Technical Data PRODUCT:
MULTILINK速AUTOMIX- Self curing resin based cement with light curing option in 3 Shades- Transparent, Yellow, and Opaque
SHELF LIFE:
24 Months*- Always refer to the expiration date on the package
COMPOSITION: Monomer matrix: dimethacrylate & HEMA. Inorganic fillers are barium glass, ytterbium trifluoride, spheroid mixed oxide.
COMPOSITION: Primer A & Primer B
3 gram bottles - Mixed in 1:1 ratio Primer A -Aqueous solution of initiators, Primer B- HEMA and phosphoric acid and acrylic acid monomers
COMPOSITION: Metal Primer
Metal Primer- 87.9 % Solvent, Phosphonic acid acrylate, and methacrylate cross linking agents in an organic solution.
FILLER: %
39.7% by Volume- Inorganic fillers are barium glass, ytterbium trifluoride, spheroid mixed oxide
SHEAR BOND STRENGTH:
26 MPa to Dentin, 22 MPa to Enamel 28 MPa to Gold with metal primer 36 MPa to Non-precious metal with metal primer
PARTICLE SIZE
Range of particle sizes 0.25-3.0 microns Mean particle size is .9 microns
FILM THICKNESS
<20 microns
WORKING TIME:
180+/- 30 sec. room temperature 120+/- 30 sec.intraoral
CURING TIME (Without working time):
300+/- 30 sec. room temperature 180+/- 30 sec. intraoral
RADIOPACITY:
350 % Al
STORAGE:
Multilink, Primer A & Primer B should be stored in cool storage 36-46 degrees F /2-8 degrees C
FLEXURAL STRENGTH: FLEXURAL MODULUS: COMPRESSIVE STRENGTH SHEAR BOND STRENGTH SHEAR BOND STRENGTH VICKERS HARDNESS
90+/- 10 MPa 5000 +/- 1000 N/mm2 240+/- 20 N/mm2 21+/- 2 N/mm2 to dentin after 24 hours 23 +/- 4 N/mm2 to enamel after 24 hours 370 +/- 30 N/mm2