PRODUCT CATALOG
INTRODUCTION
BKP GROUP, a.s. was established in 1991 as a producer of polyester
putties. Since 1995 we have been producing in new operating premises, which are fully equipped with modern technological devices. In Czech Republic we were the first to start with production of twocomponent polyester putties, which replace before used materials such as oil, acrylic and epoxy putties. Over the years, we have broadened our production assortment with spraying putties, fillers, clear coats, protective spray coats, sprays, thinners, abrasives etc. Nowadays we are the biggest Czech producer of such products exporting into neighbouring countries. Our products are supplied via distributors and wholesales into industry, auto paint shops and trade networks including foreign hobby shops We are holders of ISO 9001, ISO 14001 and OHSAS 18001 certificates.
BKP GROUP, a.s. 1.května 333 687 34 Uherský Brod 3 CZECH REPUBLIC www.bkp.cz obchod@bkp.cz Tel.: +420 572 61 00 61 Fax: +420 572 61 00 70
Page 2
CONTENT
BASIC PUTTIES
page 4
SPECIAL PUTTIES
page 6
LAMINATING KITS
page 9
SPRAY PUTTIES
page 11
FILLERS
page 11
THINNERS
page 13
OTHER RANGE
page 14
________ VOLUMES OF PACKAGING
page 15
TECHNICAL DATA SHEETS
page 16
Page 3
BASIC PUTTIES
DESCRIPTION
LENT
Middle dense, very well workable, soft, both upper and finishing fast putty used for filling of small and middle-sized disparities.
USAGE
Intended for common surface including castiron, aluminum, zinc and glass fibre
HARDENING
Red paste in tube in weight ratio 100:2
POT LIFE
5 minutes
SANDING
25 – 30 minutes
COLOUR
Bright orange
DESCRIPTION
UNIX
Middle rough, very well sandable, suitable as universal filling putty.
________ USAGE
Intended for common surface including castiron, aluminum, zinc and glass fibre
HARDENING
Red paste in tube in weight ratio 100:2
POT LIFE
5 minutes
SANDING
25 – 30 minutes
COLOUR
Ochry
Page 4
BASIC PUTTIES
DESCRIPTION
FIN
Very fine putty intended for filling of small disparities, striae and pits on car bodies, various metal products, iron castings or machine exteriors.
USAGE
It is easy to applicable and has very good sandability. It is suitable as finishing putty.
HARDENING
Red paste in tube in weight ratio 100:2
POT LIFE
7 minutes
SANDING
25 - 30 minutes
COLOUR
White
DESCRIPTION
MASTER
Middle dense, rougher putty intended for common surface including cast-iron, aluminum, zinc and glass fibre. It is suitable as universal filling putty.
________ USAGE
Recommended especially for container producers.
HARDENING
Red paste in tube in weight ratio 100:2
POT LIFE
5 minutes
SANDING
20 – 30 minutes
COLOUR
Ochry
Page 5
SPECIAL PUTTIES
DESCRIPTION
FLAT
It contains high volume of fibreglass, which is necessary for formation of very strong, with fibreglass fixed layer of putty.
USAGE
Suitable especially for vaulting of missing parts in material, possible to put on in thick layer
HARDENING
Red paste in tube in weight ratio 100:2
POT LIFE
5 minutes
SANDING
20 - 30 minutes
COLOUR
Dark green
DESCRIPTION
EXTRA
It has a high content of aluminium powder, what is necessary for better adhesion on filled surface. It has soft structure. It is well applicable.
________ USAGE
Intended for filling of light metals, galavanized sheets of car bodies, steel and glass fibre
HARDENING
Red paste in tube in weight ratio 100:2
POT LIFE
6 minutes
SANDING
25 – 35 minutes
COLOUR
Metallic
Page 6
SPECIAL PUTTIES
DESCRIPTION
USAGE HARDENING POT LIFE SANDING COLOUR
DESCRIPTION
PLASTEX
It is a special two component fine polyester putty with very high elasticity and increased adhesion to plastics. It is non-porous, easy to apply. Excels with workability and easy sandable. Red paste in tube in weight ratio 100:2 4 - 6 minutes 20 - 25 minutes Black
HOLS
It has high content of wooden powder, which is necessary for chromatosis of the putty with common wood stains both before application and after hardening of putty.
________ USAGE
Suitable for filling of massif, chipboard, blockboard and all products made from wood
HARDENING
White paste in tube in weight ratio 100:2
POT LIFE
6 minutes
SANDING
30 minutes
COLOUR
Light brown (transparent)
Page 7
SPECIAL PUTTIES
DESCRIPTION
LITE
Light-weight putty, middle dense and very well workable. There is a minimal increase of weight of construction, so it is suitable for aircraft industry and ship-building sector.
USAGE
Intended for filling small and bigger disparities on common surfaces
HARDENING
Red paste in tube in weight ratio 100:3
POT LIFE
5 minutes
SANDING
20 - 30 minutes
COLOUR
Light blue
DESCRIPTION
RAPID R
Middle rough, elastic two-component polyester putty intended for filling of large surfaces during railway carriages repairs.
________ USAGE
Excels in toughness, endures big load in bend and stroke during changing of temperatures and vibrations
HARDENING
Red paste in tube in weight ratio 100:2
POT LIFE
30 minutes
SANDING
6 – 8 hours
COLOUR
Light gray
Page 8
SPECIAL PUTTIES
DESCRIPTION
LONG
Two-component putty intended for filling of dimensional workpieces, machine parts and large surfaces during the repairs of machine exteriors.
USAGE
Possible to use successfully also for filling of various metal products or iron castings
HARDENING
Red paste in tube in weight ratio 100:2
POT LIFE
30 minutes
SANDING
4 – 5 hours
COLOUR
Gray
LAMINATING KITS DESCRIPTION
LAMINO REPAIR BOX
Two-component polyester repair set for small repairs. The repair set is used for repairing of holes or splits in metal or laminate materials as for example rusted up places on car bodies, boats or camping caravans
________ USAGE
HARDENING
Red paste in tube in weight ratio 100:2
POT LIFE
8 - 10 minutes
SANDING
40 minutes
COLOUR
Light yellow transparent liquid
Page 9
LAMINATING KITS LAMINO RESIN DESCRIPTION
Two-component polyester resin for repairing of laminate and lamination.
USAGE
Used for repairing of holes or splits in metal or laminate materials as for example rusted up places on car bodies, boats or camping caravans
HARDENING
Red paste in tube in weight ratio 100:2
POT LIFE
8 - 10 minutes
SANDING
40 minutes
COLOUR
Light yellow transparent liquid
DESCRIPTION
GLASS MAT
Non-woven glass mat Density 300g/m2 Size 1,5 m2
________ Page 10
SPRAY PUTTIES
DESCRIPTION
USAGE
FINAL
Two-component spray putty intended for unification of surface between filled and no filled places, or for straightening of surface on car bodies.
It is used for formation of equable layer of putty on whole car body, which is necessary before application of filler and subsequently upper paint
HARDENING
Initiator 40 (liquid) in weight ratio 100:5
POT LIFE
40 minutes
SANDING
2 hours
COLOUR
white / gray
FILLERS DESCRIPTION
FIL 4:1 PREMIUM
Two-compound high-quality acrylic primer for majority of common surfaces.
________ USAGE
It has excellent filling properties. It is an ideal base which ensures high-quality appearance of coated things
HARDENING
4 parts of filler : 1 part of hardener in volume ratio
POT LIFE
45 minutes
SANDING
3 hours
COLOUR
gray / black
Page 11
FILLERS
DESCRIPTION
FIL 4:1 NORMAL
Two-compound high-quality acrylic primer for majority of common surfaces.
USAGE
It has excellent spill, perfect covering. It dries fast also in thicker layers, is very well sandable.
HARDENING
4 parts of filler : 1 part of hardener in volume ratio
POT LIFE
60 minutes
SANDING
3 hours
COLOUR
white / gray / black
DESCRIPTION
FIL 1K
One-component acrylic filler with excellent filling properties. It can be applied on majority of common materials. It dries on air, is resistant against atmospheric and chemical influences. It is well sandable, easy to use.
________ USAGE
SANDING
45 – 60 minutes
COLOUR
Beige
Page 12
THINNERS
DESCRIPTION
TRIN ACRYL
High quality acrylic thinner, which is used for modification of consistence of acrylic fillers and clearcoats. It is suitable into all acrylic coating compositions.
COLOUR
Transparent
DESCRIPTION
TRIN POLYESTER
Thinner, which is used for thinning of two-component polyester spray putties. It is suitable also for cleaning of working tools polluted by all types of polyester putties. Spray putties can be thinned max. 10% of their weight.
________ COLOUR
Transparent
Page 13
THINNERS
DESCRIPTION
TRIN POLYURETAN
It is a thinner used for adjusting the consistency of fillers VARIOL FIL 4:1 PREMIUM and VARIOL FIL 2K PUR. It is suitable also for thinning acrylic paints and cleaning of working tools polluted by all types of polyurethane coatings. Transparent
COLOUR
OTHER RANGE DESCRIPTION
TOPEKOR
It contains effective preparation for dispersion of anorganic and organic sediments, and inhibitor which protect against corrosion in closed systems of central heating. TOPEKOR can be used also in circulating systems where is the possibility of formation of scale or corrosion.
________ DOSAGE
Content of the container (500 ml) guarantee perfect protection of system with capacity up to 400 litres of water during minimally two years.
COMPATIBILITY It does not work aggresively on common materials WITH as iron, steel, cast iron, zinc coating, copper, MATERIALS polyethylene, polypropylene, rubber, sealing rubbers, teflon. It gets on glycols in water antifreezing systems.
Page 14
VOLUMES OF PACKAGING Polyester putties are normally packed in cans in volumes 0.2, 0.5, 1, 2 or 5 kg. It is also possible packing in a special 3 kg can for the batcher. Each package includes the initiator. Group packaging (cardboard, stretch-foil) can be adapted to customer requirements.
Overview of packaging product
putties
Fillers are packed in cans in volumes 1 or 4 liters. Hardeners are included in the appropriate packages 0.25 or 1 liters. Thinners are commonly supplied in packages of 1 liter can, or 5 liters canister. Transportation of so packaged products is thus excluded from the provisions of ADR, due to the limited quantity per unit.
fillers hardeners thinners
content
quantity [pcs] group
layer
pallet
0.2 kg
10
150
1500
0.5 kg
10
70
1050
1.0 kg
6
90
540
2.0 kg
3
30
300
3.0 kg
4
60
240
5.0 kg
-
35
105
1.0 l
6
84
504
4.0 l
-
20
100
0.25 l
10
70
1050
1.0 l
6
84
504
1.0 l
6
84
504
5.0 l
-
42
126
________ Page 15
TECHNICAL DATA SHEETS LENT
page 17
UNIX
page 18
FIN
page 19
MASTER
page 20
FLAT
page 21
EXTRA
page 22
PLASTEX
page 23
HOLS
page 24
LITE
page 25
RAPID R
page 26
LONG
page 27
LAMINO RESIN / REPAIR BOX
page 28
FINAL
page 29
FIL 4:1 PREMIUM
page 30
FIL 4:1 NORMAL
page 31
________ FIL 1K
page 32
TRIN ACRYL
page 33
TRIN POLYESTER
page 34
TRIN POLYURETAN
page 35
TOPEKOR
page 36
Page 16
TECHNICAL DATA SHEET
VARIOL LENT technical description: 10. 10. 2012 DESCRIPTION AND USAGE
LENT is a two component polyester medium dense, well-workable putty for filling small to medium sized disparities. It is intended for common surface including iron, aluminum, zinc and fiberglass. It is very well sandable, pore-free, it is also applicable to even out inequalities on wood (harder types), concrete, etc. The putty is due to its structure very well applicable.
ENVIRONMENT
The putty must not be used for filling places which are in direct contact with food and drinking water.
VOC VOLUME
VOC = 51 g / l This product complies with EU Directive (2004/42/EC), which gives for the preparation of this category (B / b) the limit value of volatile matter content of 250 g / l in finished product.
APPLICATION
Get rid of rust and abrade the bonded surface by sandpaper P80. Surface must be clean, dry and free of dust and grease. For maximum corrosion protection use epoxy or polyurethane basecoat. Do not apply the putty on reactive, single or nitrocellulose basecoats. Apply with a trowel.
HARDENING
The putty is hardened with hardener (PE-initiator, dibenzoyl peroxide, red paste in tube) in weight ratio: - 100 parts of putty : 2 parts of hardener – recommended ratio for temperature 23°C
POT LIFE
The putty is necessary to be used within 5 minutes after mixing with hardener at temperature 23°C and hardening ratio 100:2. Adjusting of the hardening ratio can partly eliminate the influence of temperature on the potlife. At lower temperatures (at least 17°C), the potlife increases, at higher temperatures is reduced. Do not exceed the recommended hardening ratio.
SANDING
The putty is sandable after 25-30 minutes at temperature 23°C and hardening ratio 100:2. Rough sanding begins with sanding paper P80-120 and finishes with sanding paper P180-240. For sanding is recommended to use rotating or vibrating sander.
UPPER COATINGS
It is possible to use all common paint systems on the putty. The putty withstands temperatures of 80-110 °C.
TOOLS CLEANING
Dirty parts of tools for filling can be cleaned with VARIOL TRIN POLYESTER or nitrothinner C-6000. Only non-hardened putty can be cleaned.
STORAGE
It is necessary to ensure the temperature from +5°C to + 25°C and avoid direct solar radiation during storage and transport. Dash of the resin on the surface of putty is acceptable. We guarantee shelf life and quality of the product for 12 months.
PACKAGING
- 0,2 kg, 0,5 kg, 1 kg, 1,8 kg, 5 kg, 15 kg – a can - 3 kg – a can for batching plant
COLOUR
Bright orange
Page 17
TECHNICAL DATA SHEET
VARIOL UNIX technical description: 10. 10. 2012 DESCRIPTION AND USAGE
UNIX is a two polyester medium rough and very well applicable putty. Due to its higher viscosity is perfectly sandable. It is an universal pore-free putty intended for the common surface including iron, aluminum and fiberglass.
ENVIRONMENT
The putty must not be used for filling places which are in direct contact with food and drinking water.
VOC VOLUME
VOC = 119 g / l This product complies with EU Directive (2004/42/EC), which gives for the preparation of this category (B / b) the limit value of volatile matter content of 250 g / l in finished product.
APPLICATION
Get rid of rust and abrade the bonded surface by sandpaper P80. Surface must be clean, dry and free of dust and grease. For maximum corrosion protection use epoxy or polyurethane basecoat. Do not apply the putty on reactive, single or nitrocellulose basecoats. Apply with a trowel.
HARDENING
The putty is hardened with hardener (PE-initiator, dibenzoyl peroxide, red paste in tube) in weight ratio: - 100 parts of putty : 2 parts of hardener – recommended ratio for temperature 23°C
POT LIFE
The putty is necessary to be used within 5 minutes after mixing with hardener at temperature 23°C and hardening ratio 100:2. Adjusting of the hardening ratio can partly eliminate the influence of temperature on the potlife. At lower temperatures (at least 17°C), the potlife increases, at higher temperatures is reduced. Do not exceed the recommended hardening ratio.
SANDING
The putty is sandable after 25-30 minutes at temperature 23°C and hardening ratio 100:2. Rough sanding begins with sanding paper P80-120 and finishes with sanding paper P180-240. For sanding is recommended to use rotating or vibrating sander.
UPPER COATINGS
It is possible to use all common paint systems on the putty. The putty withstands temperatures of 80-110 °C.
TOOLS CLEANING
Dirty parts of tools for filling can be cleaned with VARIOL TRIN POLYESTER or nitrothinner C-6000. Only non-hardened putty can be cleaned.
STORAGE
It is necessary to ensure the temperature from +5°C to + 25°C and avoid direct solar radiation during storage and transport. Dash of the resin on the surface of putty is acceptable. We guarantee shelf life and quality of the product for 12 months.
PACKAGING
- 0,2 kg, 0,5 kg, 1 kg, 1,8 kg, 5 kg, 15 kg – a can - 3 kg – a can for batching plant
COLOUR
Beige green
Page 18
TECHNICAL DATA SHEET
VARIOL FIN technical description: 10. 10. 2012 DESCRIPTION AND USAGE
FIN is a two-component soft putty intended for filling of small disparities, striae and pits on car bodies. It is possible to fill various metal products, iron castings or machine exteriors successfully with this product. It is applicable also for straightening of disparities on wood (harder kinds), glass fibre, concrete etc. Thanks to its very fine structure the putty is easy to applicable and has very good sandability. It is suitable as finishing putty.
ENVIRONMENT
The putty must not be used for filling places which are in direct contact with food and drinking water.
VOC VOLUME
VOC = 99 g / l This product complies with EU Directive (2004/42/EC), which gives for the preparation of this category (B / b) the limit value of volatile matter content of 250 g / l in finished product.
APPLICATION
Get rid of rust and abrade the bonded surface by sandpaper P80. Surface must be clean, dry and free of dust and grease. For maximum corrosion protection use epoxy or polyurethane basecoat. Do not apply the putty on reactive, single or nitrocellulose basecoats. Apply with a trowel.
HARDENING
The putty is hardened with hardener (PE-initiator, dibenzoyl peroxide, red paste in tube) in weight ratio: - 100 parts of putty : 2 parts of hardener – recommended ratio for temperature 23°C
POT LIFE
The putty is necessary to be used within 7 minutes after mixing with hardener at temperature 23°C and hardening ratio 100:2. Adjusting of the hardening ratio can partly eliminate the influence of temperature on the potlife. At lower temperatures (at least 17°C), the potlife increases, at higher temperatures is reduced. Do not exceed the recommended hardening ratio.
SANDING
The putty is sandable after 25-30 minutes at temperature 23°C and hardening ratio 100:2. Rough sanding begins with sanding paper P120-180 and finishes with sanding paper P240-320. For sanding is recommended to use rotating or vibrating sander.
UPPER COATINGS
It is possible to use all common paint systems on the putty. The putty withstands temperatures of 80-110 °C.
TOOLS CLEANING
Dirty parts of tools for filling can be cleaned with VARIOL TRIN POLYESTER or nitrothinner C-6000. Only non-hardened putty can be cleaned.
STORAGE
It is necessary to ensure the temperature from +5°C to + 25°C and avoid direct solar radiation during storage and transport. Dash of the resin on the surface of putty is acceptable. We guarantee shelf life and quality of the product for 12 months.
PACKAGING
- 0,2 kg, 0,5 kg, 1 kg, 2 kg, 5 kg, 15 kg – a can - 3 kg – a can for batching plant
COLOUR
White
Page 19
TECHNICAL DATA SHEET
VARIOL MASTER technical description: 10. 10. 2012 DESCRIPTION AND USAGE
MASTER is middle dense, rougher putty intended for common surface including castiron, aluminum, zinc and glass fibre. It is very well sandable, without pits, suitable as universal filling putty. It is recommended especially or container producers.
ENVIRONMENT
The putty must not be used for filling places which are in direct contact with food and drinking water.
VOC VOLUME
VOC = 53 g / l This product complies with EU Directive (2004/42/EC), which gives for the preparation of this category (B / b) the limit value of volatile matter content of 250 g / l in finished product.
APPLICATION
Get rid of rust and abrade the bonded surface by sandpaper P80. Surface must be clean, dry and free of dust and grease. For maximum corrosion protection use epoxy or polyurethane basecoat. Do not apply the putty on reactive, single or nitrocellulose basecoats. Apply with a trowel.
HARDENING
The putty is hardened with hardener (PE-initiator, dibenzoyl peroxide, red paste in tube) in weight ratio: - 100 parts of putty : 2 parts of hardener – recommended ratio for temperature 23°C
POT LIFE
The putty is necessary to be used within 5 minutes after mixing with hardener at temperature 23°C and hardening ratio 100:2. Adjusting of the hardening ratio can partly eliminate the influence of temperature on the potlife. At lower temperatures (at least 17°C), the potlife increases, at higher temperatures is reduced. Do not exceed the recommended hardening ratio.
SANDING
The putty is sandable after 20-30 minutes at temperature 23°C and hardening ratio 100:2. Rough sanding begins with sanding paper P80-120 and finishes with sanding paper P180-240. For sanding is recommended to use rotating or vibrating sander.
UPPER COATINGS
It is possible to use all common paint systems on the putty. The putty withstands temperatures of 80-110 °C.
TOOLS CLEANING
Dirty parts of tools for filling can be cleaned with VARIOL TRIN POLYESTER or nitrothinner C-6000. Only non-hardened putty can be cleaned.
STORAGE
It is necessary to ensure the temperature from +5°C to + 25°C and avoid direct solar radiation during storage and transport. Dash of the resin on the surface of putty is acceptable. We guarantee shelf life and quality of the product for 12 months.
PACKAGING
- 0,2 kg, 0,5 kg, 1 kg, 2 kg, 5 kg, 15 kg – a can - 3 kg – a can for batching plant
COLOUR
Ochry
Page 20
TECHNICAL DATA SHEET
VARIOL FLAT technical description: 10. 10. 2012 DESCRIPTION AND USAGE
FLAT is a special two component polyester putty intended for the common surface including iron, aluminum, zinc and fiberglass. It is especially suited for bridging the missing parts of the material, it can be applied in a thick layer. It has a high content of glass fiber, which allows you to create very strong layer of putty tied by fiberglass, that can be sanded as needed.
ENVIRONMENT
The putty must not be used for filling places which are in direct contact with food and drinking water.
VOC VOLUME
VOC = 67 g / l This product complies with EU Directive (2004/42/EC), which gives for the preparation of this category (B / b) the limit value of volatile matter content of 250 g / l in finished product.
APPLICATION
Get rid of rust and abrade the bonded surface by sandpaper P80. Surface must be clean, dry and free of dust and grease. For maximum corrosion protection use epoxy or polyurethane basecoat. Do not apply the putty on reactive, single or nitrocellulose basecoats. Apply with a trowel.
HARDENING
The putty is hardened with hardener (PE-initiator, dibenzoyl peroxide, red paste in tube) in weight ratio: - 100 parts of putty : 2 parts of hardener – recommended ratio for temperature 23°C
POT LIFE
The putty is necessary to be used within 5 minutes after mixing with hardener at temperature 23°C and hardening ratio 100:2. Adjusting of the hardening ratio can partly eliminate the influence of temperature on the potlife. At lower temperatures (at least 17°C), the potlife increases, at higher temperatures is reduced. Do not exceed the recommended hardening ratio.
SANDING
The putty is sandable after 20-30 minutes at temperature 23°C and hardening ratio 100:2. Rough sanding begins with sanding paper P60-80 and finishes with sanding paper P120. For sanding is recommended to use rotating or vibrating sander.
UPPER COATINGS
It is possible to use all common paint systems on the putty. The putty withstands temperatures of 80-110 °C.
TOOLS CLEANING
Dirty parts of tools for filling can be cleaned with VARIOL TRIN POLYESTER or nitrothinner C-6000. Only non-hardened putty can be cleaned.
STORAGE
It is necessary to ensure the temperature from +5°C to + 25°C and avoid direct solar radiation during storage and transport. Dash of the resin on the surface of putty is acceptable. We guarantee shelf life and quality of the product for 12 months.
PACKAGING
- 0,15 kg, 0,5 kg, 1 kg, 1,8 kg, 5 kg, 15 kg – a can - 3 kg – a can for batching plant
COLOUR
Green
Page 21
TECHNICAL DATA SHEET
VARIOL EXTRA technical description: 10. 10. 2012 DESCRIPTION AND USAGE
EXTRA is a special two component polyester putty designed for filling light metal, galvanized sheets of car bodies, steel and fiberglass. It has a high content of aluminium powder, which brings a soft structure and good applicability, easy sanding and increased adhesion to filled surface.
ENVIRONMENT
The putty must not be used for filling places which are in direct contact with food and drinking water.
VOC VOLUME
VOC = 65 g / l This product complies with EU Directive (2004/42/EC), which gives for the preparation of this category (B / b) the limit value of volatile matter content of 250 g / l in finished product.
APPLICATION
Get rid of rust and abrade the bonded surface by sandpaper P80. Surface must be clean, dry and free of dust and grease. For maximum corrosion protection use epoxy or polyurethane basecoat. Do not apply the putty on reactive, single or nitrocellulose basecoats. Apply with a trowel.
HARDENING
The putty is hardened with hardener (PE-initiator, dibenzoyl peroxide, red paste in tube) in weight ratio: - 100 parts of putty : 2 parts of hardener – recommended ratio for temperature 23°C
POT LIFE
The putty is necessary to be used within 6 minutes after mixing with hardener at temperature 23°C and hardening ratio 100:2. Adjusting of the hardening ratio can partly eliminate the influence of temperature on the potlife. At lower temperatures (at least 17°C), the potlife increases, at higher temperatures is reduced. Do not exceed the recommended hardening ratio.
SANDING
The putty is sandable after 25-35 minutes at temperature 23°C and hardening ratio 100:2. Rough sanding begins with sanding paper P80-120 and finishes with sanding paper P180-240. For sanding is recommended to use rotating or vibrating sander.
UPPER COATINGS
It is possible to use all common paint systems on the putty. The putty withstands temperatures of 80-110 °C.
TOOLS CLEANING
Dirty parts of tools for filling can be cleaned with VARIOL TRIN POLYESTER or nitrothinner C-6000. Only non-hardened putty can be cleaned.
STORAGE
It is necessary to ensure the temperature from +5°C to + 25°C and avoid direct solar radiation during storage and transport. Dash of the resin on the surface of putty is acceptable. We guarantee shelf life and quality of the product for 12 months.
PACKAGING
- 0,2 kg, 0,5 kg, 1 kg, 1,8 kg, 5 kg, 15 kg – a can - 3 kg – a can for batching plant
COLOUR
Green
Page 22
TECHNICAL DATA SHEET
VARIOL PLASTEX technical description: 10. 10. 2012 DESCRIPTION AND USAGE
PLASTEX is a special two component fine polyester putty with very high elasticity and increased adhesion to plastics. It is non-porous, easy to apply and very well sandable.
ENVIRONMENT
The putty must not be used for filling places which are in direct contact with food and drinking water.
VOC VOLUME
VOC = 35 g / l This product complies with EU Directive (2004/42/EC), which gives for the preparation of this category (B / b) the limit value of volatile matter content of 250 g / l in finished product.
APPLICATION
Get rid of rust and abrade the bonded surface by sandpaper P150. Surface must be clean, dry and free of dust and grease. Apply with a trowel.
HARDENING
The putty is hardened with hardener (PE-initiator, dibenzoyl peroxide, red paste in tube) in weight ratio: - 100 parts of putty : 2 parts of hardener – recommended ratio for temperature 23°C
POT LIFE
The putty is necessary to be used within 4-6 minutes after mixing with hardener at temperature 23°C and hardening ratio 100:2. Adjusting of the hardening ratio can partly eliminate the influence of temperature on the potlife. At lower temperatures (at least 17°C), the potlife increases, at higher temperatures is reduced. Do not exceed the recommended hardening ratio.
SANDING
The putty is sandable after 20-25 minutes at temperature 23°C and hardening ratio 100:2. Rough sanding begins with sanding paper P150 and finishes with sanding paper P240. For sanding is recommended to use rotating or vibrating sander.
UPPER COATINGS
It is possible to use all common paint systems on the putty. The putty withstands temperatures of 80-110 °C.
TOOLS CLEANING
Dirty parts of tools for filling can be cleaned with VARIOL TRIN POLYESTER or nitrothinner C-6000. Only non-hardened putty can be cleaned.
STORAGE
It is necessary to ensure the temperature from +5°C to + 25°C and avoid direct solar radiation during storage and transport. Dash of the resin on the surface of putty is acceptable. We guarantee shelf life and quality of the product for 12 months.
PACKAGING
- 0,2 kg, 0,5 kg, 1 kg, 2 kg, 5 kg, 15 kg – a can - 3 kg – a can for batching plant
COLOUR
Black
Page 23
TECHNICAL DATA SHEET
VARIOL HOLS technical description: 10. 10. 2012 DESCRIPTION AND USAGE
HOLS is a special two-component polyester putty intended for filling of all kinds of wood. It is suitable for filling of massif, chipboard, blockboard and all products made from wood. HOLS has high content of wooden powder, which is necessary for chromatosis of the putty with common wood stains both before application and after hardening of putty. HOLS is both well sandable and elastic, what is necessary according to volume non-stability of wooden materials.
ENVIRONMENT
The putty must not be used for filling places which are in direct contact with food and drinking water.
VOC VOLUME
VOC = 50 g / l This product complies with EU Directive (2004/42/EC), which gives for the preparation of this category (B / b) the limit value of volatile matter content of 250 g / l in finished product.
APPLICATION
Bonded wood surface is necessary to get rid of moisture, dust, old paint and sand by sandpaper. Apply with a trowel. If you need to create a larger layer of putty, we recommend filling in multiple layers of about 5 mm. Between the layers wait at least 30 minutes.
HARDENING
The putty is hardened with hardener (PE-initiator, dibenzoyl peroxide, white paste in tube) in weight ratio: - 100 parts of putty : 2 parts of hardener – recommended ratio for temperature 23°C
POT LIFE
The putty is necessary to be used within 6 minutes after mixing with hardener at temperature 23°C and hardening ratio 100:2. Adjusting of the hardening ratio can partly eliminate the influence of temperature on the potlife. At lower temperatures (at least 17°C), the potlife increases, at higher temperatures is reduced. Do not exceed the recommended hardening ratio.
SANDING
The putty is sandable after 30 minutes at temperature 23°C and hardening ratio 100:2. Rough sanding begins with sanding paper P80-120 and finishes with finer sandpaper as needed. For sanding is recommended to use rotating or vibrating sander.
UPPER COATINGS
The putty can be covered with commercially available stains (based on water or alcohol). It can be used for any conventional coating systems.
TOOLS CLEANING
Dirty parts of tools for filling can be cleaned with VARIOL TRIN POLYESTER or nitrothinner C-6000. Only non-hardened putty can be cleaned.
STORAGE
It is necessary to ensure the temperature from +5°C to + 25°C and avoid direct solar radiation during storage and transport. Dash of the resin on the surface of putty is acceptable. We guarantee shelf life and quality of the product for 12 months.
PACKAGING
- 0,15 kg, 0,5 kg, 0,75 kg, 1,5 kg, 4 kg, 12 kg – a can - 2,5 kg – a can for batching plant
COLOUR
Light brown transparent
Page 24
TECHNICAL DATA SHEET
VARIOL LITE technical description: 10. 10. 2012 DESCRIPTION AND USAGE
LITE is a considerably light-weight putty, middle dense and very well workable. This upper putty is intended for filling small and bigger disparities. It is intended for common surface. It has lower adhesion on aluminum and zinc materials. Thanks to low density it is very well sandable with severalfold lower abrasive consumption. It has high resistance of stress on material. There is a minimal increase of weight of construction, so it is suitable for aircraft industry, ship-building sector and auto-tuning.
ENVIRONMENT
The putty must not be used for filling places which are in direct contact with food and drinking water.
VOC VOLUME
VOC = 12 g / l This product complies with EU Directive (2004/42/EC), which gives for the preparation of this category (B / b) the limit value of volatile matter content of 250 g / l in finished product.
APPLICATION
Get rid of rust and abrade the bonded surface by sandpaper P80. Surface must be clean, dry and free of dust and grease. For maximum corrosion protection use epoxy or polyurethane basecoat. Do not apply the putty on reactive, single or nitrocellulose basecoats. Apply with a trowel.
HARDENING
The putty is hardened with hardener (PE-initiator, dibenzoyl peroxide, red paste in tube) in weight ratio: - 100 parts of putty : 3 parts of hardener – recommended ratio for temperature 23°C
POT LIFE
The putty is necessary to be used within 5 minutes after mixing with hardener at temperature 23°C and hardening ratio 100:3. Adjusting of the hardening ratio can partly eliminate the influence of temperature on the potlife. At lower temperatures (at least 17°C), the potlife increases, at higher temperatures is reduced. Do not exceed the recommended hardening ratio.
SANDING
The putty is sandable after 20-30 minutes at temperature 23°C and hardening ratio 100:3. Rough sanding begins with sanding paper P80-120 and finishes with sanding paper P240. For sanding is recommended to use rotating or vibrating sander.
UPPER COATINGS
It is possible to use all common paint systems on the putty. The putty withstands temperatures of 80-110 °C.
TOOLS CLEANING
Dirty parts of tools for filling can be cleaned with VARIOL TRIN POLYESTER or nitrothinner C-6000. Only non-hardened putty can be cleaned.
STORAGE
It is necessary to ensure the temperature from +5°C to + 25°C and avoid direct solar radiation during storage and transport. Dash of the resin on the surface of putty is acceptable. We guarantee shelf life and quality of the product for 12 months.
PACKAGING
- 0,6 l, 1,0 l – a can
COLOUR
Light blue
Page 25
TECHNICAL DATA SHEET
VARIOL RAPID R technical description: 10. 10. 2012 DESCRIPTION AND USAGE
RAPID R is middle rough, elastic two-component polyester putty intended for filling of large surfaces during railway carriages repairs. RAPID R is possible to use successfully for filling of various metal products, iron castings or machine exteriors. It is applicable on straightening of disparities on wood (harder kinds), glass fibre, concrete, stone etc. The putty has good filling ability and is well workable and sandable. It excels in toughness, endures big load in bend and stroke during changing of temperatures and vibrations. This putty has the certificate from State Testing Laboratory ČD (Czech railway) for repairs of railway carriages surfaces.
ENVIRONMENT
The putty must not be used for filling places which are in direct contact with food and drinking water.
VOC VOLUME
VOC = 91 g / l This product complies with EU Directive (2004/42/EC), which gives for the preparation of this category (B / b) the limit value of volatile matter content of 250 g / l in finished product.
APPLICATION
Get rid of rust and abrade the bonded surface by sandpaper P80. Surface must be clean, dry and free of dust and grease. For maximum corrosion protection use epoxy or polyurethane basecoat. Do not apply the putty on reactive, single or nitrocellulose basecoats. Apply with a trowel.
HARDENING
The putty is hardened with hardener (PE-initiator, dibenzoyl peroxide, red paste in tube) in weight ratio: - 100 parts of putty : 2 parts of hardener – recommended ratio for temperature 23°C
POT LIFE
The putty is necessary to be used within 30 minutes after mixing with hardener at temperature 23°C and hardening ratio 100:2. Adjusting of the hardening ratio can partly eliminate the influence of temperature on the potlife. At lower temperatures (at least 17°C), the potlife increases, at higher temperatures is reduced. Do not exceed the recommended hardening ratio.
SANDING
The putty is sandable after 6-8 hours at temperature 23°C and hardening ratio 100:2. Rough sanding begins with sanding paper P80-120 and finishes with sanding paper P180-240. For sanding is recommended to use rotating or vibrating sander.
UPPER COATINGS
It is possible to use all common paint systems on the putty. The putty withstands temperatures of 80-110 °C.
TOOLS CLEANING
Dirty parts of tools for filling can be cleaned with VARIOL TRIN POLYESTER or nitrothinner C-6000. Only non-hardened putty can be cleaned.
STORAGE
It is necessary to ensure the temperature from +5°C to + 25°C and avoid direct solar radiation during storage and transport. Dash of the resin on the surface of putty is acceptable. We guarantee shelf life and quality of the product for 12 months.
PACKAGING
- 2 kg, 5 kg, 15 kg – a can - 3 kg – a can for batching plant
COLOUR
Light gray
Page 26
TECHNICAL DATA SHEET
VARIOL LONG technical description: 10. 10. 2012 DESCRIPTION AND USAGE
LONG is soft surface two-component putty intended for filling of dimensional workpieces, machine parts and large surfaces during the repairs of machine exteriors. LONG is possible to use successfully also for filling of various metal products or iron castings. The putty has thinner consistence and it is very well workable. It is applicable also for straightening of disparities on wood (harder kinds), glass fibre, concrete, stone etc. The putty has excellent adhesion on various surfaces, good elasticity, is easy applicable and excellent sandable.
ENVIRONMENT
The putty must not be used for filling places which are in direct contact with food and drinking water.
VOC VOLUME
VOC = 53 g / l This product complies with EU Directive (2004/42/EC), which gives for the preparation of this category (B / b) the limit value of volatile matter content of 250 g / l in finished product.
APPLICATION
Get rid of rust and abrade the bonded surface by sandpaper P80. Surface must be clean, dry and free of dust and grease. For maximum corrosion protection use epoxy or polyurethane basecoat. Do not apply the putty on reactive, single or nitrocellulose basecoats. Apply with a trowel.
HARDENING
The putty is hardened with hardener (PE-initiator, dibenzoyl peroxide, red paste in tube) in weight ratio: - 100 parts of putty : 2 parts of hardener – recommended ratio for temperature 23°C
POT LIFE
The putty is necessary to be used within 30 minutes after mixing with hardener at temperature 23°C and hardening ratio 100:2. Adjusting of the hardening ratio can partly eliminate the influence of temperature on the potlife. At lower temperatures (at least 17°C), the potlife increases, at higher temperatures is reduced. Do not exceed the recommended hardening ratio.
SANDING
The putty is sandable after 4-5 hours at temperature 23°C and hardening ratio 100:2. Rough sanding begins with sanding paper P80-120 and finishes with sanding paper P180-240. For sanding is recommended to use rotating or vibrating sander.
UPPER COATINGS
It is possible to use all common paint systems on the putty. The putty withstands temperatures of 80-110 °C.
TOOLS CLEANING
Dirty parts of tools for filling can be cleaned with VARIOL TRIN POLYESTER or nitrothinner C-6000. Only non-hardened putty can be cleaned.
STORAGE
It is necessary to ensure the temperature from +5°C to + 25°C and avoid direct solar radiation during storage and transport. Dash of the resin on the surface of putty is acceptable. We guarantee shelf life and quality of the product for 12 months.
PACKAGING
- 2 kg, 5 kg, 15 kg – a can - 3 kg – a can for batching plant
COLOUR
Light gray
Page 27
TECHNICAL DATA SHEET
VARIOL LAMINO
resin / repair box technical description: 10. 10. 2012
DESCRIPTION AND USAGE
LAMINO is a two-component polyester resin / repair set for small repairs. The repair set is used for repairing of holes or splits in metal or laminate materials as for example rusted up places on car bodies, boats or camping caravans. Glass texture soaked with polyester resin forms steady base for application of next layers of putties during the repair.
ENVIRONMENT
This product must not be used for filling places which are in direct contact with food and drinking water.
VOC VOLUME
VOC = 62 g / l This product complies with EU Directive (2004/42/EC), which gives for the preparation of this category (B / b) the limit value of volatile matter content of 250 g / l in finished product.
APPLICATION
Repaired surface must be without rust and old coatings. It is necessary to degrease the surface carefully, eventually to roughen with sanding paper: - glass fibre – sanding paper P40 - steel, galvanized steel – sanding paper P60 Before starting the repair it is necessary to cut out suitable piece of glass texture. Prepared mixture of resin and hardener is applicated on repaired place by brush, then the glass texture is laid. After that also the glass texture shall be soaked. It is possible to lay more layers of glas texture, if it is necessary.
HARDENING
The putty is hardened with hardener (PE-initiator, dibenzoyl peroxide, red paste in tube) in weight ratio: - 100 parts of putty : 2 parts of hardener – recommended ratio for temperature 23°C
POT LIFE
The putty is necessary to be used within 8-10 minutes after mixing with hardener at temperature 23°C and hardening ratio 100:2. Adjusting of the hardening ratio can partly eliminate the influence of temperature on the potlife. At lower temperatures (at least 17°C), the potlife increases, at higher temperatures is reduced. Do not exceed the recommended hardening ratio.
SANDING
Repaired place is sandable after 40 minutes at temperature 23°C and hardening ratio 100:2. For dry sanding it is used the sanding paper P80 – P180.
UPPER COATINGS
The repair should be finished with putties VARIOL FLAT or VARIOL LENT, eventually with extra soft putty VARIOL FIN, which alignes the margins finely. We recommend also to use spray putty or filler. After that it is possible to use all common paint systems. Hardened resin resists common baking temperatures 80 – 110°C.
TOOLS CLEANING
Dirty parts of tools for filling can be cleaned with VARIOL TRIN POLYESTER or nitrothinner C-6000. Only non-hardened putty can be cleaned.
STORAGE
It is necessary to ensure the temperature from +5°C to + 25°C and avoid direct solar radiation during storage and transport. Dash of the resin on the surface of putty is acceptable. We guarantee shelf life and quality of the product for 12 months.
PACKAGING
Resin: 1 l, 5 l – a can Repair box: 0,25 kg of resin – a can + 0,2 m2 of glass texture under the plastic cap
COLOUR
Light yellow transparent liquid
Page 28
TECHNICAL DATA SHEET
VARIOL FINAL technical description: 10. 10. 2012 DESCRIPTION AND USAGE
FINAL is a two-component spray putty intended for unification of surface between filled and no filled places, or for straightening of surface on car bodies. It is used for formation of equable layer of putty on whole car body, which is necessary before application of filler and subsequently upper paint. After hardening FINAL provides equable layer, which is easily sand able and also stays hard, tough, resistant to bend, stroke and vibrations. Also suitable for surfaces of hardwood and MDF-boards.
ENVIRONMENT
The putty must not be used for filling places which are in direct contact with food and drinking water.
VOC VOLUME
VOC = 220 g / l This product complies with EU Directive (2004/42/EC), which gives for the preparation of this category (B / b) the limit value of volatile matter content of 250 g / l in finished product.
APPLICATION
Get rid of rust and abrade the bonded surface by sandpaper P80. Surface must be clean, dry and free of dust and grease. For maximum corrosion protection use epoxy or polyurethane basecoat. Do not apply the putty on reactive, single or nitrocellulose basecoats. For application we recommend to use the nozzle 1,8-3,0 mm and the air pressure 0,40,6 MPa. Spray putty can forms dry layer in thickness up to 1000 µm. We recommend to use the thinner VARIOL TRIN POLYESTER for modification of consistence before usage. Stir the content of the can well before usage!
HARDENING
The putty is hardened with hardener (INICIÁTOR 40, transparent liquid) in weight ratio: - 100 parts of putty : 5 parts of hardener – recommended ratio for temperature 23°C The mixture must be homogenized perfectly and filtered.
POT LIFE
The putty is necessary to be used within 40 minutes after mixing with hardener at temperature 23°C and hardening ratio 100:5. Adjusting of the hardening ratio can partly eliminate the influence of temperature on the potlife. At lower temperatures (at least 17°C), the potlife increases, at higher temperatures is reduced. Do not exceed the recommended hardening ratio.
SANDING
The putty is dry against dust after 60 minutes and sand able after 120 minutes at temperature 23°C and hardening ratio 100:5. This time can be shortened by baking at temperature around 60°C. Dry sanding starts with sanding paper P80 and finishes with sanding paper P120-180. Wet sanding starts with sanding paper P120 and finishes with sanding paper P180-220. We recommend use the rotary or vibratory grinding machine.
UPPER COATINGS
It is possible to use all common paint systems on the putty. The putty withstands temperatures of 80-110 °C.
TOOLS CLEANING
Dirty parts of tools for filling can be cleaned with VARIOL TRIN POLYESTER or nitrothinner C-6000. Only non-hardened putty can be cleaned.
STORAGE
It is necessary to ensure the temperature from +5°C to + 25°C and avoid direct solar radiation during storage and transport. Dash of the resin on the surface of putty is acceptable. We guarantee shelf life and quality of the product for 12 months.
PACKAGING
- 1 kg, 4 kg, 15 kg – a can
COLOUR
White / gray
Page 29
TECHNICAL DATA SHEET
VARIOL FIL 4:1 PREMIUM technical description: 10. 10. 2012 DESCRIPTION AND USAGE
FIL 4:1 PREMIUM is a high quality two-component acryl-urethane filler for car repair and industry. It has a high solid content, excellent flow properties, good stability when applied to vertical surfaces and high filling power. Cures rapidly in larger layers, perfectly sandable. It is an ideal base to ensure a high quality look of painted objects. FIL 4:1 PREMIUM finds wide usage in coating systems for coating fleet Railways, urban transportation and various engineering products. SURFACE
ADHESION
steel
excellent
aluminum (pretreatment required)
excellent
hardwood, concrete
good
plastics (pretreatment required)
good
BKP putties
excellent
laminate
excellent
old coatings
excellent
ENVIRONMENT
The putty must not be used for filling places which are in direct contact with food and drinking water.
VOC VOLUME
VOC = 527 g / l This product complies with EU Directive (2004/42/EC), which gives for the preparation of this category (B /c) the limit value of volatile matter content of 540 g / l in finished product even after dilution in the recommended ratio.
APPLICATION
Surface after filling sand with sandpaper P220-240 and perfectly degrease. It is applicated separately in 2-3 layers (40-60 µm). Each layer must be leaved to draught about 5-10 minutes. Filling system – thin by VARIOL TRIN POLYURETAN (max. 10%) Working viscosity: 4/20°C. circa 19 s Nozzle of spray gun: 1.5 - 1.8 mm Air pressure: 0,3 - 0,4 MPa 1 liter of filler covers about 3,2 m2 in thickness of layer 100 µm.
COVERAGE HARDENING
The filler is hardened with hardener TVRDIDLO 1:4 PREMIUM in volume ratio 4:1 - 4 parts of filler : 1 part of hardener. The mixture must be homogenized perfectly and filtered.
POT LIFE
The filler is necessary to be used within 45 minutes after mixing with hardener at temperature 20°C and hardening ratio 4:1.
SANDING
The filler is sandable after 3 hours at temperature 23°C and thickness of dry layer 150 µm, after 30-40 minutes at temperature 60°C. Dry sanding is done with sanding paper P400-800. Wet sanding is done with sanding paper P600-1000.
UPPER COATINGS
It is possible to use all common paint systems on the filler. The filler withstands temperatures of 80-110 °C.
TOOLS CLEANING
Dirty parts of tools for filling can be cleaned with VARIOL TRIN POLYURETAN or nitrothinner C-6000. Only non-hardened filler can be cleaned.
STORAGE
It is necessary to ensure the temperature from +5°C to + 25°C and avoid direct solar radiation during storage and transport. Store in a cool and dry place. We guarantee shelf life and quality of the product for 12 months.
PACKAGING
- filler 1 l + 0,25 l hardener – a can - filler 4 l + 1 l hardener – a can
COLOUR
Gray / black
Page 30
TECHNICAL DATA SHEET
VARIOL FIL 4:1 NORMAL technical description: 10. 10. 2012 DESCRIPTION AND USAGE
FIL 4:1 NORMAL is a quality two-component acrylic filler for car repair and industry. It has good filling properties and excellent flow properties. Cures rapidly also in larger layers and is perfectly sandable. It is an ideal base to ensure a high quality look of painted objects. SURFACE
ADHESION
steel
excellent
aluminum (pretreatment required)
excellent
hardwood, concrete
good
plastics (pretreatment required)
good
BKP putties
excellent
laminate
excellent
old coatings
excellent
ENVIRONMENT
The putty must not be used for filling places which are in direct contact with food and drinking water.
VOC VOLUME
VOC = 465 g / l This product complies with EU Directive (2004/42/EC), which gives for the preparation of this category (B /c) the limit value of volatile matter content of 540 g / l in finished product even after dilution in the recommended ratio.
APPLICATION
Surface after filling sand with sandpaper P220-240 and perfectly degrease. It is applicated separately in 2-3 layers (40-60 µm). Each layer must be leaved to draught about 5-10 minutes. Filling system – thin by VARIOL TRIN ACRYL (max. 10%) Working viscosity: 4/20°C. circa 22 s Nozzle of spray gun: 1.5 - 1.8 mm Air pressure: 0,3 - 0,4 MPa
COVERAGE
1 liter of filler covers about 5,6 m2 in thickness of layer 100 µm.
HARDENING
The filler is hardened with hardener TVRDIDLO 1:4 NORMAL/PLUS in volume ratio 4:1 - 4 parts of filler : 1 part of hardener. The mixture must be homogenized perfectly and filtered.
POT LIFE
The filler is necessary to be used within 60 minutes after mixing with hardener at temperature 20°C and hardening ratio 4:1.
SANDING
The filler is sandable after 3 hours at temperature 23°C, after 30-40 minutes at temperature 60°C. Dry sanding is done with sanding paper P400-800. Wet sanding is done with sanding paper P600-1000.
UPPER COATINGS
It is possible to use all common paint systems on the filler. The filler withstands temperatures of 80-110 °C.
TOOLS CLEANING
Dirty parts of tools for filling can be cleaned with VARIOL TRIN ACRYL or nitrothinner C-6000. Only non-hardened filler can be cleaned.
STORAGE
It is necessary to ensure the temperature from +5°C to + 25°C and avoid direct solar radiation during storage and transport. Store in a cool and dry place. We guarantee shelf life and quality of the product for 12 months.
PACKAGING
- filler 1 l + 0,25 l hardener – a can - filler 4 l + 1 l hardener – a can
COLOUR
White / gray / black
Page 31
TECHNICAL DATA SHEET
VARIOL FIL 1K technical description: 10. 10. 2012 DESCRIPTION AND USAGE
FIL 1K is a quality one-component acrylic filler for car repair and industry. It has very good filling properties and excellent adhesion. Cures in air, is resistant to weathering and chemical action. Well sandable, is simple to use. It is an ideal base to ensure a high quality look of painted objects. SURFACE
ADHESION
steel
excellent
aluminum (pretreatment required)
excellent
hardwood, concrete plastics (pretreatment required)
good good
BKP putties
excellent
laminate
excellent
old coatings
excellent
ENVIRONMENT
The putty must not be used for filling places which are in direct contact with food and drinking water.
VOC VOLUME
VOC = 533 g / l This product complies with EU Directive (2004/42/EC), which gives for the preparation of this category (B /c) the limit value of volatile matter content of 540 g / l in finished product even after dilution in the recommended ratio.
APPLICATION
Surface after filling sand with sandpaper P220-240 and perfectly degrease. It is applicated separately in 2-3 layers (40-60 µm). Each layer must be leaved to draught about 5-10 minutes. Filling system – thin by VARIOL TRIN ACRYL (max. 10%) Working viscosity: 4/20°C. circa 25 s Nozzle of spray gun: 1.4 - 1.6 mm Air pressure: 0,3 - 0,4 MPa
COVERAGE
1 liter of filler covers about 10 m2 in thickness of layer 40 µm.
HARDENING
As one component does not require a hardener.
SANDING
The filler is sandable after 45-60 minutes at temperature 23°C, after 15 minutes at temperature 60°C. Dry sanding is done with sanding paper P400-800. Wet sanding is done with sanding paper P600-1000.
UPPER COATINGS
It is possible to use all common paint systems on the filler.
TOOLS CLEANING
Dirty parts of tools for filling can be cleaned with VARIOL TRIN ACRYL or nitrothinner C-6000. Only non-hardened filler can be cleaned.
STORAGE
It is necessary to ensure the temperature from +5°C to + 25°C and avoid direct solar radiation during storage and transport. Store in a cool and dry place. We guarantee shelf life and quality of the product for 12 months.
PACKAGING
- 0,8, 5 l – a can
COLOUR
Beige
Page 32
TECHNICAL DATA SHEET
VARIOL TRIN ACRYL technical description: 10. 10. 2012
DESCRIPTION AND USAGE
TRIN ACRYL is a high quality acrylic thinner, which is used for modification of consistence of acrylic fillers and clearcoats. It is suitable into all acrylic coating compositions.
ENVIRONMENT
TRIN ACRYL must not be used for filling places which are in direct contact with food and drinking water.
STORAGE
It is necessary to ensure the temperature +5°C - +20°C and avoid direct solar radiation during storage and transport. Store in dry and cold place. We guarantee shelf life and quality of the product for 12 months.
PACKAGING
- 1,0 l – can - 5,0 l - canister
COLOUR
Transparent
Page 33
TECHNICAL DATA SHEET
VARIOL TRIN POLYESTER technical description: 10. 10. 2012
DESCRIPTION AND USAGE
TRIN POLYESTER is thinner, which is used for thinning of two-component polyester spray putties. It is suitable also for cleaning of working tools polluted by all types of polyester putties.
ENVIRONMENT
TRIN POLYESTER must not be used for filling places which are in direct contact with food and drinking water.
STORAGE
It is necessary to ensure the temperature +5°C - +20°C and avoid direct solar radiation during storage and transport. Store in dry and cold place. We guarantee shelf life and quality of the product for 12 months.
PACKAGING
- 1,0 l – can - 5,0 l - canister
COLOUR
Transparent
Page 34
TECHNICAL DATA SHEET
VARIOL TRIN POLYURETAN technical description: 10. 10. 2012
DESCRIPTION AND USAGE
TRIN POLYURETAN is thinner, which is used for adjusting the consistency of fillers VARIOL FIL 4:1 PREMIUM and VARIOL FIL 2K PUR. It is suitable also for thinning acrylic paints and cleaning of working tools polluted by all types of polyurethane coatings.
ENVIRONMENT
TRIN POLYURETAN must not be used for filling places which are in direct contact with food and drinking water.
STORAGE
It is necessary to ensure the temperature +5°C - +20°C and avoid direct solar radiation during storage and transport. Store in dry and cold place. We guarantee shelf life and quality of the product for 12 months.
PACKAGING
- 1,0 l – can - 5,0 l - canister
COLOUR
Transparent
Page 35
TECHNICAL DATA SHEET
TOPEKOR technical description: 10. 10. 2012
DESCRIPTION AND USAGE
TOPEKOR contains effective preparation for dispersion of anorganic and organic sediments, and inhibitor which protect against corrosion in closed systems of central heating. TOPEKOR can be used also in circulating systems where is the possibility of formation of scale or corrosion.
MECHANISM AND TIME OF EFFICIENCY
Anticorrosive effects of TOPEKOR are based on formation of molecular layer, which avoid access of oxygen (which is dissolved in heating medium) to the surface of heating tube. Prevent sedimentation effect is based on slow chemical dissolving of sediments in slightly acid environment. The time of TOPEKOR treatment is not exactly limited, because dissolving of harder sediments (mainly in older systems) goes slowly and in the long term. Function of TOPEKOR in central heating system shows itself in better control over regulation valves and advanced efficiency of furnace.
DOSAGE
Content of the container (500 ml) guarantee perfect protection of system with capacity up to 400 litres of water during minimally two years. TOPEKOR fundamentally improves heating efficiency of system thanks to removing of scale and enlarges its shelf life with limitation of corrosion. TOPEKOR should be dosed into circulating system in the beginning of heating season to obtain perfect shuffle by the water circulation. Content of the container must be shaked before usage and then filled into the heating system. Changing of the water is not necessary. Dosage should be done in rubber gloves. In case of protection of old systems highly polluted with scale, where the protection hasn´t been done before, we recommend to drain the system off and fill again with new dose of TOPEKOR after further 2 months, when the bigger sediments are dissolved.
ELECTROCHEMICAL STABILITY
The preparation TOPEKOR doesn´t advanced the conductivity of heating medium and also does not implement ions inside, which should influence electrochemical balance of the system. This is fundamental difference against common anticorrosive preparatives.
COMPATABILITY WITH MATERIALS
TOPEKOR does not work aggresively on common materials as: iron, steel, cast iron, zinc coating, copper, polyethylene, polypropylene, rubber, sealing rubbers, teflon. It gets on glycols in water antifreezing systems.
ENVIRONMENT
TOPEKOR is ecological, biodegradable preparation. Draining of the central heating system into canalization has no harmful influence on environment.
STORAGE AND PACKAGING
Protect against freezing temperatures. We guarantee shelf life and quality of the product for 24 months. Packaging: - 500ml – plastic container (different container according to agreement)
Page 36