next use, so you do not need to waste the paste anymore. Careful attention to such a small factor leads to efficiency.

The New Aesthetic Standard

14

Natural Looking Surface The wonderful surface brilliance and play of colour effect enables the reproduction of the natural looking teeth. Long Term Shade Stability High content of DUOS fillers can minimize water absorption while maximizing the surface hardness, which prevents surface roughness, stains and discoloration. Thanks to such properties, the intraoral shade can be secured for ages.

www.mutsumidental.eu


Hybrid Composite Resin (For Crowns & Bridges)

EYE SIGHT Hybrid Composite Resin.

NEW STANDARD FOR OPAQUE PASTE •O paque Paste - Having DUOS Fillers* (=inorganic fillers) 70wt%, the material strength and hence the durability of the body opaque paste are improved, which leads to stable bonding properties for long term. Moreover, EYE SIGHT Body Opaque Paste brings you better cover performance and deeper light penetration.

The DUO - SPHERICAL Filler (DUOS Filler) has a special structure with two kinds of inorganic spherical fillers: • BIG FILLER - 1.5 μm • SMALL FILLER - 0.01 μm - 0.5 μm, brings you the superior material hardness, durability and aesthetic of EYE SIGHT!

EYE SIGHT FLOW OPAQUE

NEW STANDARD FOR OPAQUE PASTE The EYE SIGHT’s Opaque System, which contains a high density of DUOS Filler, consists of adhesive Opaque Primer, Flow Opaque Paste with appropriate fluidity and Body Opaque Paste. • Opaque Primer – ensures great adhesion with the metal. • Flow Opaque – mainly consists of 1.5 µm spherical fillers to maximize the bearing effect and fluidity of itself.

www.mutsumidental.eu

The slightly transparent milky colour of the paste allows light to penetrate faster and deeper, and thus promotes curing. Bearing efect of the spherical fillers promote the paste infiltration in the narrow spaces of the retention beads. Indefinite shape fillers resist to pressure, hence prevent paste infiltration into narrow spaces.

15


Glazing Agent

BRIGHTENER III

Surface brightening reinforcing agent Brightener III is a surface brightening reinforcing agent that can be used inside the mouth. Colourless and transparent, its low viscosity makes it both easy to apply and highly economical. Following the process of applying the composite resin and polishing, simply apply the Brightener and expose it to light to achieve the lustre of natural teeth.

No finishing polish is required. In addition, our Glazing Agent cement creates a hard film on the surface to prevent staining. The film maintains its lustre even after 30.000 brush exposures. This material is indispensable for more accurate dental restoration with a more sophisticated finish. Net content: • 3ml Bottle

It is cured by exposure to Halogen Lamp.

Applicable for all dental resin materials. Composite Resins Smoothnes the surface

 BEFORE

AFTER

Prevent Stains

Soaked in oil orange solution/black tea of 37oC for 20 days • Oil orange solution: dissolve 2g of oil orange in 100ml of olive oil. • Black tea: Extract 2g of tea leaves with 100ml of hot water

Oil orange solution Brightener III applied. BEFORE AFTER

Brightener III not applied. BEFORE AFTER

Brightener III applied. BEFORE AFTER

Brightener III not applied. BEFORE AFTER

Abrasion resistance 30,000 times of tooth brush abrasion Brightener III applied. Surface

Brightener III

Tooth brush abrasion test Equipment: Universal abrasion tester (Shimadzu Corp.), Tooth brush: G.U.M. toothbrush (Sunstar Inc.), Paste: White&White (Lion Corp.), Load: 300g Brightener III not applied.

CR 30,000 times of tooth brush abrasion

16

Black tea

Surface

CR

30,000 times of tooth brush abrasion

www.mutsumidental.eu


Hybrid Composite Resin (For Direct Use)

PROGRESS PLUS Light Cured Ion-Releasing Composite

SMOOTH POLISHED SURFACE and NATURAL LUSTER PROGRESS PLUS is the composite resin which includes fluoride and combines beauty with strength. Its manipulation is superior.

Net content: • 4g

Prominent aesthetic PROGRESS PLUS does not stain, discolor and leave the uneven surface because DuoSpherical Filler is filled densely. It realizes the brightness and the smoothness. COMPARISON OF FILLER FORM (X10.000) Comparison of coloring experiment results (Cofee of 37oC for 20 days) PROGRESS PLUS (Flourine included)

Competitor A Competitor B Competitor C (Flourine included) (Flourine included) (Flourine not included)

BEFORE

PROGRESS PLUS

AFTER

Competitor

PROGRESS PLUS has high physical property while fluoride is included. The hardness of the surface is high. The abrasion resistance is excellent, besides it would not wear away antagonist. COMPARISON OF PHYSICAL PROPERTIES

PROGRESS Competitor A Competitor B PLUS Flourine included

Competitor C Not included

PROGRESS Competitor A Competitor B PLUS

Competitor C

Flourine included

Not included

• Compressive strength 400 350 300 250 200 150 100 50 0

• Compressivel strength (MPa)

80 60 40 20 0

• Flexural strength 200 180 160 140 120 100 80 60 40 20 0

• Flexural strength (MPa)

• Surface hardness (Hv)

• Surface hardness 120 100

PROGRESS Competitor A Competitor B PLUS

Competitor C

Flourine included

Not included

• Shade: A1, A2, A3, A3.5, B2, B3, C3, Enamel

www.mutsumidental.eu

17


Hybrid Composite Resin (For Direct Use)

PROGRESS FLOW

Light Cured Ion-Releasing Composite Flowable Composite

Perfect filling for even difficult areas with easy handling. You can fill PROGRESS FOLW easlily into even difficult areas (shallow, narrow, complicated, hard-to-see etc.) thanks to is flowability. Its aesthetic is excellent becauseit dose not stain and has high physical property. It is the most suitable as a base material for CR filling. You can use it to both of anterior and posterior tooth. (Slightly pull the plunger or syringe in case the flow of the paste does not stop) Pits and fissures filling

Resin coating before impression taking for hard resin crown

Natural shine & smoothness can be realized.

Treatment of caries

Net content: • 1,8g • Filled chip x 5pieces • Needle cap x 1 piece

Comparison of coloring experiment results (oil orange solution of 37oC for 20 days) PROGRESS FLOW

Duo-Spherical Filler is contained densely, hence prevent stain, discoloration and unevenness.

Competitor A

Competitor B

Competitor C

BEFORE AFTER

PROGRESS FLOW has high physical property while fluoride is included. Excellent in surface hardness & abrasion resistance besides it would not wear away antagonists. COMPARISON OF PHYSICAL PROPERTIES

Competitor C

PROGRESS Competitor A Competitor B FLOW

Competitor C

• Compressive strength 400 350 300 250 200 150 100 50 0

• Compressivel strength (MPa)

PROGRESS Competitor A Competitor B FLOW

• Flexural strength 140 120 100 80 60 40 20 0

• Flexural strength (MPa)

• Surface hardness (Hv)

• Surface hardness 70 60 50 40 30 20 10 0

PROGRESS Competitor A Competitor B FLOW

Competitor C

• Shade: A1, A2, A3, A3.5, B3

18

www.mutsumidental.eu


Bonding, Etching & Applicators

BELL BOND ETCHING Etching material

Phosphoric acid-type enamel etching material.

Precise application.

Net content: • 5ml bottle

BELL BOND BONDING Superior bonding

Bell Bond eliminates the need to mix two liquids as well as the priming process. Subsequent to etching the enamel, apply the bond and expose to light for ten seconds:

that is all it takes to achieve superior bonding. Net content: • 6ml bottle

SPONGES

MUTSUMI MASKS

Sponge applicators for Bell Bond Bonding and Bell Bond Etching. Total control.

These masks use a softer rubber designed not to cut or to dig into the ears. Comfortable fit and reasonable prices. Hygienic disposable type.

www.mutsumidental.eu

19


Applicators & Prophylaxis

FLAT / ROUND BRUSH Flat brush for a perfect application of Eye Sight Opaque Pastes. Round type is designed for Eye Sight Opaque Primer application.

BELL FEEL SMALL BRUSH Pursuing further easiness of operation by adopting double angle brush tip, this brush is applicable to etching and bonding agent applications.

POCKET DENTIST - TRAVEL Pocket Dentist - Travel With three active ends: • Toothbrush • Interdental Brush for in Between Teeth • Toothpick

Small size as it can be folded, for great travels.

3 colours: • Pink • Sky-blue • Green with a spare interdental brush

MUTSUMI TOOTHBRUSHES The active head is made of Tynex nylon fibers, which are proven to retain their water resistance and elasticity 1.5 times longer than other products. Regular and Soft.

Bring you the optimal brushing experience!

20

www.mutsumidental.eu


Prophylaxis

PURETECT Prophylaxis Paste

PURETECT, which contains two kinds of inorganic particles with different sizes, forms and hardness, is formulated to enable tooth surface cleaning and finish-polishing at one time. Moreover, a natural product derived glazing material is added to realise the natural shine. • Polishing after scaling • Removal of stains such as nicotine • Polishing after orthodontic appliance attachament • Polishing after breaching • Polishing before cavity preparation

One Paste, Three Works. Cleaning

1

Porous silica particles with large dimension and low hardness removes stains.

Porous silica particles Stains

Porous silica particles break down due to its self-breaking nature. Less abrasive to enamel.

Stains removed.

<SEM> photo 1 xPorous particles: ×100Average particle size: 25 µm approx. Particle form: Porous, partly agglutinated. Efficacy: Low hardness, cleans well.

Enamels

Polishing

2

Silicone nitride particles of 1µm size with high hardness smooth the tooth surface. Silicone nitride particles

Rough, scratched tooth surface is well polished and smoothed.

<SEM photo 2> Silicone nitride particles: ×1000Average particlesize: 1 µm approx. Particle form: RoundEfficacy: High hardness, smooth the surface.

Enamels

Glazing

3

Natural-product-derived glazing material makes the surface shinny. Glazing material

Glazing material smoothes and coats the surface.

Enamels

Before

Aplication example

1. S tain removal, polishing and glazing are available for all kinds of discoloured teeth except for calcified, with one paste

After

2. Apply on prophy brush or prophy cup with a little excess to operate with low speed rotation. PURETECT can also be applied for metal prosthesis or resin surface with with no damages.

Precaution Close the cap after every usage to prevent moisture loss.

www.mutsumidental.eu

21


Denture Lining

REBASE HARMONY Denture base hard relining materials

REBASE HARMONY (kit) At Mutsumi, we are fully familiar with the intricacies of particle technology and dynamics. Based on this knowledge, we have developed our own special denaturalized monomer and combined it with a catalyst in this product to yield optimal rapid hardening. This facilitates superior flow and accurate muscle trimming, designed especially to prevent discomfort in patients.

Packaging Set: • Powder 80g • Liquid 50ml • Primer 25ml • Lubber Cup

• Medical Device Category: Class II • Shades: Live Pink and Pink

• Measuring Cup • Spatula • Dropper • Small Brush

Rebase Harmony Fast-Hardening Agent Elasticity rate

10,000,000

• Testing Equipment: Rheometer by Bohlin • Frequency of vibration: 1 Hz using a parallel • Frequency of vibration: 1 Hz using a parallel • Measurement temperature: 37oC • Powder: Liquid ratios • Average Product 1,6:1 • Fasthardening product: 1,8:1

Fast-hardening product

1,000,000 100,000 10,000

Average product

1,000 100 1 1

0

2

4

6

*Measured 1 min after blending initiated

8 Time (min.)

Usage

Standarg powder-to-liquid ratio: Powder: one division of a cup, liquid: one division of a dropper Outside the mouth cavity

Inside the mouth cavity

Bite adjusment Trimming and muscle trimming

Build up to base

Outside the mouth cavity

Inside the mouth cavity

Outside the mouth cavity

Hardening reaction

Morphology modification

By type

Standard powder:liquid ratio

Mixing

Fast

1.8/1

30s

1~2min.

2.5~3min.

4~4.5min.

6~7min.

Normal

1.6/1

30s

2~2.5min.

4~4.5min.

6~6.5min.

8~9min.

* The speed of the rise in the level of viscosity depends on the ambient temperature. Please note that some adjustment may need to be made to the time for bite adjustment and muscle trimming when the object is placed in the mouth. When using hardening acceleration agents, use them prior to morphology modification

22

www.mutsumidental.eu


Cutting, Polishing, Wax

HIRO WAX Plate Paraffin Wax

Featuring the superior toughness and plasticity needed for the job, as well as minimum shrinkage, this wax is superior for welding procedures and denture maintenanceIt has a thick. It is also designed for use throughout the four seasons under essentially identical conditions.

• ISO 15854, Type 2 Classification 2 Hard • Medical Device Category: Class I • Sheet Size: 187mm X 85mm X 1,5mm thick; • Primary softening temperature 41-45OC

Packaging:

Color:

500g per box | 2,5 kg box | 20 kg box.

PLASTER CUTTING BLADE This produce features a side hole, our own special design to that prevents clogging. It s unrivalled in terms of sharpness and durability.

Pink

SILICON POINT Featuring excellent polishing capability, this silicon point can be used to polish a variety of metals and oral prosthesises whit minimum heat generation. We also offer silicon point for resin bases.

Dimensions:

• Long - 13,3cm, Regular - 10cm, Short: 7,5cm • Thickness: 0,2mm and 0,15mm

• Medical Device Category: Class I • Shades: SB-10, SB-13, SB-13S, SB-28, SB-125 (for resin bases) • Packaging: 10 and 100 • Shades variation (Actual size) • Use by 5.000 - 30.000 rotation per minute

SB-10

www.mutsumidental.eu

SB-13

SB-13S

SB-28

SB-125

23


www.mutsumidental.eu


Turn static files into dynamic content formats.

Create a flipbook
Issuu converts static files into: digital portfolios, online yearbooks, online catalogs, digital photo albums and more. Sign up and create your flipbook.