Widespread Blackout Triggers Study Of Contaminated Wet Snow On Insulator Strings

Widespread Blackout Triggers Study Of Contaminated Wet Snow On Insulator Strings

TESTING

Widespread Blackout triggers study of contaminated Wet snoW on insulator strings

On 22 Dec. 2005, a severe snowstorm in northern Japan led to one of the country’s worst long-term outages in decades and impacted the Niigata Kaetsu region supplied by Tohoku Electric Power Co. About 650,000 households were affected over a maximum duration of as much as 31 hours. For a country such as Japan, with among the highest reliability levels in the world, this was truly an extraordinary event.

The massive blackout was induced by wet snow mixed with sea salt that had packed the sheds of porcelain long rod insulators on both 66 kV and 154 kV lines. Conductor galloping along 275 kV transmission lines also contributed to the scale of the problem. In this case, the wet snow accreted on insulators and filled the gaps between sheds due to the effect of strong winds. Because the snow contained large amounts of sea salt, the insulation strength of the strings deteriorated rapidly and led to numerous flashovers – but in a way quite

96

INMR® Q2 2010

INMR Issue 88 (2).indd 96

different from the better-known phenomena of ice accretion or snow cover on insulator strings.

While much research has been performed on ice accretion/snow accumulation on insulators, knowledge related to the effect of wet snow containing contamination such as sea salt is still comparatively rare. More research is therefore necessary to clarify the mechanisms of failure and establish the most effective countermeasures.

This article, an edited version of a contribution by Manabu ‘Gaku’ Sakata of Tohoku Electric Power and Hiroya Homma of Japan’s Central Research Institute of Electrical Power Industry (CRIEPI), provides a brief overview of the event. It also discusses the properties of wet snow accretion on insulator strings based on the results of artificial wet snow tests. All this was part of a larger project also dealing with wet snow accretion on conductors as well as conductor galloping.

widESprEad blackOUt triGGErS StUdy Of cOntaminatEd wEt SnOw On inSUlatOr StrinGS

5/15/10 8:51:08 PM

Introduction

This event was

In late December of 2005, a powerful low-pressure system from induced by heavy, the Pacific moved south to north high conductivity along the east coast of Japan’s main island while another similar system snow combined with in the Sea of Japan crossed the island. Ambient temperatures in the strong winds – a Niigata Kaetsu area, on the island’s northwest, stabilized in the range climatic condition that of 0 to +2°C with a combination of heavy precipitation and wind. Total is quite different from precipitation and maximum 10 min. average wind velocity were 26 mm and that which usually 14 m/sec respectively (with an overall maximum wind speed of over 25 m/ deposits ice or snow sec). Cascading electrical failures on 66 kV and 154 kV lines started just cover on insulators. before 09:00 and resulted in numerous tripped lines. At the same time, some 275 kV transmission lines also began wind direction. These shapes of snow to trip out due to conductor galloping. on insulator strings are quite different Eventually, 30 transmission lines and from those that result from simple ice 49 circuits were affected. accretion or snow cover. For example, the volume density of the packed Maintenance workers discovered snow ranged from 0.54 to 0.94g/cm3 that many of the porcelain long rod while its maximum conductivity was insulators used on the affected 66 kV and 154 kV lines were packed with wet approximately 0.2 mS/cm. snow. Figs.1a and 1b show examples The worst of the weather ended before of this on insulator strings as well as nightfall and restoration work began on a gap-type arrester. The shapes of at midnight. More than 2500 workers packed snow on insulators in some climbed the towers and removed the cases were cylindrical while in other packed snow from insulator surfaces cases were eccentric pennant into the

by hand. This proved very difficult since the wet snow had by then nearly transformed into ice and it took many hours for the affected electrical system to again be fully operational.

During restoration, numerous traces of power arcs on insulator surfaces and hardware were observed on both horizontally and vertically mounted insulators, including V-strings. These were found over a broad area, even as much as 30 to 40 km inland. In fact, measured conductivities of the packed snow were actually highest in this area as sea salt was apparently carried inland by the powerful winds.

Tohoku Electric Power Co. completed change-out of the long rod insulators of one circuit in the affected area to cap & pin strings and have since adopted the same countermeasure in other regions where similar events seem possible in the future.

Impact on Insulators of Wet Snow with Sea Salt This blackout event was induced by heavy, high conductivity snow combined with strong winds – a climatic condition quite different from that which usually deposits ice accretion or snow cover. Similarly, the affected lines ran along coastal and

Arrester

Fig. 1a: Examples of packed snow on horizontally-mounted long rod insulator strings.

Long rod

Fig. 1b: Example of packed snow on vertically mounted long rod insulator strings and gap type arresters.

widESprEad blackOUt triGGErS StUdy Of cOntaminatEd wEt SnOw On inSUlatOr StrinGS

INMR Issue 88 (2).indd 97

Q2 2010 INMR®

97

5/15/10 8:51:10 PM

Table 1: Typical Features of Snow and Ice Accretions on Insulator Strings Items

Wet Snow Packed with Sea salt

Ice Accretion

Covered Snow

Temperature

-5 to +2°C

-10 to 0°C

Below 0°C

Precipitation

Large

Depends on case

Very large

Wind

More than 10 m/sec of sea wind

Depends on case

Almost zero

Affected areas

Area facing Sea of Japan West coast of Norwegian Sea

Cold district such as high altitude area

Areas with heavy snow

Quality of snow

Very wet, high volume density

Ice, very high volume density

Dry, low volume density

Climate

Contamination

Very severe

Depends on case

Very light

Flashover timing

During snow accretion

After sunrise or as temperatures rise

After sunrise or as temperatures rise

Examples of snow or ice accretion

See fig.1a and b

(Example of in-cloud icing)

inland plains instead of traversing snow-covered mountains. Moreover, the electrical failures occurred during the snow accretion process itself whereas failures due to simple ice accretion and snow cover usually take place after sunrise as ambient temperatures begin to increase. It can therefore be concluded that the phenomena behind this event are quite distinct from the better-known ice accretion or covered snow that occurs on insulator strings.

Table 1 summarizes the typical features of wet snow packed with sea salt compared with simple ice accretion and covered snow.

Snow Mesh

Wind

Wind generator

Insulator sample

Fig. 2a: Schematic of wind generator.

Figure 3 shows a horizontally mounted long rod porcelain insulator after the test. Although a small number of snow particles were attached to its surface, these never grew into a large-scale accretion. This finding agrees with service experience that indicates outages caused by snow packed with sea salt are induced only by wet snow.

Figures 2a and 2b show a schematic of the wind generator and test set-up.

98

INMR® Q2 2010

INMR Issue 88 (2).indd 98

Table 2 shows the types of insulators used in the test. The 66 kV porcelain long rod, cap & pin and polymeric insulators were all tested in both horizontal and vertical configurations and their snow accretion properties studied and compared.

Test Results

Since dealing with this type of problem requires an understanding of the basic properties of the process, an artificial wet snow accretion test was carried out in January 2008 to clarify the mechanism of failure caused by wet snow packed with sea salt. The purpose of the test, which took place at a wind generator test station in Niigata, was to evaluate the basic properties of wet snow accretion on insulators having different shed profiles. As experience with packed wet snow is still limited, the test was performed qualitatively.

Both dry and wet types of snow were

used for the test, with the difference between the two consisting only of its liquid water content. LWC was adjusted by putting natural snow into a test room where ambient temperature was kept around 2°C. While the LWC of natural snow is about 0%, the LWC after adjustment was approximately 5 to 8%.

Fig. 2b: Test set up.

The process of snow accretion on conductors is already quite well known and is the result of two different combined mechanisms: one sees the snow accreted onto the conductor surface sliding slowly along the strands from its weight; the other sees the conductor itself rotate due to the weight of accreted snow. In the case

widESprEad blackOUt triGGErS StUdy Of cOntaminatEd wEt SnOw On inSUlatOr StrinGS

5/15/10 8:51:11 PM

Table 2: Specifications of Insulators Tested Items

Long Rod 8A

Cap & Pin 250 mm×6

Polymeric

Total Length

1175 mm

876 mm

1200 mm

Creepage

2470 mm

1680 mm

2640 mm

Shed Diameter

160 mm

254 mm

135 mm

Core Rod Diameter

80 mm

-

30 mm

Shed Spacing

40 mm

170 mm

65 mm

Service experience indicates

wind Fig. 3: Snow accretion for horizontally-mounted long rod insulator with dry snow (after the test)

that outages caused by snow packed with sea salt are induced only by wet snow.

of insulators, the process is basically the same although, since insulator strings are fixed to towers, the latter mechanism clearly does not apply.

In the case of the wet snowstorm in the Niigata area, the cylinder-like shape of packed snow was observed on both horizontally and vertically mounted long rod insulators.

The shape of packed snow in this test, however, was developed on only the windward side of the insulator and therefore did not exactly reproduce the shape of packed snow observed in the field. On the other hand, the eccentric pennant shape of packed snow into the wind direction was also found on a polymeric gap type arrester during the Niigata storm. The differences in formation conditions and processes between the cylindrical shape and the eccentric pennant into the wind is not yet clear and will be left for future research.

Three important points were confirmed during this test.

Fig. 4a: Snow accretion on horizontally mounted long rod insulator (after about 20 min).

Fig. 4b: Windward side (after the test).

Fig. 4c: Leeward side (after the test).

1. The time for vertically mounted insulators to be bridged between the sheds was shorter than for horizontally mounted ones. In the vertical arrangement, the upper parts of sheds are quickly covered with snow and the sheds are easily bridged.

This suggests that I-strings may be more prone to failure than either tension or dead-end strings. At the same time, many traces of power arcs were also found on horizontal insulator strings during the wet snowstorm. In this respect, field experience does not agree with test results and electrical failures may be related not only to wet snow accretion but also to various flashover mechanisms that still need to be clarified.

2. Movement of water to the bottom of packed snow was seen in this case (see Fig. 7 and 8) and could be related to the subsequent flashover mechanism.

Fig. 4d: Packed snow after part is removed.

widESprEad blackOUt triGGErS StUdy Of cOntaminatEd wEt SnOw On inSUlatOr StrinGS

INMR Issue 88 (2).indd 99

Q2 2010 INMR®

99

5/15/10 8:51:12 PM

Fig. 5 depicts the mechanism by which wet snow accretion forms a cylindrical shape.

shed

cap

snow

snow

(a) Initial

(b) Snow accretion starts

(c) Snow rotates by 45°

(d) Snow rotates by 90°

(e) Snow rotates by 180°

(f) Snow rotates by 270°

Fig. 5: Process of forming cylindrical snow on horizontally mounted long rod insulator (seen from the axis of insulator).

3. Once snow does bridge sheds, the packed snow cannot easily be removed from the insulator surface whereas before bridging the snow tends to be blown away by wind. Nevertheless, snow accretion progresses quite slowly along the insulator’s axial direction and this effect can be explained by the fact that the adhesive tensile strength of snowflakes is greater than their adhesive shear strength. Long rod insulators are not only more easily bridged by snow but the accreted snow is at the same time not easily removed by wind-induced vibrations in the field.

A test with wet snow (LWC 5% and volume density 0.3 g/cm3) was also carried out for a horizontally mounted cap & pin insulator. In this case, the snow accreted on the cap parts first but tended to be easily removed by its weight so that it never grew to bridge the sheds. Figs. 9 a & b show the snow accretion after the test. Since a cap &

100 INMR® Q2 2010

INMR Issue 88 (2).indd 100

Fig. 6b

Fig. 6a: Snow accretion on vertically mounted long rod insulator (after test).

Fig. 6c: Examples of snow removed from insulator after test.

widESprEad blackOUt triGGErS StUdy Of cOntaminatEd wEt SnOw On inSUlatOr StrinGS

5/15/10 8:51:14 PM

Fig. 7: Movement of water inside snow

Fig. 8: Packed snow can rotate slowly but not be taken away easily

Fig: 9a water

Fig: 9b Fig: 7

Fig: 8

pin type insulator has a relatively larger shed diameter and spacing, snow accretion cannot easily grow to bridge sheds and tends to be removed by its weight.

A vertically mounted cap & pin insulator string was also tested (LWC 7% and volume density 0.4 g/cm3). At first, the snow accreted on the upper parts of the sheds and finally bridged the sheds in a packed condition. Fig. 10a shows the snow accretion just before bridging while Fig. 10b shows the comparison between the cap & pin and the porcelain long rod insulator tested at the same time. The time needed to bridge the cap & pin type was about 50 minutes but only about 10 min for the long rod.

Fig. 9b: Accreted snow on horizontally mounted cap & pin insulator (after the test).

about 20-30 min. versus about 10 min. for the porcelain long rod. Since shed spacing for the polymeric type is larger than for the porcelain long rod, the time to bridge it is about two to three times longer.

During the test, the polymeric insulator maintained high hydrophobicity (Fig. 13), but this property seemed to have little effect on snow accretion. In this regard it can be concluded that shed profile appears to be more important than shed material.

Conclusions

1. Electrical failures of insulators by wet snow packed with sea-salt can be induced by unusual climatic conditions Finally, tests were performed involving wet snow (LWC 7 % involving a great deal of wet snow with high conductivity and volume density 0.3 g/cm3) on a horizontally mounted combined with heavy winds. This phenomenon is quite polymeric insulator over a duration of 30 minutes. The distinct from the more commonly observed ice accretion or snow accreted on the core rod first and then gradually covered snow on insulator strings. became packed, followed by bridging between the sheds.

Figs. 11a & b show the snow accretion after the test. The 2. In order to clarify the failure mechanisms and establish shape of packed snow was like eccentric pennants into the effective countermeasures, the basic properties of the packed snow need to be better understood. To this end, artificial wind. However, the snow tended to be easily blown off by snow accretion tests have been performed on a qualitative wind in comparison with the porcelain long rod insulator.

This might the result of a smaller core rod for the polymer basis as a first step toward future quantitative studies. in comparison with the long rod insulator – which results in a smaller area of contact between the surface and snow 3. In these tests, several basic properties of packed wet particles. As a result, in the case of polymeric insulators snow were demonstrated and issues for future research the shape of accreted snow was not cylinder-like but rather identified, including: eccentric perpendicular into the wind. a) The packed snow was reproduced on insulators using The same test with wet snow (LWC 4 % and volume density wet snow (LWC of 5-8%) whereas no snow accretion was 0.3g/cm3) was then carried out for a vertically mounted seen using dry snow (LWC of 0%). This corresponds well polymeric insulator for 50 min. A porcelain long rod with service experience that indicates that such outages insulator was also set in parallel for comparison. At first, the are caused by packed, wet snow laden with contamination snow accreted on the upper part of the sheds, (Fig. 12a) such as sea salt. and finally bridged and packed between the sheds. b) The cylinder-like shape of packed snow occurring The time needed to bridge the polymeric insulator was in Niigata and triggering the widespread blackout of

102 INMRÂŽ Q2 2010

INMR Issue 88 (2).indd 102

widESprEad blackOUt triGGErS StUdy Of cOntaminatEd wEt SnOw On inSUlatOr StrinGS

5/15/10 8:51:17 PM

Fig. 10a: Accreted snow on vertically mounted cap & pin insulator (after about 40 min.)

Packed snow on horizontally mounted polymer insulator (after the test).

Fig: 10a

Fig: 11a Fig. 10b: Comparison between cap & pin and long rod insulator.

Fig: 10b

Fig: 11b

2005 was reproduced on horizontally mounted long rod insulators and the mechanism of such a snow pack process was demonstrated. This mechanism – whereby snow grows by rotating along the insulator surface to become cylindrical – is basically the same as with snow accretion on conductors.

vulnerable and I-strings also become vulnerable as they sway due to winds.

c) The shape of packed snow on vertically mounted long rod insulators in this test was eccentric pennant into the wind. While this shape shows some similarity with the packed snow on the polymeric arresters in Niigata, the cylinder like shape seen on many long rods was not reproduced. Test methodology or conditions may therefore have to be improved for any future research.

f) Once snow bridges the sheds and becomes packed, it cannot easily be removed from the insulator surface. The adhesion tensile strength between the snow particles and between the insulator surface and snow particles is strong.

d) Shed profile affects the properties of wet snow accretion. Wider shed diameter and larger shed spacing results in lesser amounts of snow accretion and reduced possibility of bridging sheds. Therefore, cap & pin insulators perform the best and polymeric insulators are the next choice. Porcelain long rod insulators are the most vulnerable to packed snow. Bridging of the sheds can more easily occur on vertical than on horizontally mounted long rod insulators. This suggests that V-strings are most

e) The hydrophobicity of polymeric insulators seems to play little role in snow accretion. Shed profile is more important than shed material.

g) Water inside the packed wet snow tends to move downward and accumulate near the bottom of the insulator, making the LWC at the bottom larger than on other sections or even that of the original snow. While clarifying the flashover mechanism will be left for the future research, water migration may play an important role in this process.

Based on all these findings and the areas identified as requiring further research, another artificial wet snow accretion test having an improved test methodology is planned for the near future. 

(a) After about10 min.

Fig. 12: Comparison of snow between polymeric and long rod insulator.

(b) After test.

Fig. 13: Hydrophobic surface of polymeric insulator (after test).

widESprEad blackOUt triGGErS StUdy Of cOntaminatEd wEt SnOw On inSUlatOr StrinGS

INMR Issue 88 (2).indd 103

Q2 2010 INMR® 103

5/15/10 8:51:20 PM