CDP Weld Cladded Plates: Traditional welded plate offers the optimum resistance to abrasion, erosion and metal-to-metal friction. Available as-welded in straight or XuperWave. PLATE THICKNESS
WEAR PLATE
DESCRIPTION
CDP 395N
395 NanoPlate is based on the science and engineering of ultra-fine, submicron grain structures. NanoAlloy provides high hardness within a ductile matrix resistant to moderate impact. Hardness is HRC 68-71.
CDP 4603
CDP 4624
Optimized chromium carbide plate for general use in abrasion and erosion applications. The carbides represent at least 40% (primary solidified) of the weld deposit. Hardness is HRC 55-59. Affordable chrome carbide plate that maintains structural integrity in situations involving abrasion, light impact and heat. Hardness is HRC 58-61.
CDP 4666
Complex chromium carbide plate for severe wear applications. Used for applications where high stress abrasion is involved. High hardness of HRC 61-64 with a primary carbide distribution of 57%
CDP 4923
Highest impact resistant, welded overlay plate, on the market today. This plate has titanium carbides that resist the combination of impact and abrasion. HRC 54-57
Base metal
Coating
Total
6mm
4mm
10mm (3/8”)
8mm
5mm
13mm (1/2”)
12mm
7mm
19mm (3/4”)
6mm
4mm
10mm (3/8”)
8mm
5mm
13mm (1/2”)
12mm
7mm
19mm (3/4”)
6mm
4mm
10mm (3/8”)
8mm
5mm
13mm (1/2”)
12mm
7mm
19mm (3/4”)
5mm
3mm
8mm (5/16”)
6mm
4mm
10mm (3/8”)
8mm
5mm
13mm (1/2”)
12mm
7mm
19mm (3/4”)
8mm
5mm
13mm (1/2”)
12mm
7mm
19mm (3/4”)
CDP Powder Plates: Metal alloy powder is vacuum fused to steel plate creating a uniform hardfacing with very few stress relief cracks. Powder plates provide maximum protection even with the thinnest of deposits, making this plate lightweight, easy to handle and easily formed into a tight radius. WEAR PLATE
DESCRIPTION
PLATE THICKNESS Base metal
Coating
Total
CDP 112
CDP 112 contains densely packed tungsten carbide particles in a hard, nickel alloy, corrosion resistant HRC 58 matrix. Superior performance in a light weight plate.
4mm
2mm
6mm (1/4”)
CDP 212
CDP 212 Contains evenly distributed tungsten carbide and chromium carbide particles in an HRC 58, iron alloy matrix. This economical and lightweight powder wear plate offers a high abrasion and erosion resistance when it is used in non corrosive conditions.
4mm
2mm
6mm (1/4”)
Plasma Transferred Arc (PTA) Plates: PTA welded plates contain the highest carbide content with very low dilution. They are the ultimate solution for combined erosive and abrasive wear in the most demanding applications. PLATE THICKNESS
WEAR PLATE
CDP 6503
A high performance, 65% tungsten carbide wear plate for the ultimate resistance in the most demanding wear and corrosion applications. A high concentration of tungsten carbide, distributed in a tough, nickel based alloy for low and high stressed abrasion. Hardness is HRC 61-65.
Base metal
Coating
Total
5mm
2mm
7mm (5/16”)
6mm
3mm
9mm (3/8”)
Stronger, with Eutectic
www.eutecticusa.com