Díptico Hot Melt SIMES 2015

8 mm 5/16”

12 mm 1/2”

Since 1951

15 mm 5/8”

Your complete HOT MELT solution Full range

Service

Quality

18 mm 3/4”

43 mm 1 11/16”

AUTOMOTIVE INDUSTRY

CARDBOARD PACKAGING

CRATES

FURTNITURE FRAMEWORK

GENERAL INDUSTRY

MATTRESSES

sticks & slugs 43 mm 1 11/16”

EVA (Ethylene Vinyl Acetate)

12 mm 1/2”

8 mm 5/16”

18 mm 3/4”

15 mm 5/8”

08–––

12 – – –

15 – – –

18 – – –

43–––

100 mm - 3 15/16”

100 mm - 3 15/16” 200 mm - 7 7/8” 300 mm - 11 13/16”

300 mm - 11 13/16”

300 mm - 11 13/16”

43 mm - 1 11/16”

SIMHM12 P 100 W

SIMHM12 P 180 W

SIMHM12 I 300 W

SIMHM12 HD 400 W

SIMHM18 HD 600 W

220 - 240 V / 50 Hz 100 - 120 V / 60 Hz

220 - 240 V / 50 Hz 100 - 120 V / 60 Hz

220 - 240 V / 50 Hz 100 - 120 V / 60 Hz

220 - 240 V / 50 Hz 100 - 120 V / 60 Hz

220 - 240 V / 50 Hz 100 - 120 V / 60 Hz

100 W

180 W

300 W

400 W

600 W

30 g / min 1.05 oz / min

45 g / min 1.58 oz / min

1 - 1.5 Kg / Hr 2.20 - 3.30 lb / Hr

1.5 - 2 Kg / Hr 3.30 - 4.41 lb / Hr

2 - 2.5 kg / Hr 4.41 - 5.51 lb / Hr

193 ºC 380 ºF

193 ºC 380 ºF

140 °C - 230 °C 284 ºF - 446 ºF

140 °C - 220 °C 284 ºF - 428 ºF

140 °C - 230 °C 284 ºF - 446 ºF

Ø 12 mm Ø 1/2”

0.539 Kg 1.18 lb

0.681 Kg 1.50 lb

0.914 Kg 2 lb

0.907 Kg 2 lb

Ø 12 mm Ø 1/2”

Ø 12 mm Ø 1/2”

Ø 12 mm Ø 1/2”

Ø 18 mm Ø 3/4”

AUTOMOTIVE INDUSTRY

TRANSLUCENT

CARDBOARD PACKAGING

CRATES

TRANSPARENT

FURTNITURE FRAMEWORK

WHITE

GENERAL INDUSTRY

amber

CHEMICAL BASE

MATTRESSES

brown

ivory

electric tool

yellow

VOLTAGE

SILVER GLITTER

POWER

GOLD GLITTER

PERFORMANCE

TEMPERATURE

FLUOR / acid COLORS

COLORS

WEIGHT

diameter

FORMULA

USE

VISCOSITY (180 ºC)

OPEN TIME

SETTING TIME

SOFTENING POINT

APPLICATION TEMPERATURE

001

Universal - Cold environment

10,000 ± 3,000 cP

45” - 55”

25” - 30”

85 ± 5 ºC

170 ºC - 210 ºC

009LC

General use

12,000 ± 3,000 cP

10” - 20”

15” - 20”

90 ± 5 ºC

180 ºC - 210 ºC

010LC

General use

12,000 ± 3,000 cP

25” - 35”

15” - 20”

90 ± 5 ºC

180 ºC - 210 ºC

020

Porous materials

12,000 ± 3,000 cP

25” - 35”

15” - 20”

90 ± 5 ºC

180 ºC - 210 ºC

021

Porous materials - Fast bonding

2,200 ± 500 cP

10” - 12”

3” - 4”

105 ± 5 ºC

160 ºC - 200 ºC

022

Porous materials - Fast bonding

2,600 ± 500 cP

8”

3”

106 ± 5 ºC

160 ºC - 200 ºC

030

Universal

10,000 ± 3,000 cP

40” - 50”

20” - 25”

87 ± 5 ºC

170 ºC - 210 ºC

031

Universal

7,500 ± 2,000 cP

30” - 35”

15”

87 ± 4 ºC

160 ºC - 200 ºC

040

Universal

10,000 ± 3,000 cP

40” - 50”

20” - 25”

87 ± 5 ºC

160 ºC - 200 ºC

048

Universal

10,000 ± 3,000 cP

40” - 50”

20” - 25”

87 ± 5 ºC

170 ºC - 210 ºC

050

Ceramics - Metals - Plastics

9,000 ± 2,500 cP

30” - 40”

15” - 20”

88 ± 5 ºC

180 ºC - 210 ºC

055

Universal

8,000 ± 2,500 cP

30” - 40”

15” - 25”

90 ± 5 ºC

180 ºC - 210 ºC

073

Universal

10,000 ± 3,000 cP

40” - 50”

20” - 25”

87 ± 5 ºC

170 ºC - 210 ºC

075

Universal “Low Melt”

4,000 ± 1,200 cP

25” - 30” * 40” - 50” **

20” * 30” **

75 ± 3 ºC

120 ºC - 180 ºC

087

Universal - Cold environment

10,000 ± 3,000 cP

45” - 55”

25” - 30”

85 ± 5 ºC

170 ºC - 210 ºC

094

Universal

10,000 ± 3,000 cP

40” - 50”

20” - 25”

87 ± 5 ºC

170 ºC - 210 ºC

095

Porous materials - Fast bonding

5,000 ± 1,500 cP

15” - 25”

10” - 15”

98 ± 6 ºC

170 ºC - 210 ºC

101

Wood - Ceramics - Plastics

7,000 ± 2,500 cP

30” - 40”

15” - 20”

90 ± 5 ºC

170 ºC - 210 ºC

102

General use

8,000 ± 2,500 cP

25” - 30”

15” - 20”

90 ± 5 ºC

170 ºC - 210 ºC

110

Universal

10,000 ± 3,000 cP

40” - 50”

20” - 25”

87 ± 5 ºC

170 ºC - 210 ºC

131

Universal

10,000 ± 3,000 cP

40” - 50”

20” - 25”

87 ± 5 ºC

170 ºC - 210 ºC

135

Universal

10,000 ± 3,000 cP

40” - 50”

20” - 25”

87 ± 5 ºC

170 ºC - 210 ºC

136

Universal

10,000 ± 3,000 cP

40” - 50”

20” - 25”

87 ± 5 ºC

170 ºC - 210 ºC

220

Universal

4,000 ± 1,200 cP

15” - 25”

10” - 15”

100 ± 6 ºC

170 ºC - 210 ºC

260

Ceramics - Metals - Plastics

8,500 ± 3,000 cP

20” - 30”

–

90 ± 5 ºC

170 ºC - 210 ºC

COLOR

* – at 120 ºC / ** – at 180 ºC

INDUSTRIAL HM

FORMULA

BASIS

USE

10084

Rubber

Bonding of large areas

10088

Rubber

10089

VISCOSITY (180 ºC)

OPEN TIME

SETTING TIME

SOFTENING POINT

APPLICATION TEMPERATURE

800 ± 300 cP

Permanent

–

70 ± 5 ºC

140 ºC - 170 ºC

Bonding of large areas

1,000 ± 300 cP

Permanent

–

75 ± 5 ºC

145 ºC - 175 ºC

Rubber

Bonding of large areas

1,600 ± 400 cP

Permanent

–

80 ± 5 ºC

150 ºC - 175 ºC

10090

Rubber

Bonding of large areas

2,100 ± 400 cP

Permanent

–

80 ± 5 ºC

160 ºC - 180 ºC

10302

Rubber

Bonding of large areas

1,100 ± 300 cP

Permanent

–

70 ± 5 ºC

140 ºC - 170 ºC

10606

Polyolefine

Bonding of large areas

2,500 ± 500 cP

120”

–

70 ± 5 ºC

150 ºC - 180 ºC

10607

Polyolefine

Bonding of large areas

2,500 ± 500 cP

120”

–

70 ± 5 ºC

150 ºC - 180 ºC

EXPORT export@grupodesa.es

T +34 948 33 52 66

www.simes.es/hotmelt/en

F +34 948 33 02 53 www.simes.es /hotmelt/en/

COLOR