Flux Cored Wires

ArcStar 81N1M AWS A5.29 E81T1-Ni1M

Characteristics and Applications: ArcStar 81N1M is a gas-shielded flux cored wire for all-position welding. It is designed for welding 590 N/mm2 high tensile steel for low temperatures. It provides good weldability with smooth bead appearance, less spatter and stable arc as well as good impact properties down to -40 . It is also suitable for welding on construction machinery, shipbuilding, offshore, structures, bridges, storage tanks and piping.

Notes on Usage: 1. When the heat input is excessive, the impact value tends to be reduced. Therefore, perform welding with selecting proper heat input depending on the required impact value. 2. Preheating at 50~150 is required depending on steels, plate thickness and restraint. 3. Use DC(+) polarity. 4. Use 75~80%Ar+25~20%CO2 as shielding gas.

Typical chemical composition of weld metal(wt%) C

0.04

1.25

0.28

0.015

0.005

1.0

Typical mechanical properties of weld metal YS (MPa)

TS (MPa)

EL %

560

610

CVN -40

120

Welding position

Sizes and recommended current range (DC＜＜+＞＞) Diameter (mm) Current (A)

F HF

UV OH

1.2

1.6

150-300

200-350

150-220

160-220

1011

ArcStar 101K3 AWS A5.29 E101T1-K3C-J

Characteristics and Applications: ArcStar-101K3 offers excellent arc stability and low spatter with CO2 shielding gas. It also has a fast freezing slag for all-position welding. These features, along with relatively low diffusible hydrogen levels, excellent slag removal, good impact values and high strength levels, make ArcStar-101K3 a superior choice for welding higher-strength steels.

Notes on usage: (1) Use (DC+) polarity. (2) Use 100%CO2, 20~25 l/min shielding gas. (3) Welding heat input must be controlled in order to get required impact value, since notch tough ness tends to decrease due to excessive heat input. (4) Keep dry during handling and storage.

Typical chemical composition of weld metal(wt%): C 0.05

Mn 1.36

Si 0.40

P 0.018

S 0.007

Ni 2.23

Mo 0.39

Typical mechanical properties of weld metal: Yield stress (MPa) 715

Tensile strength (MPa) 760

Charpy V-Notch -40 (J) 55

Elongation (%) 21

Welding position

Sizes and recommended current range (DC＜＜+＞＞) : Stick out: 15-25 (mm), gas flow rate: 20-25 (l/min): Diameter(mm) Parameters F, HF VU, OH VD H

1.2 160A-300A/22V-34V 150A-220A/21V-26V 230A-300A/26V-34V 200A-260A/23V-28V

1105

ArcStar 111K3 AWS A5.29 E111T1-K3C-J

Characteristics and Applications: ArcStar 111K3 offers excellent arc stability and low spatter with CO2 shielding gas. It also has a fast freezing slag for all-position welding. These features, along with relatively low diffusible hydrogen levels, excellent slag removal, good impact values and high strength levels, make ArcStar 111K3 a superior choice for welding quench and tempered low alloy steels, such as ASTM A514, S690QL1 (EN 10025-6) etc.

Notes on usage: (1) Use (DC+) polarity. (2) Use 100%CO2, 20~25 l/min shielding gas. (3) Welding heat input must be controlled in order to get required impact value, since notch toughness tends to decrease due to excessive heat input. (4) Keep dry during handling and storage.

Typical chemical composition of weld metal(wt%) : C 0.04

Mn 1.65

Si 0.40

P 0.019

S 0.002

Ni 2.37

Mo 0.48

Typical mechanical properties of weld metal: Yield stress (MPa) 735

Tensile strength (MPa) 790

Charpy V-Notch -40 (J) 60

Elongation (%) 22

Welding position:

Sizes and recommended current range (DC＜＜+＞＞) : Stick out: 15-20 (mm), gas flow rate: 20-25 (l/min): Diameter(mm) Parameters F, HF VU, OH H

1.2 160A-300A/22V-34V 150A-220A/21V-26V 200A-260A/23V-28V

1105

ArcStar 711

AWS A5.20 E71T- 1C EN758 T 42 2 P C 1 H5 JIS Z3313 T 49J 2 T1-1 C A-U

Characteristics and Applications: ArcStar 711 is a gas-shielded flux cored wire designed for mild steel and 490N/mm2 high tensile steel. It is suitable for all position welding, especially straight up weld ability. It provides stable arc, less spatter, easy slag removable, and excellent X-Ray inspection. The typical applications include shipbuilding, vessels, piping etc.

Notes on usage: (1) Use (DC+) polarity. (2) Use 100%CO2, 20~25 l/min shielding gas. (3) Welding heat input must be controlled in order to get required impact value, since notch toughness tends to decrease due to excessive heat input. (4) Keep dry during handling and storage.

Typical chemical composition of weld metal(wt%): C 0.04

Mn 1.35

Si 0.30

P 0.017

S 0.007

Typical mechanical properties of weld metal: Yield stress (MPa) 530

Tensile strength (MPa) 571

Charpy V-Notch -20 (J) 70

Elongation (%) 30

Welding position:

Sizes and recommended current range (DC＜＜+＞＞): Stick out: 15-25 (mm), gas flow rate: 20-25 (l/min): Diameter (mm) Parameters F, HF VU, OH VD H

1.2 160A-300A/22V-34V 150A-220A/21V-26V 250A-300A/26V-34V 200A-260A/23V-28V

1105

ArcStar 711Ni

AWS A5.20 E71T- 9MJ EN758 T 42 4 P M 1 JIS Z 3313 T 49 4 TH M A

Characteristics and Applications: ArcStar 711Ni is a gas-shielded flux cored wire designed for mild steel and 490N/mm2 high tensile steel. It is suitable for all position welding. It provides stable arc, less spatter, easy slag removable, and excellent X-Ray inspection. It provides good low-temperature impact value due to 0.4%Ni in weld metal. The typical applications include shipbuilding, vessels, piping etc.

Notes on usage: (1) Use (DC+) polarity. (2) Use 80%Ar + 20%CO2, 20~25 l/min shielding gas. (3) Welding heat input must be controlled in order to get required impact value, since notch tough ness tends to decrease due to excessive heat input. (4) Keep dry during handling and storage.

Typical chemical composition of weld metal(wt%): C 0.04

Mn 1.31

Si 0.44

P 0.018

S 0.007

Ni 0.45

Typical mechanical properties of weld metal: Yield stress (MPa)

Tensile strength (MPa)

Elongation (%)

Charpy V-Notch -40 (J)

568

610

Welding position:

Sizes and recommended current range (DC＜＜+＞＞) : Stick out: 15-25 (mm), gas flow rate: 20-25 (l/min): Diameter (mm) Parameters F, HF VU, OH VD H

1.2 160A-300A/22V-34V 150A-220A/21V-25V 250A-300A/26V-34V 200A-260A/23V-28V

1105

ArcStar T9

AWS A5.20 E71T-9CJ EN758 T 46 4 P C 1 H10 JIS Z3313 T49J 4 T1-C1 A

Characteristics and Applications: ArcStar T9 is a gas-shielded flux cored wire designed for mild steel and 490N/mm2 high tensile steel. It is suitable for all position welding. It provides stable arc, less spatter, easy slag removable, excellent X-Ray inspection and good low temperature impact at -40°C. The typical applications include shipbuilding, vessels, offshore, piping etc.

Notes on usage: 1. Use DC(+) polarity. 2. Use CO2 as shielding gas. 3. Maintain interpass temperature under 150°C in multi-pass welding to keep excellent mechanical properties.

Typical chemical composition of weld metal (wt%)：： C 0.05

Mn 1.35

Si 0.51

P 0.015

S 0.005

Typical mechanical properties of weld metal：： Yield stress (MPa) 565

Tensile strength (MPa) 615

Elongation (%) 28

Charpy V-Notch -40 (J) 70

Welding position:

Sizes and recommended current range ( DC＜＜+＞＞): Stick out: 15-25 (mm), gas flow rate: 20-25 (l/min): Diameter (mm) Parameters F, HF, VU, OH, VD, H

1.2mm 140A-300A/22V-34V

1105

FabStar 80G

AWS A5.26 EG80T-G

Characteristics and Applications: FabStar 80G is a self-shielded flux-cored wire used for single pass, vertical up, electrogas welding of shipbuilding, heavy equipment fabrication and structural welding. It is suitable for welding 590N/mm2 high tensile steels with high deposition rate and with or without consumable guide. Diameters 1.6mm and 2.4mm are recommended for 9 to 19mm thick plate, the 3.0mm diameter is recommended for 19mm to 101mm thick plate.

Notes on usage: 1. Use DC(+) polarity. 2. Composition of consumable guide tube should be as close as possible to parent steel and be aware to add an insulating ring to the tube made without insulating coating to prevent from a short circuit. 3. Mechanical properties are dependent on plate chemistry and joint geometry. 4. Pre-heat the workpiece and star-up zone. 5. Baffle plate should be tightened firmly to prevent a leak of deposited metal. 6. Control all parameters with cares during welding, such as shape of weld joint, tube material, cooling rate.

Typical chemical composition of weld metal (wt%): C

0.06

1.60

0.35

0.017

0.006

0.22

Typical mechanical properties of weld metal: Yield stress (MPa)

Tensile strength (MPa)

Elongation (%)

Charpy V-Notch -20 (J)

480

630

Sizes and recommended current range ( DC＜＜+＞＞): Diameter (mm)

3.0

Parameters Thickness Wire Feed Speed (cm/min) Voltage(Volt)

19 510 35-38

25 580 38-40

38 750 42-44

50 890 42-44

1105

FabStar 721

AWS A5.26 EG72T-1

Characteristics and Applications: FabStar 721 is a self-shielded flux-cored wire used for single pass, vertical up, electrogas welding of shipbuilding, heavy equipment fabrication and structural welding. It is suitable for welding of mild steel and high tensile steels with high deposition rate and with or without consumable guide. Diameters 1.6mm and 2.4mm are recommended for 9 to 19mm thick plate, the 3.0mm diameter is recommended for 19mm to 101mm thick plate.

Typical chemical composition of weld metal (wt%): C

0.05

1.50

0.30

0.015

0.007

0.18

Typical mechanical properties of weld metal on A36 base metal: Yield stress (MPa) 470

Tensile strength (MPa) 575

Elongation (%) 25

Charpy V-Notch -30 (J) 50

Sizes and recommended current range ( DC＜＜+＞＞): Diameter (mm) Parameters Thickness Wire Feed Speed (cm/min) Voltage(Volt)

1.6 9 280 30

2.4 12 300 32

12 350 36

3.0 19 400 38

19 510 35-38

25 580 38-40

38 750 42-44

50 890 42-44

1105

RolClad-19-S /TF-R85 Characteristics and Applications: RolClad-19-S/TF-R85 is a submerged arc flux-cored wire / flux which produces low impurities weld deposit (2~3 layers) with a typical hardness of 32RC. It provides good resistance to impact and highly resistance for high temperature softness, as well as resistance of corrosion, cold work deformation. It is suitable for build-up welding on high carbon base metal, such as S45C, S50C, S60C...etc. Crack susceptibility is very low particular in multiplayer that can weld up to 20mm thickness and without micro-fissure. RolCald-19-S can be used for both build-up and hardfacing on rollers and idlers where there is metal-to-metal wear. Typical applications include high carbon steel crane wheels, idlers, mine car wheels and house rollers, etc..

Characteristics (1) It is suit able for welding on high carbon base metal, such as S45C, S50C, S60C...etc. (2) It has good impact resistance and low crack susceptibility. (3) It has good resistance for pitting corrosion.

Notes on usage: 1.RolClad-19-S has good resistance to cross checking and is not restricted with regard to deposit thickness. 2.Applications that are inherently crack sensitive may require one or more of the following: High preheat and interpass temperatures 350-400 . for 1st layer. Controlled slow cooling.

Typical chemical composition (wt%): C

(Cr+Mo+Nb+V)

0.07

2.1

0.6

3.0

Range of weld metal hardness (On Mild Steel): Layer

1st layer

2nd layer

Hardness (HRC)

26-29

29-34

Suggested welding parameter (DC<+>): Diameter (mm) Parameters

3.2

Voltage (Volt)

23-32

Current (Amp)

300-450

Flow rate of shield gas (l/min.)

30-40

1103

SubCor M13K Characteristics and Applications: SubCor M13K is a metal cored wire for submerged arc welding designed for welding 490N/mm2 grade high tensile steel and low temperature steel, the application is similar to solid wire classification EM13K. It provides high deposition rates as compared to the solid wires of equal size, with the same amperage, electrical stick out and flux. Welded with SAW flux that provides smooth bead appearance, high porosity resistance and excellent low temperature impact toughness at -50 . Typical applications include structure steel, bridges, tank fabrication, shipbuilding and offshore fabrication.

Notes on usage: 1. Suitable for welding single and multi-wire processes. 2. To keep the toughness, the plates should not be welded with excessive heat input. 3. When the flux has been affected by moisture pick up; it has to be re dried at a temperature of 300 to 350 for 1 hour.

Typical chemical composition of weld metal (wt%): Wire

A5.17

TF-565

F7A6-EC1

0.05

1.60

0.27

0.025

0.008

Typical mechanical properties of weld metal: Wire

Yield stress (MPa)

Tensile strength (MPa)

Elongation (%)

Charpy V-Notch -50 (J)

TF-565

450

515

Welding position

Sizes and recommended current range ( DC＜＜+＞＞) Diameter (mm) Parameters Voltage(Volt) Current(Amp)

φ2.4 mm

φ3.2 mm

φ4.0 mm

24-29 250-450

26-32 300-600

27-34 350-750

1105

TF-81 An agglomerated flux for SAW Characteristics and Applications: TF-81 is a neutral agglomerated flux for SAW. During welding, it wonâ&#x20AC;&#x2122;t result any significant changes composition of weld bead and thus the arc length by changing arc voltage,. This makes TF-81 very suitable to use with wire for hardfacing applications such as TWH- 12-S, 17-S, 31-S, and TWS-410NiMo-S, 420-S, etc.

Notes on usage: 1.Dry flux at 300~350

for one hour if there is any concern about moisture pick-up while opening the pack.

2.Add reasonable amount of new flux when recycled flux is used.

1103

TFW-308H

AWS A5.22 E308HT1-1 JIS Z 3323 TS308H-FC1

Characteristics and Applications: TFW-308H is special for 100% CO2 gas and all-position welding. The weld bead has very excellent slag release. An 19Cr-9Ni austenitic stainless steel deposited that can be used for joining 18Cr-8Ni austenitic steels such as AISI304. AISI301. 302. SUS304H. It provides good resistance to inter-granular corrosion and has higher tensile strength than TFW-308L. It can also be used as an intermediate layer for hardfacing.

Notes on usage: 1. Before welding, the base material should be cleaned from oil, rusty, moisture and the welding place should have the proper protection from the wind. 2. Use 100% purity or higher CO2 shielding gas. Maintain the flow rate not less than 20L/min when wire diameter is 1.2 or 1.6 mm. 3. Trailer Shield is required to ensure the weld pool completely shielded until solidification is complete and no porosity problem. 4. Keep dry while in storage and delivery.

Typical chemical composition of weld metal (wt%): C

0.05

1.64

0.50

0.028

0.009

20.37

9.54

0.10

Typical mechanical properties of weld metal: Tensile strength (MPa)

Elongation (%)

586(60)

Welding position:

Sizes and recommended current range (DC＜＜+＞＞): Stick out:15-20(mm),flow rate:20-25(l/mm): Diameter (mm) Parameters F, H V-UP, OH

1.2

1.6

140A-220A/23V-33V 120A-220A/24V-30V

200A-300A/27V-32V --

1105

TFW-308L

AWS A5.22 E308LT1-1 EN 12073 T 19 9 L P C 1 JIS Z 3323 TS308L-FC1

Characteristics and Applications: TFW-308L is designed for 100% CO2 gas shielding and all-position welding. It exhibits very excellent slag detachability. And almost spatter-free operating features can be used for joining of austenitic steels such as Types 304, 304L, 321, CF-8, and CF-3. It also provides better inter-granular corrosion resistance due to a low carbon weld deposit.

Notes on usage: 1. Before welding, the base material should be cleaned from oil, rusty, moisture and the welding place should have the proper protection from the wind. 2. Use 99.8% purity or higher CO2 shielding gas. Maintain the flow rate not less than 20L/min when wire diameter is 1.2 mm. 3. Trailer Shield is required to ensure the weld pool completely shielded until solidification is complete and no porosity problem. 4. Keep dry while in storage and delivery.

Typical chemical composition of weld metal (wt%): C

0.029

0.56

0.025

0.008

0.06

1.63

9.93

19.50

0.08

Typical mechanical properties of weld metal: Tensile strength (MPa) 565

Elongation (%) 40

Welding position:

Sizes and recommended current range (DC＜＜+＞＞): Stick out:15-20(mm),flow rate:20-25(l/mm): Diameter (mm) Parameters F, HF H V-UP OH

1.2 130A-220A/24V-33V 140A-180A/25V-29V 130A-160A/24V-28V 150A-180A/25V-29V

1105

TFW-308LP

AWS A5.22 E308LT1-4 EN 12073 T 19 9 L P M 1

Characteristics and Applications: TFW-308LP is designed for all position welding by gas shield of mix gas (75 80% Argon and 25 20% CO2). It has very excellent slag-removal property. An austenitic stainless steel deposit that can be used for joining common austenitic steels such as Types 304,304L, 321, CF-8, and CF-3. It provides good resistance to intergranular corrosion.

Typical chemical composition of weld metal (wt%): C 0.028

Mn 1.71

Si 0.57

P 0.022

S 0.009

Cr 19.10

Ni 10.10

Mo 0.05

Typical mechanical properties of weld metal: Tensile strength (MPa) 555

Yield stress (MPa) 390

Elongation (%) 42

Welding position:

Sizes and recommended current range (DC＜＜+＞＞): Stick out:15-20(mm),flow rate:20-25(l/mm): Diameter (mm) Parameters F, HF H V-UP V-down OH

1.2 130A-220A/24V-33V 140A-180A/25V-29V 130A-180A/24V-29V 150A-180A/25V-29V 150A-180A/25V-29V

1105

TFW-308LT

AWS A5.22 E308LT0-4 EN ISO 17633-A T 19 9 L R M 3 JIS Z 3323 TS308L-FM0

Characteristics and Applications: TFW-308LT is designed for Flat position welding by gas shield of mix gas (75 80% Argon and 25 20% CO2). It has very excellent slag-removal property. An austenitic stainless steel deposit that can be used for joining common austenitic steels such as Types 304,304L, 321, CF-8, and CF-3. It provides good resistance to intergranular corrosion.

Typical chemical composition of weld metal (wt%): C

0.028

1.90

0.45

0.024

0.008

0.09

9.20

19.75

0.10

Typical mechanical properties of weld metal: Tensile strength (MPa) 560

Yield stress (MPa) 385

Elongation (%) 40

Welding position:

Sizes and recommended current range (DC＜＜+＞＞): Diameter (mm) Parameters F, HF

1.2 130A-220A/24V-33V

1103

TFW-309L

AWS A5.22 E309LT1-1 EN 12073 T 23 12 L P C 1 JIS Z 3323 TS309L-FC1

Characteristics and Applications: TFW-309L is designed for 100% CO2 gas shielding and all position welding. It is commonly used for welding similar alloys in wrought or cast forms, or used in dissimilar welding, such as low alloy steel, heat-resistant steel and clad steel.

Notes on usage: 1. Before welding, the base material should be cleaned from oil, rusty, moisture and the welding place should have the proper protection from the wind. 2. Use 99.8% purity or higher CO2 shielding gas. Maintain the flow rate not less than 20L/min when wire diameter is 1.2 or 1.6 mm. 3. Trailer Shield is required to ensure the weld pool completely shielded until solidification is complete and no porosity problem. 4. Keep dry while in storage and delivery.

Typical chemical composition of weld metal (wt%): C

0.026

1.51

0.55

0.024

0.009

0.06

24.07

0.07

12.78

Typical mechanical properties of weld metal: Tensile strength (MPa)

Elongation (%)

586

Welding position:

Sizes and recommended current range ( DC＜＜+＞＞): Stick out:15-20(mm),flow rate:20-25(l/mm): Diameter (mm) Parameters F, HF H V-UP OH

1.2 130A-220A/24V-33V 140A-180A/25V-29V 130A-160A/24V-28V 150A-180A/25V-29V

1103

TFW-309LMo

AWS A5.22 E309LMoT1-1 EN 12073 T 23 12 2 L P C 2

Characteristics and Applications: TFW-309LMo is a modified type of TFW-309L with the addition of molybdenum. It is suitable for joining stainless steels to unalloyed steels. The addition of molybdenum enhances creep strength and improves corrosion resistance.

Notes on usage: 1. Before welding, the base material should be cleaned from oil, rusty, moisture and the welding place should have the proper protection from the wind. 2. Use 99.8% or higher purity CO2 as shielding gas. Maintain the flow rate no under than 20L/min when wire diameter is 1.2 or 1.6mm. 3. Trailer Shield is required to ensure the weld pool completely shielded until solidification is complete and no porosity problem.

Typical chemical composition of weld metal (wt%): C

0.025

1.50

0.57

0.023

0.010

22.93

12.70

2.35

Typical mechanical properties of weld metal: Tensile strength (MPa)

Elongation (%)

685

Welding position:

Sizes and recommended current range ( DC＜＜+＞＞): Stick out:15-20(mm),flow rate:20-25(l/mm): Diameter (mm) Parameters F, HF H V-UP OH

1.2 130A-220A/24V-33V 140A-180A/25V-29V 130A-160A/24V-28V 150A-180A/25V-29V

1105

TFW-309LMoP

AWS A5.22 E309LMoT1-4 JIS Z 3323 TS309LMo-FB1 EN 12073 T 23 12 2 L P C/M 1

Characteristics and Applications: TFW-309LMoP is a modified type of TFW-309L with the addition of molybdenum. It is suitable for joining stainless steels to unalloyed steels. The addition of molybdenum enhances creep strength and improves corrosion resistance.

Notes on Usage: 1. Before welding, the base material should be cleaned from oil, rusty moisture and the welding place should have the proper protection from the wind. 2. Use 99.8% or higher purity CO2 as shielding gas. Maintain the flow rate no under than 20L/min when wire diameter is 1.2 or 1.6mm. 3. Trailer Shield is required to ensure the weld pool completely shielded until solidification is complete and no porosity problem.

Typical chemical composition of weld metal (wt%) C

0.025

1.61

0.68

0.023

0.009

22.85

12.43

2.38

Typical mechanical properties of weld metal Yield stress (MPa)

Tensile strength (MPa)

Elongation (%)

540

690

Welding position

Size and recommended current range (DC＜＜+＞＞) Stick out: 18-25 (mm) Diameter (mm) Parameters F, HF H V-UP V-down OH

1.2 130A-220A/24V-33V 140A-180A/25V-29V 130A-180A/24V-29V 150A-180A/25V-29V 150A-180A/25V-29V

1010

TFW-309LNb

AWS A5.22 E309LCbT0-1,4

Characteristics and Applications: TFW-309LNb, a 100% CO2 or mix gas (75~80%Ar+25~20%CO2) gas shielded flux cored wire, is specially designed for one layer of overlay to achieve the chemical composition of SUS 347. The wire operates with a very stable, less-spatter arc and deposits an excellent smooth weld bead surface and self-releasing slag.

Notes on usage: 1.Before welding need clean the base material from oil, rusty, moisture and the welding place should have the proper protection from the wind. 2.Use both 100% CO2 gas and mix gas (75~80%Ar+25~20%CO2).

Typical chemical composition of weld metal (wt%) (Base metal: A387 Gr.22): Condition All weld metal 2mm from the surface

0.027

1.9

0.5

0.025

0.007

23.5

12.7

0.77

0.040

1.32

0.4

0.022

0.009

19.0

9.95

0.58

Typical mechanical properties of weld metal: Tensile strength (MPa)

Elongation (%)

678

Welding position:

Sizes and recommended current range ( DC＜＜+＞＞): Stick out:15-20(mm),flow rate:20-25(l/mm): Diameter (mm) Parameters F, HF

1.2

1.6

140A-220A/23V-33V

200A-300A/27V-32V

1105

TFW-309LP

AWS A5.22 E309LT1-4 EN 12073 T 23 12 L P M 1

Characteristics and Applications:

TFW-309LP is designed for all position welding by gas shield of mix gas (75 80% Argon and 25 20% CO2). The weld metal of TFW-309LP contains 24 Cr and 13 Ni. It is commonly used for welding similar alloys in wrought or cast forms, also used in welding dissimilar metals, such as joining Type 304 to mild steel. It can also be used as an intermediate layer for hard facing.

Typical chemical composition of weld metal (wt%): C 0.025

Mn 1.58

Si 0.58

P 0.022

S 0.008

Cr 24.02

Ni 12.48

Mo 0.05

Typical mechanical properties of weld metal: Tensile strength (MPa) 565

Yield stress (MPa) 420

Elongation (%) 37

Welding position:

Sizes and recommended current range ( DC＜＜+＞＞): Stick out:15-20(mm),flow rate:20-25(l/mm): Diameter (mm) Parameters F, HF H V-UP V-down OH

1.2 130A-220A/24V-33V 140A-180A/25V-29V 130A-180A/24V-29V 150A-180A/25V-29V 150A-180A/25V-29V

1105

TFW-309LT

AWS A5.22 E309LT0-4 EN ISO 17633-A T 23 12L R M 3 JIS Z 3323 TS309L-FM0

Characteristics and Applications:

TFW-309LT is designed for Flat position welding by gas shield of mix gas (75 80% Argon and 25 20% CO2). The weld metal of TFW-309L contains 24 Cr and 13 Ni. It is commonly used for welding similar alloys in wrought or cast forms, also used in welding dissimilar metals, such as joining Type 304 to mild steel.

Typical chemical composition of weld metal (wt%): C

0.026

1.75

0.62

0.022

0.009

0.11

24.07

0.11

13.00

Typical mechanical properties of weld metal: Tensile strength (MPa) 580

Yield stress (MPa) 423

Elongation (%) 34

Welding position:

Sizes and recommended current range ( DC＜＜+＞＞): Diameter (mm) Parameters F, HF

1.2 130A-220A/24V-33V

1103

TFW-310

AWS A5.22 E310T1-4

Characteristics and Applications: TFW-310 is designed for all position welding by gas shield of mix gas (75 80% Argon and 25 20% CO2). It has very excellent slag-removal property. It is suitable for the welding of dissimilar metals, low-temperature service stainless steel and Cr-Mo steel and applicable for AISI 310S. Proper base metals are including stainless steel plate, steel strip, steel tube, seamless pipe, heat transfer tube, pressure vessel, and steel bar.

Typical chemical composition of weld metal (wt%): C 0.09

Mn 1.90

Si 0.27

P 0.022

S 0.011

Cr 25.54

Ni 20.9

Mo 0.33

Typical mechanical properties of weld metal: Tensile strength (MPa) 590

Elongation (%) 38

Welding position:

Welding condition:

Welding Current DC+ Amp 200 300

Welding condition

Wire diameter 1.6mm Shielding gas mixed gases (75 80% Argon and 25 20% CO2) 20-30mm Stick out Packaging 12.5kgs D300 Spool

Welding Voltage Volt 27 32 20 l/min

1103

TFW-316L

AWS A5.22 E316LT1-1 JIS Z 3323 TS316L-FC1

Characteristics and Applications: TFW-316L is designed for 100% CO2 gas shielding and all-position welding. It exhibits very excellent slag release and almost spatter-free operating features. It can be used for joining types of 316,316L, CF-8M, and CF-3M stainless steels. It provides high inter-granular corrosion resistance to pressure vessel application due to the low carbon content.

Typical chemical composition of weld metal (wt%): C

0.027

0.69

0.025

0.010

2.68

1.55

12.63

19.03

0.08

Typical mechanical properties of weld metal: Tensile strength (MPa)

Elongation (%)

560(57)

Welding position:

Size and recommended current range (DC＜＜+＞＞) Stick out:15-20(mm),flow rate:20-25(l/mm): Diameter (mm) Parameters F, HF H V-UP OH

1.2 130A-220A/24V-33V 140A-180A/25V-29V 130A-160A/24V-28V 150A-180A/25V-29V

1105

TFW-316LP

AWS A5.22 E316LT1-4 EN 12073 T 19 12 3 L P M 1 JIS Z 3323 TS316L-FB1

Characteristics and Applications: TFW-316LP is designed for all position welding by gas shield of mix gas (75 80% Argon and 25 20% CO2). An austenitic stainless steel deposit that can be used for joining Types 316,316L,CF-8M, and CF-3M stainless steels. It provides high resistance to inter-granular corrosion with low carbon weld deposit.

Typical chemical composition of weld metal (wt%): C 0.026

Mn 1.70

Si 0.68

P 0.023

S 0.010

Cr 18.95

Ni 12.52

Mo 2.70

Typical mechanical properties of weld metal: Tensile strength (MPa) 552

Yield stress (MPa) 370

Elongation (%) 41

Welding position:

Size and recommended current range (DC＜＜+＞＞) Stick out:15-20(mm),flow rate:20-25(l/mm): Diameter (mm) Parameters F, HF H V-UP V-down OH

1.2 130A-220A/24V-33V 140A-180A/25V-29V 130A-180A/24V-29V 150A-180A/25V-29V 150A-180A/25V-29V

1105

TFW-316LT

AWS A5.22 E316LT0-4 EN ISO 17633-A T 19 12 3 L R M 3 JIS Z 3323 TS316L-FM0

Characteristics and Applications: TFW-316LT is designed for flat position welding by gas shield of mix gas (75~80% Argon and 25~20% CO2 ) An austenitic stainless steel deposited that can be used for joining Types 316,316L stainless steels. It provides high resistance to intergranular corrosion with low carbon weld deposit.

Typical chemical composition of weld metal (wt%): C

0.027

1.74

0.55

0.025

0.010

2.79

12.5

19.3

0.16

Typical mechanical properties of weld metal: Tensile strength (MPa) 553

Yield stress (MPa) 394

Elongation (%) 32

Welding position:

Size and recommended current range (DC＜＜+＞＞): Stick out: 18-25 (mm) Diameter (mm) Parameters F, HF

1.2 130A-220A/24V-33V

1103-2

TFW-317L

AWS A5.22 E317LT1-1 JIS Z 3323 TS317L-FC1

Characteristics and Applications: TFW-317L is designed for 100% CO2 gas shielding and all-position welding wire. It is used for joining types of stainless steels such as 317, 317L, 316, 316L, 316LN, CF-8M and CF-3M. The weld metal exhibits excellent performance of pitting inter-granular corrosion resistance. Common applications include offshore fabrication, chemical tankers as well as petro-chemical, pulp and paper industries.

Notes on usage: 1. Clean up the contaminations on the base metal. 2. Use 99.8% or higher purity CO2 as shielding gas. Maintain the flow rate not under than 20L/min while wire diameter is 1.2 or 1.6mm. 3. Trailer Shield is required to ensure the weld pool completely shielded until solidification is complete and no porosity problem.

Typical chemical composition of weld metal (wt%): C

0.03

1.42

0.71

0.028

0.009

12.81

19.20

3.35

Typical mechanical properties of weld metal: Tensile strength (MPa)

Elongation (%)

620

Welding position:

Sizes and recommended current range (DC＜＜+＞＞): Stick out:15-20(mm),flow rate:20-25(l/mm): Diameter (mm) Parameters F, H V-UP, OH

1.2

1.6

140A-220A/23V-33V 120A-200A/24V-30V

130A-220A/27V-35V --

1105

TFW-347LT

AWS A5.22 E347T0-1

Characteristics and Applications: TFW-347LT is designed for Flat position welding by gas shield of 100% CO2. It has very excellent slag-remove property. It is commonly used for cladding welding, such as joining ASTM A387 Gr.22.

Notes on usage: 1.Before welding, the base material should be cleaned from oil, rusty, moisture and it should have the proper protection from the wind in welding site. 2.Use with 100% CO2.

Typical chemical composition of weld metal (wt%): C 0.023

Mn 1.40

Si 0.50

P 0.026

S 0.009

Cr 18.91

Ni 10.60

Mo 0.08

Nb 0.68

Cu 0.10

Typical mechanical properties of weld metal: Yield stress (MPa)

Tensile strength (MPa)

Elongation (%)

550

372 FN WRC1992 6.0

Welding position:

Sizes and recommended current range (DC＜＜+＞＞): Stick out: 18-25 (mm) Diameter (mm) Parameters F, HF

1.2

1.6

130A-220A/24V-33V

200A-300A/27V-32V

1103

TFW-347L

AWS A5.22 E347T1-1 EN 12073 T 19 9 Nb P C 2 JIS Z 3323 TS347-FC1

Characteristics and Applications: TFW-347L is designed for 100% CO2 gas shielding and all-position welding wire. It exhibits very excellent slag detachability and almost spatter-free operating features. It is used for joining stabilized stainless steels such as Types 321 and 347. It is also suitable for joining nonstabilized austenitic stainless steels such as Types 301, 302, 304, and CF-8.

Notes on usage: 1. Before welding, the base material should be cleaned from oil, rusty, moisture and the welding place should have the proper protection from the wind. 2. Use 99.8% or higher purity CO2 as shielding gas. Maintain the flow rate no under than 20L/min when wire diameter is 1.2 or 1.6mm. 3. Trailer Shield is required to ensure the weld pool completely shielded until solidification is complete and no porosity problem. 4. Keep dry while in delivery and storage.

Typical chemical composition of weld metal (wt%): C

0.03

1.48

0.54

0.029

0.009

19.56

10.50

0.10

0.54

Typical mechanical properties of weld metal: Tensile strength (MPa)

Elongation (%)

627

Welding position:

Sizes and recommended current range (DC＜＜+＞＞): Stick out:15-20(mm),flow rate:20-25(l/mm): Diameter (mm) Parameters F, HF V-UP, OH

1.2

1.6

140A-220A/23V-33V 120A-200A/24V-30V

200A-300A/27V-32V -

1105

TFW-347LP

AWS A5.22 E347LT1-4 EN ISO 17633-A T 19 9 Nb P M 1 JIS Z 3323 TS347L-FC1

Characteristics and Applications: TFW-347LP is designed for all position welding by gas shield of mix gas (75 80% Argon and 25 20% CO2). It exhibits well slag detachability, arc stability and almost spatter-free operating features. It’s suitable for joining stabilized stainless steels such as Types 321 and 347. And it also can be used for joining nonstabilized austenitic stainless steels such as Types 301, 302, 304, and CF-8.

Notes on usage: 1.Before welding, the base material should be cleaned from oil, rusty, moisture and it should have the proper protection from the wind in welding site. 2.Use with mix gas (75 80% Argon and 25 20% CO2 ). Maintain the flow rate no under than 20L/min. 3.Trailer Shield is required to ensure the weld pool completely shielded until solidification is complete and no porosity problem.

Typical chemical composition of weld metal (wt%): C

0.028

1.45

0.61

0.025

0.009

19.00

10.21

0.06

0.60

Typical mechanical properties of weld metal: Tensile strength (MPa) 580

Yield stress (MPa) 438

Elongation (%) 41

Welding position:

Size and recommended current range (DC＜＜+＞＞) Stick out:15-20(mm),flow rate:20-25(l/mm): Diameter (mm) Parameters F, HF H V-UP V-down OH

1.2 130A-220A/24V-33V 140A-180A/25V-29V 130A-180A/24V-29V 150A-180A/25V-29V 150A-180A/25V-29V

1105

TFW-347LT

AWS A5.22 E347LT0-4 EN ISO 17633-A T 19 9 Nb R M 3

Characteristics and Applications: TFW-347LT is designed for flat and horizontal position welding by gas shield of mix gas (75 80% Argon and 25 20% CO2). It has excellent slag detachability. Itâ&#x20AC;&#x2122;s suitable for welding the Nb stabilized stainless steel types 347 and 321.

Typical chemical composition of weld metal (wt%): C 0.026

Cr 18.55

Ni 10.40

Mo 0.07

Mn 1.79

Si 0.73

P 0.030

S 0.01

Cu 0.13

Nb 0.67

Typical mechanical properties of weld metal: TS MPa 400

YS MPa 570

Welding position:

Welding condition: Welding condition Welding Current DC+ Amp Welding Voltage Volt 130 220 24 33

Welding position Flat, Horizontal Fillet Wire diameter 1.2mm mix gas (75 80% Argon and 25 20% CO2) Shield gas 18-25mm Stick out Packaging 12.5kgs D300 Spool

20â&#x201E;&#x201C;/min

1101

TFW-410

AWS A5.22 E410T1-1

Characteristics and Applications: TFW-410 is an air-hardening steel, so it requires preheat and postheat treatments in order to achieve welds of adequate ductility. It is suitable for joint welding by 13Cr steel SUS410, 405 .And it can be used the cladding welding by preventing Cavitation and Erosion.

Notes on usage: (1) The preheat and interpass temperature keep at 200~400 730~760 for 1 hour. (2) Use 100% CO2 as shielding gas.

. After welding, the PWHT condition is

Typical chemical composition (wt%): C

0.069

12.90

0.15

0.02

0.32

0.40

0.019

0.005

0.01

Typical mechanical properties of weld metal: Tensile strength (MPa)

Elongation (%)

PWHT

545

750 1hr

Welding position:

Sizes and recommended current range (DC＜＜+＞＞): Diameter (mm) Parameters F, HF H V-UP OH

1.2 130A-220A/24V-33V 140A-180A/25V-29V 130A-160A/24V-28V 150A-180A/25V-29V

1101

TFW-410NiMo

AWS A5.22 E410NiMoT1-1 EN 12073 T 13 4 P C 2 JIS Z 3323 TS410NiMo-FC1

Characteristics and Applications: TFW-410NiMo is a gas-shielded flux-cored wire with better control of hydrogen levels and excellent impact toughness at 0 . It is generally used for welding of ASTM CA6NM castings, materials, with similar composition, and turbines of hydro plant.

Notes on usage: 1. Use 99.8% or higher purity of CO2 as shielding gas. 2 Pre-heat and inter-pass temperature 150 ~260 , and post weld heat treatment.

Typical chemical composition (wt%): C

0.040

0.5

0.015

0.008

0.5

0.45

4.50

11.30

0.01

Typical mechanical properties of weld metal: Tensile strength (MPa)

Elongation (%)

875

PWHT 610 x 1hr

Welding position:

Sizes and recommended current range (DC＜＜+＞＞): Stick out:15-20(mm),flow rate:20-25(l/mm): Diameter (mm) Parameters F, HF H V-UP OH

1.2 130A-220A/24V-33V 140A-180A/25V-29V 130A-160A/24V-28V 150A-180A/25V-29V

1105

TFW-410NiMoM

AWS A5.22 E410NiMoT0-4 JIS Z 3323 TS410NiMo-MM0 EN 12073 T 13 4 M M 3

Characteristics and Applications: TFW-410NiMoM is a gas-shielded metal-cored wire with better control of hydrogen levels and excellent impact toughness at 0 . It is generally used for welding of ASTM CA6NM castings, materials, with similar composition, and turbines of hydro plant.

Notes on usage: 1. Before welding, the base material should be cleaned from oil, rusty, moisture and it should have the proper protection from the wind in welding site. 2. Use with mix gas (75 80% Argon and 25 20% CO2 ). 3. Pre-heat and inter-pass temperature 150 ~260 , and post weld heat treatment.

Typical chemical composition (wt%): C 0.031

Cr 11.70

Ni 4.50

Mo 0.50

Mn 0.45

Si 0.29

P 0.009

S 0.008

Cu 0.01

Typical mechanical properties of weld metal: Yield stress (MPa)

Tensile strength (MPa)

Elongation (%)

PWHT

742

860

610 1hr

Welding position:

Sizes and recommended current range (DC＜＜+＞＞): Stick out:15-20(mm),flow rate:20-25(l/mm): Diameter (mm) Parameters F, HF

1.2 130A-220A/24V-33V

1105

TFW-2209

AWS A5.22 E2209T1-1 EN 12073 T 22 9 3NL P C 2 JIS Z 3323 TS2209-FC1

Characteristics and Applications: TFW-2209 is a flux-cored wire that is applicable for the welding of duplex stainless steel such as UNS S31803 (Alloy 2205). Excellent pitting corrosion resistance, stress corrosion resistance and crack resistance can be obtained. It is suitable for the weldings of heat exchanger, chemical equipments and pipes.

Notes on usage: 1. 100% CO2 shielding gas with 99.8% purity is recommended and the flow rate should be kept over 20L/min for the wire diameter is 1.2 and 1.6mm. 2. Clean the surface of base metal completely to prevent the contamination. 3. Trailer Shield is required to ensure the weld pool completely shielded until solidification is complete and no porosity problem. 4. The welding place should have the proper protection from wind to prevent generating the welding defects due to improper gas shielding.

Typical Chemical Composition of Weld Metal (wt%): C 0.029

Mn 0.85

Si 0.68

P 0.025

S 0.009

Cr 22.57

Ni 8.36

Mo 3.2

Cu 0.08

N 0.16

Typical Mechanical Properties of Weld Metal: Tensile strength (MPa) 786

Elongation (%) 26

Welding position:

Sizes and recommended current range (DC＜＜+＞＞): Stick out:15-20(mm),flow rate:20-25(l/mm): Diameter (mm) Parameters F, HF H V-UP OH

1.2 130A-220A/24V-33V 140A-180A/25V-29V 130A-160A/24V-28V 150A-180A/25V-29V

1105

TFW-2209P

AWS A5.22 E2209T1-4 EN 12073 T 22 9 3 N L P M 1

Characteristics and Applications: TFW-2209P is applicable to weld duplex stainless steel such as UNS S31803 (Alloy 2205). Excellent pitting corrosion resistance, stress corrosion resistance and crack resistance can be obtained. It is suitable for welding of heat exchanger, chemical equipments and pipes.

Typical chemical composition of weld metal (wt%): C 0.027

Mn 0.90

Si 0.5

P 0.023

S 0.007

Cr 23.05

Ni 8.60

Mo 3.2

N 0.16

Typical mechanical properties of weld metal: Yield stress (MPa)

Tensile strength (MPa)

Elongation (%)

Charpy V-Notch -46°C (J)

610

780

Welding position:

Sizes and recommended current range (DC＜＜+＞＞): Stick out:15-20(mm),flow rate:20-25(l/mm): Diameter (mm) Parameters F, HF H V-UP V-down OH

1.2 130A-220A/24V-33V 140A-180A/25V-29V 130A-180A/24V-29V 150A-180A/25V-29V 150A-180A/25V-29V

1105

TGFA-308L AWS A5.22 R308LT1-5 /JIS Z 3323 TS308L-R1 TGFA-316L AWS A5.22 R316LT1-5 / JIS Z 3323 TS316L-R1 TGFA-309L AWS A5.22 R309LT1-5 / JIS Z 3323 TS309L-R1 TGFA-347 AWS A5.22 R347T1-5 / JIS Z 3323 TS347-R1

TGFA-308H/TGFA-308L/ TGFA-316L/TGFA-309L/ TGFA-317L/ TGFA-347/ Characteristics and Applications:

TGFA series is a flux cored wire of stainless steel for TIG welding used on first layer for butt joint. Good bead soundness without back shielding can be obtained.

Notes on usage: 1. 100%Ar shielding gas is recommended. 2. In order to have beautiful back bead appearance, the key hole formation during welding is necessary. The proper key hole size is recommended. 3. High pitch and little by little feeding of a filler rod is a must in order to melt it adequately. 4. Keep away from moisture during storage and transportation.

Typical Chemical Composition of Weld Metal (wt%)：： Product Name TGFA-308H TGFA-308L TGFA-316L TGFA-309L TGFA-317L TGFA-347

C 0.059 0.02 0.027 0.022 0.024 0.024

Si 0.61 0.4 0.52 0.35 0.5 0.5

Mn 1.42 1.40 1.35 1.45 1.20 1.53

P 0.022 0.022 0.023 0.024 0.023 0.024

S 0.009 0.008 0.007 0.009 0.007 0.006

Reference Welding Conditions:

Groove Preparation

Ni 10.52 10.30 12.50 13.50 12.70 10.22

Cr 20.51 20.20 18.56 23.26 18.50 20.00

Mo 2.30 3.36 -

Nb 0.63

Root Face 1~3mm

Plate Thickness Root Gap

Package: Diameter & Length (mm) 2.2 x 915

Sizes and Recommended Current Range：： Plate Thickness mm

Root Gap mm

Current A

Power DCSP

2~4 5~9 >10

2.0 2.5 3.0

80~90 90~105 90~110

DC+

1105

TM-70

AWS A5.18 E70C-3M/6M EN758 T 42 0 M M 3 JIS Z 3313 T49 0T15-0 M A

Characteristics and Applications: TM-70 is a metallic flux cored wire designed to be used with Ar/CO2 for mild steel and 490N/mm2 high tensile steel, its deposition rate is 10-30% higher than a solid wire. Multi-layer welding can be performed without removing slag. It is suitable for the multi-layer welding of thick plate welding in such applications as: steel structure, bridges, shipbuilding, vehicles, storage tanks, etc.

Notes on usage: 1. Use DC(+) polarity. 2. When larger diameters (1.6mm or higher) are used, higher power supply of welder is recommended. 3. Trailer Shield is required to ensure the weld pool completely shielded by 75~80%Ar-25~20% CO2 gas until solidification is complete and no porosity problem. 4. Inter-pass temperature should be under 150 while in multiple-pass welding. 5. Keep dry while in storage and delivery.

Typical chemical composition of weld metal (wt%): C

0.04

1.50

0.63

0.012

0.010

Typical mechanical properties of weld metal: Yield stress (MPa)

Tensile strength (MPa)

Elongation (%)

545

595

Charpy V-Notch (J) -20째C -30째C 57 45

Welding position:

Sizes and recommended current range ( DC+) Stick out: 15-25 (mm), flow rate: 20-25 (l/min) Diameter (mm) Parameters F, H

1.2mm

1.6mm

200A-320A/28V-36V

250A-350A/28V-36V

1105

TM-70C

AWS A5.20 E70T-1C EN758 T 42 2 P C 3 JIS Z 3313 T49J 0T15-0 CA-U

Characteristics and Applications: TM-70C is a high deposition rate flux cored wire suitable for high speed fillet welding application in flat and horizontal position. The wire has excellent porosity resistibility for use in welding over zinc-primer surface and mill scale in high speed fillet welding. The wire generates low spatter and produces thinner slag with good slag detachability. In addition it produces deep effective throat on fillet weld and it has good arc stability and welder appeal. TM-70C is widely used in shipbuilding, bridge construction and structural fabrication.

Notes on usage:

1. Proper pre-heating 50~150 (120~300 ) and inter-pass temperature must be used in order to release hydrogen which may cause cracking in weld metal when welding on medium and heavy plates. 2. Use DC(+) polarity and 100% CO2 shielding gas. 3. Maintain the temperature of inter-pass under 150 when in multiple-pass welding. 4. Keep dry while in storage and delivery.

Typical chemical composition of weld metal (wt%): C

0.05

1.55

0.60

0.017

0.007

Typical mechanical properties of weld metal: Yield stress (MPa)

Tensile strength (MPa)

Elongation (%)

550

595

Charpy V-Notch (J) -20°C 90

-30°C 70

Welding position:

Sizes and recommended current range ( DC＜＜+＞＞): Stick out: 15-25 (mm), flow rate: 20-25 (l/min) Diameter (mm)

1.2mm

1.4mm

1.6mm

F H

160A-300A / 24V-36V

200A-350A / 26V~34V

270A-400A / 28V-40V

1105

TM-77

AWS A5.18 E70C-6M EN 758 T 46 4 M M 3 H5 JIS Z 3313 T49 4 T15-0 M A-U

Characteristics and Applications: TM-77 is a gas-shielded metal-cored wire that provides smooth spray arc, low slag volume, low spatter, low fume emission and excellent low temperature impact toughness under -40°C. It welds with a wider penetration profile and higher deposition efficiency than solid wire. Multi-layer welding can be performed without removing slag. It is suitable for steel structures, storage vessels and multi-layer welding on heavy plate thickness.

Notes on usage: 1. Ar-CO2 mixture. 75%~80%Ar 25%~20%CO2.

Typical chemical composition of weld metal (wt%): C 0.06

Mn 1.45

Si 0.54

P 0.015

S 0.005

Typical mechanical properties of weld metal: Yield stress (MPa)

Tensile strength (MPa)

Elongation (%)

Charpy V-Notch -40°C (J)

580

630

Welding position:

Sizes and recommended current range ( DC＜＜+＞＞): Stick out: 15-25 (mm)，，flow rate: 20-25 (l/min) Diameter (mm) Parameters F, H

1.2mm

1.6mm

200A-320A/26V-34V

250A-350A/ 28V-35V

1105

Characteristics and Applications: TWE-81K2 is a titania type flux-cored wire, it is designed for welding 560 N/mm2 high tensile steel for low temperatures. The weld metal contains about 1.5%Ni and makes good notch toughness at temperatures down to -60 under as-welded condition. It provides excellent usability with stable arc and efficiency in all-position welding. It is suitable for butt or fillet welding of offshore structures for low-temperature districts, LNG and LPG carriers, and storage tanks, etc.

Notes on usage: 1. When the heat input is excessive, the impact value tends to be reduced. Therefore, perform welding with selecting proper heat input depending on the required impact value. 2. Use DC(+) polarity. 3. Use 99.8% or higher purity of CO2 gas.

Typical chemical composition of weld metal (wt%): C

0.04

0.45

1.35

0.016

0.008

1.60

Typical mechanical properties of weld metal : Yield stress (MPa)

Tensile strength (MPa)

Elongation (%)

580 640 27 * CTOD Value -10 , 0.3328, 0.3250 & 1.3197 mm at WMC

Charpy V-Notch -60 (J) 50

Welding position:

1105

TWE-81W2

AWS A5.29 E81T1-W2C

Characteristics and Applications: TWE-81W2 is a titania type flux-cored wire and suitable for butt or fillet MAG welding of 590N/mm2 weather-proof grade steel and A588 A234 A242 A333 or COR-TEN 60 (used normally without painting) at low temperatures. It can be applicable for all-position welding and show smooth bead appearance and shape, spattering.

Notes on usage:

1. Pre-heat is required and inter-pass temperature should be controlled around 50 ~150 . 2. To keep the toughness, the plates should not be welded with excessive heat input. 3. Use DC(+) polarity and CO2 gas. 4. Keep dry during storage and delivery.

Typical chemical composition of weld metal (wt%): C

0.03

0.57

1.15

0.015

0.007

0.60

0.65

0.45

Typical mechanical properties of weld metal: Yield stress (MPa)

Tensile strength (MPa)

Elongation (%)

Charpy V-Notch -30 (J)

550

620

Welding position:

Sizes and recommended current range (DC＜＜+＞＞): Stick out:15-25(mm), gas flow rate:20-25(l/mm): Diameter(mm) F H V OH

1.2 180-300A / 26V-36V

1.6 200-350A / 26V-40V

150-220A / 24V-28V

160-220A / 24V-28V

1105

TWE-704-O

AWS A5.20 E70T-4 EN758 T 42 Z W N 3

Characteristics and Applications: TWE-704-O is a self-shielded flux-cored wire, it is designed for on site general fabrication and structural work requiring, good slag release and friendly to manage variant weld joints by sticking out the wire longer. Excellent performance in desulfuration reduces porosity effectively. The welding for heavy machinery, large construction components is appropriate, also stiffens in large building. It is suitable for flat, horizontal and downhill positions, also it can be applied to build up the worn parts.

Notes on usage: 1. DC(+) polarity is recommended. 2. When impact toughness of weld metal is required, TM-70C or TWE-711 would be recommended. 3. Keep dry while in storage and delivery.

Typical chemical composition of weld metal (wt%): C 0.28

Mn 0.45

Si 0.30

P 0.015

S 0.006

Al 1.50

Typical mechanical properties of weld metal: Yield stress (MPa)

Tensile strength (MPa)

Elongation (%)

445

570

Welding position:

Sizes and recommended current range (DC＜＜+＞＞) : Stick out: 40-60 (mm) Diameter (mm) Parameters F, HF

2.4mm

2.8mm

250A-400A/26V-34V

280A-450A/27V-36V

1105

TWE-707-O

AWS A5.20 E70T-7 EN758 T 42 Z W N3

Characteristics and Applications: TWE-707-O is a self-shielded flux cored wire designed for high deposition welding. It is suitable for flat, horizontal and downhill positions on DCEN polarity. Excellent performance on X-ray inspection, and desulfuration reduces cracking in welding thick plates, constrained joints and medium-carbon steel. The typical applications of TWE-707-O are general fabrication and structural weldment where high deposition with good penetration and / or fast travel speed is needed. Available positions are flat weld, horizontal weld and vertical down ones of welding for fillet weld and lap joint.

Notes on usage: 1. DC(-) polarity is recommended. 2. When impact toughness of weld metal is required, TM-70C or TWE-711 would be recommended.

Typical chemical composition of weld metal (wt%): C 0.28

Mn 0.45

Si 0.15

P 0.016

S 0.005

Al 1.50

Typical mechanical properties of weld metal: Yield stress (MPa) 450

Tensile strength (MPa) 630

Elongation (%) 26

Welding position:

Sizes and recommended current range ( DC＜＜-＞＞): Stick out: 40-60 (mm) Diameter (mm) Parameters F, HF, VU, VD

2.4mm

2.8mm

250A-400A/26V-34V

280A-450A/28V-38V

1105

TWE-711

AWS A5.20 E71T-1C EN758 T 46 2 P C 1 H10 JIS Z 3313 T49J 0 T1-1C A-U

Characteristics and applications: TWE-711 is a flux-cored wire designed to be used with CO2 gas and it’s available for all-position welding with both single and multiple pass welds on mild and 490N/mm2 high tensile steels. It provides good impact properties, less fume, stable arc, good slag release and excellent X-Ray inspection. Typical applications include shipbuilding, storage vessels, structural fabrication, machinery and piping etc.

Notes on usage: 1. Use DC(+) polarity. 2. Use CO2 (more than 99.8% purity) as shielding gas and flow rate should be around 20~25 l/min. 3. Keep dry during delivery and storage.

Typical chemical composition of all weld metal (wt%)：： C 0.05

Mn 1.45

Si 0.55

P 0.015

S 0.008

Typical mechanical properties of all weld metal：： Yield stress (MPa) 530

Tensile strength (MPa) 580

Elongation (%) 29

Charpy V-Notch -20 (J) 100

Welding position:

Sizes and recommended current range ( DC＜＜+＞＞) : Stick out:15-25(mm), flow rate:20-25(l/mm): Diameter (mm) Parameters F HF H VU, OH VD

1.2mm

1.4mm

1.6mm

140A~300A / 23V~36V 140A~300A / 22V~36V 140A~280A / 22V~33V 140A~220A / 22V~28V 230A~280A / 28V~33V

150A~350A / 22V~34V 150A~350A / 22V~34V 150A~280A / 22V~32V 150A~230A / 22V~28V 250A~300A / 28V~32V

200A~400A / 24V~42V 200A~400A / 24V~42V 200A~280A / 24V~30V 160A~230A / 22V~28V 250A~320A / 28V~32V

1105

TWE-711M

AWS A5.20 E71T-1M/ E71T-9M EN758 T 46 2 P M 1 H10 JIS Z 3313 T49J 0 T15-0 C M-U

Characteristics and Applications: TWE-711M is a flux-cored wire designed to be used with Ar/ CO2 gas. It’s available for all-position welding with both single and multiple pass welds on mild and 490N/mm2 high tensile steels. It provides good impact properties, less fume, stable arc, easy slag removable and excellent X-Ray inspection. Typical applications include shipbuilding, storage vessels, structural fabrication, machinery and piping etc.

Notes on usage: 1. Use DC(+) polarity. 2. Use 75~85%Ar+25~15%CO2 as shielding gas. 3. Keep dry during handling and storage.

Typical chemical composition of weld metal (wt%)：： C 0.05

Mn 1.25

Si 0.45

P 0.015

S 0.007

Typical mechanical properties of weld metal：： Yield stress (MPa) 540

Tensile strength (MPa) 590

Elongation (%) 28

Charpy V-Notch -20 (J) 95

Welding position:

Sizes and recommended current range ( DC＜＜+＞＞): Stick out: 15-25 (mm), flow rate: 20-25 (l/min) Diameter (mm) Parameters F, HF, H, VU,OH, VD

1.2mm 140A-320A/22V-35V

1105

TWE-711Ni

AWS A5.20 E71T- 1CJ /E71T-9CJ EN758 T 42 4 P C 1

Characteristics and Applications: TWE-711Ni is a gas-shielded flux cored wire designed for mild steel and 490N/mm2 high tensile steel. It is suitable for all position welding. It provides stable arc, less spatter, easy slag removable, and excellent X-Ray inspection. It provides good low-temperature impact value due to 0.4%Ni in weld metal. The typical applications include shipbuilding, vessels, piping etc.

Notes on usage: (1) Use (DC+) polarity. (2) Use CO2 as shielding gas. (3) Welding Heat Input must be controlled in order to get required impact value, since notch toughness tends to decrease due to excessive heat input. (4) Keep dry during handling and storage.

Typical chemical composition of weld metal(wt%): C 0.05

Mn 1.35

Si 0.43

P 0.018

S 0.009

Ni 0.45

Typical mechanical properties of weld metal: Yield stress Tensile strength (MPa) (MPa) 515 575 * CTOD Value 0 , 1.0060, 1.2282 & 0.4545 mm at WMC

Elongation (%) 29

Charpy V-Notch -40 (J) 80

Welding position:

Sizes and recommended current range (DC＜＜+＞＞) : Stick out: 15-25 (mm), flow rate: 20-25 (l/min): Diameter (mm) Parameters F, HF VU, OH VD H

1.2

1.6

160-280 150-220 230-280 200-260

180-300 160-230 250-300 220-280

1105

TWE-715

AWS A5.20 E71T-5C/5M EN758 T 46 3 P C/M1

Characteristics and Applications: TWE-715 is an all-position flux-cored wire designed to be used with CO2 or Ar/ CO2 gas mixture for 490N/mm2 grade high tensile steel. Its low temperature impact toughness is better than E71T-1(AWS A5.20). The typical applications of TWE-715 are constructional steel, machinery and shipbuilding.

Notes on usage: 1. DC(+) polarity is recommended. 2. Use CO2 as shielding gas. 3. Keep inter-pass temperature under 150

whiling in multiple-pass welding.

Typical chemical composition of weld metal (wt%)：： C 0.05

Mn 1.45

Si 0.50

P 0.015

S 0.007

Typical mechanical properties of weld metal：： Yield stress (MPa) 510

Tensile strength (MPa) 570

Elongation (%) 29

Charpy V-Notch -30 (J) 65

Welding position:

Sizes and recommended current range ( DC＜＜+＞＞):

Stick out:15-25(mm),flow rate:20-25(l/mm): Diameter (mm) Parameters F, HF, H, VU,OH, VD

1.2mm

1.6mm

130A-300A/24V-36V

160A-340A/24V-38V

1103

TWE-715M

AWS A5.20 E71T-5M EN758 T 42 3 P M1

Characteristics and Applications: TWE-715M is an all-position flux-cored wire designed to be used with Ar/ CO2 gas mixture for 490N/mm2 grade high tensile steel. Its low temperature impact toughness is better than E71T-1M(AWS A5.20). The typical applications of TWE-715M are constructional steel, machinery and shipbuilding.

Notes on usage: 1. DC(+) polarity is recommended. 2. Use 75~85%Ar+25~15%CO2 as shielding gas. 3. Keep inter-pass temperature under 150 whiling in multiple-pass welding.

Typical chemical composition of weld metal (wt%)：： C 0.04

Mn 1.35

Si 0.42

P 0.015

S 0.007

Typical mechanical properties of weld metal：： Yield stress (MPa) 540

Tensile strength (MPa) 590

Elongation (%) 28

Charpy V-Notch -30 (J) 75

Welding position:

Sizes and recommended current range ( DC＜＜+＞＞): Stick out:15-25(mm), gas flow rate:20-25(l/mm): Diameter (mm) Parameters F, HF, VU,OH, VD, H

1.2mm 140A-300A/22V-33V

1103

TWE-811B2

AWS A5.29 E81T1-B2C

Characteristics and Applications: TWE-811B2 is a gas-shielded and all-position flux-corded wire intended for 1~1.25%Cr-0.5%Mo low alloy steel welding. It is used with 100%CO2 shielding gas and offers good operator appeal. TWE-811B2 is ideal for welding of Cr-Mo steel pipe and Cr-Mo steel requiring high creep resistance.

Notes on usage: 1. 2. 3. 4.

Pre-heat at 150-300 , and PWHT at 620 x1hr. Keep dry during storage and delivery. Use 99.8% or higher purity of CO2 Gas. Use DC(+) polarity.

Typical chemical composition of weld metal(wt%): C

0.06

0.85

0.42

0.014

0.008

1.17

0.55

Typical mechanical properties of weld metal: Yield stress (MPa)

Tensile strength (MPa)

Elongation (%)

560

640

PWHT 690 x1hr

Welding position:

Sizes and recommended current range (DC＜＜+＞＞) : Stick out:15-25(mm), gas flow rate:20-25(l/mm): Diameter(mm) F HF VU OH

1.2

1.6

180A-300A/26V-36V

180A-350A/26V-38V

150A-220A/24V-28V

160A-230A/24V-28V

1105

TWE-811Ni1

AWS A5.29 E81T1-Ni1C

Characteristics and Applications: TWE-811Ni1 is a titania type flux-cored wire for all-position MAG welding. It is designed for welding 590 N/mm2 high tensile steel for low temperatures. It provides good weldability with smooth bead appearance, less spatter and stable arc as well as good impact properties down to -30 . It is also suitable for welding on construction machinery, shipbuilding, offshore, structures, bridges, storage tanks and piping.

Notes on usage: 1. When the heat input is excessive, the impact value tends to be reduced. Therefore, perform welding with selecting proper heat input depending on the required impact value. 2. Preheating at 50~150 is required depending on steels, plate thickness and restraint. 3. Use DC(+) polarity. 4. Use 99.8% or higher purity of CO2 Gas.

Typical chemical composition of weld metal(wt%): C

0.05

1.25

0.55

0.018

0.006

1.00

0.18

Typical mechanical properties of weld metal: Yield stress (MPa)

Tensile strength (MPa)

Elongation (%)

Charpy V-Notch -30 (J)

Condition

590

640

110

510

600

PWHT (590 x 8hr)

Welding position:

Sizes and recommended current range (DC＜＜+＞＞) : Stick out:15-25(mm), flow rate:20-25(l/mm): Diameter(mm) F HF VU OH

1.2 180-300A / 26V-36V

1.6 180-350A / 24V-38V

150-220A / 24V-28V

160-230A / 24V-28V

1105

TWE-811Ni2

AWS A5.29 E81T1-Ni2C EN 758 T 46 4 2Ni P C1 H10

Characteristics and Applications: TWE-811Ni2 is a titania type flux-cored wire for all-position MAG welding. It provides good weldability with smooth bead appearance, less spatter and stable arc as well as good impact properties down to -40 . It is suitable for welding of 590 N/mm2 high tensile strength steel on construction machinery, structures, bridges, storage tanks and piping.

Notes on usage: 1. Pre-heating at 50~150 is required depending on steels, plate thickness and restraint. 2. Mechanical properties tend to be reduced when heat input is over 35J/cm. Therefore, perform welding with lower welding current and heat input. 3. Maintain inter-pass temperature under 150 in multi-pass welding to keep excellent mechanical properties. Use 99.8% or higher purity of CO2 Gas. 4. Use DC(+) polarity. 5. Keep dry during storage and delivery.

Typical chemical composition of weld metal(wt%) : C

0.05

1.10

0.40

0.016

0.008

2.55

Typical mechanical properties of weld metal: Yield stress (MPa)

Tensile strength (MPa)

Elongation (%)

Charpy V-Notch -40 (J)

540

630

Welding position:

Sizes and recommended current range (DC＜＜+＞＞): Stick out:15-25(mm), flow rate:20-25(l/mm): Diameter(mm) F HF VU OH

1.2 120-300A / 26V-36V

1.6 200-400A / 24V-38V

120-240A / 24V-28V

170-270A / 24V-28V

1105

TWE-911B3

AWS A5.29 E91T1-B3C

Characteristics and Applications: TWE-911B3 is a gas-shielded and all-position flux-corded wire intended for 2.25%Cr-1%Mo low alloy steel welding. It is used with 100%CO2 shielding gas and offers good operator appeal. TWE-911B3 is ideal for welding of Cr-Mo steel pipe and Cr-Mo steel requiring high creep resistance.

Notes on usage: 1.Preheat at 200-350 , and PWHT at 620 2. Use DC(+) polarity. 3. Use 99.8% or higher purity of CO2 Gas. 4. Keep dry during storage and delivery.

x1hr.

Typical chemical composition of weld metal(wt%): C

0.06

0.78

0.45

0.016

0.011

2.27

1.10

Typical mechanical properties of weld metal: Yield stress (MPa)

Tensile strength (MPa)

Elongation (%)

645

730

PWHT 690 x1hr

Welding position:

Sizes and recommended current range (DC＜＜+＞＞) : Stick out:15-25(mm), gas flow rate:20-25(l/mm): Diameter(mm) F HF VU OH

1.2 180-300A / 26V-36V

1.6 180-350A / 26V-38V

150-220A / 24V-28V

160-230A / 24V-28V

1105

TWE-911Ni2

AWS A5.29 E91T1-Ni2C

Characteristics and Applications: TWE-911Ni2 is a titania type flux-cored wire for all-position welding. It provides good weldability with smooth bead appearance, less spatter and stable arc as well as good impact properties down to -40 . It is suitable for welding of 2-3%Ni steel and 620 N/mm2 HT steel on storage tanks, structures, bridges, construction machinery, shipbuilding and piping.

Notes on usage: 1. Use DC(+) polarity and 100% CO2 shielding gas. 2. When the heat input is excessive, the impact value tends to be reduced. Therefore, perform welding with selecting proper heat input depending on the required impact value.

Typical chemical composition of weld metal(wt%) : C

0.06

1.25

0.45

0.015

0.007

2.60

0.18

Typical mechanical properties of weld metal: Yield stress (MPa)

Tensile strength (MPa)

Elongation (%)

Charpy V-Notch -40 (J)

650

710

Welding position:

Sizes and recommended current range (DC＜＜+＞＞): Stick out:15-25(mm), flow rate:20-25(l/mm): Diameter(mm) F HF VU OH

1.2 180-300A / 26V-36V

1.6 200-350A / 26V-38V

150-220A / 24V-28V

160-220A / 24V-28V

1105

TWH-12-S /TF-81 Characteristics and Applications: TWH-12-S is a submerged arc flux-cored wire to provide a modified H12 tool steel deposit which retains hardness at high temperatures. TWH-12-S flux-cored wire is used with TF-81, a neutral flux, for submerged arc welding applications. The combination is suitable for work rolls, pinch rolls and surfaces subjected to sliding metal/metal wear.

Notes on usage: 1. The DC(+) polarity is recommended. 2. The workpiece should be free of moisture to prevent porosity and enhance the interfacial bonding between parent steel and weld metal. 3. The pre-heat and inter-pass temperatures for massive workpieces, heavy cylinders and highly stressed workpieces should be kept between 204-316 to prevent weld crack.

Typical chemical composition (wt%): C

0.27

1.8

0.6

5.9

1.3

0.3

1.5

Typical weld metal hardness (on mild steel) : Hardness (HRC)

Suggested welding parameter DC(+): Diameter (mm) Parameters Volt Amps Stickout(mm)

3.2 25-32 300-450 30-40

1103

TWH-17-S /TF-81 Characteristics and Applications: TWH-17-S/TF-81 is a submerged arc flux-cored wire / flux which produces a low carbon, low alloy weld deposit with a typical hardness of 37RC. It provides good resistance to compression and cold work deformation. The impact resistance is excellent and the crack susceptibility is low. After welding, the deposit could be flame cut or machined. TWH-17-S can be used for both build-up and hardfacing on rollers and idlers where there is metal-to-metal wear. Typical applications include carbon steel crane wheels, idlers, mine car wheels and house rollers, etc..

Notes on usage: 1.TWH-17-S has good resistance to cross checking and is not restricted with regard to deposit thickness.

2.Applications that are inherently crack sensitive may require one or more of the following: High prheat and interpass temperatures 204-260 .

Controlled slow cooling. Stress relieving at 480

Minimize layer thickness.

Typical chemical composition (wt%): C

0.07

2.6

0.6

2.7

0.7

Range of weld metal hardness (On Mild Steel): Layer

1st layer

2nd layer

3rd layer

Hardness (HRC)

26-30

30-35

34-38

Suggested welding parameter (DC<+>): Diameter (mm) Parameters Volt Amps Stickout(mm)

3.2 25-32 300-450 30-40

1103

TWH-31-S /TF-81 Characteristics and Applications: TWH-31-S is a flux-cored wire used for submerged arc welding, it produces a low carbon, low alloy pearlitic structure in the deposited metal. After welding, the deposit can easily be machined because hardness is about HRC 31. It is primarily used for build-up on carbon and low alloy steel components. It is suitable for build-up of continuous casting rolls, steel mill rolls, shafts, idlers, journals or workpieces that machinability is required.

Notes on usage: 1.The DC(+) polarity is recommended. 2.The preheat and interpass temperatures between 200-250 should be kept for massive workpieces, heavy cylinders, and highly stressed workpieces to prevent weld crack.

Typical chemical composition (wt%): C

0.14

2.7

0.5

0.6

Range of weld metal hardness (On Mild Steel): Layer

1st layer

2nd layer

3rd layer

Hardness (HRC)

18-24

24-27

29-32

Suggested welding parameter (DC<+>): Diameter (mm) Parameters Volt Amps Stickout(mm)

3.2 25-32 300-450 30-40

1103

TWH-34-O Characteristics and Applications: TWH-34-O is a self-shielded flux-cored wire for build-up or hardfacing on worn workpieces. The hardness of the deposited metal is about HRC 34 which can be machined by carbide tools. It is desdigned for hardfacing or build-up or repair of tractor roll, shaft, mine car wheel, gear and workpieces which medium hardness is required.

Notes on usage: 1.The DC(+) polarity is recommended. 2.The pre-heat and inter-pass temperatures between 150-250 should be kept for massive workpieces. 3. Dry the workpiece in advance to prevent from porosity caused by remnant moisture.

Typical chemical composition of weld metal (wt%): C

0.16

2.0

0.5

1.2

Range of weld metal hardness (On Mild Steel): Layer

1st layer

2nd layer

3rd layer

Hardness (HRC)

23-29

27-32

30-34

Suggested welding parameter (DC<+>): Diameter (mm) Parameters Volt Amps Stickout (mm)

2.4

2.8

25-32 250-400 50-60

25-32 300-450 50-60

1103

TWH-41-O Characteristics and Applications: TWH-41-O is a self-shielded flux-cored wire for build-up or hardfacing on worn workpieces. Its deposit is medium hardness and it is suitable for metal to metal abrasion. The applications are including hardfacing of tractor rollers, shaft, mine car wheel, gear and workpiece where medium hardness is required.

Notes on usage: 1. The DC(+) polarity is recommended. 2. Workpiece should be dried in advance to prevent from porosity caused by remnant moisture. 3. The required pre-heat and inter-pass temperatures between 150-250 should be kept for massive workpieces, heavy cylinders, highly stressed workpieces and high carbon steels.

Typical chemical composition of weld metal (wt%): C

0.31

2.2

0.60

1.4

0.4

Range of weld metal hardness (On Mild Steel): Layer

1st layer

2nd layer

3rd layer

Hardness (HRC)

29-35

34-41

39-43

Suggested welding parameter DC(+) : Diameter (mm)

2.4

2.8

Volt

28-29

Amps

280-340

350-400

Stickout (mm)

50-60

Parameters

1103

TWH-52-S X TF-81 Characteristics and Applications: TWH-52-S is a submerged arc flux-cored wire welded with TF-81 neutral flux. Its deposit contains Cr, Ni, Mo, V elements which provide resistance to extreme abrasive wear and hardness even at high temperature. It is suitable for pinch rolls, work rolls and surfaces subjected to sliding metal/metal wear.

Notes on usage: 1. The DC(+) polarity is recommended. 2. The workpiece should be free of moisture to prevent porosity and enhance the interfacial bonding between parent steel and weld metal, also slow cool-down and PWHT is require to prevent from cracks. 3. The pre-heat and inter-pass temperatures for massive workpieces, heavy cylinders and highly stressed to prevent weld crack. workpieces should be kept between 204-316 4. TF-565/TSW-EM12K is recommended as a buffer layer and followed with TWH-31-S/TF-81 as root-pass when the base metal has a poor weldability.

Typical chemical composition (wt%): C

0.19

2.0

0.6

4.2

2.0

0.5

3.0

Typical weld metal hardness (on mild steel): Hardness (HRC)

45-48

Suggested welding parameter (DC<+>): Diameter (mm) Parameters Voltage (Volt) Current (Amp) Stick out (mm)

3.2 25-32 300-450 30-40

1103

TWH-58-G Characteristics and Applications: TWH-58-G is a flux-cored wire for CO2 welding with the properties of stable arc, smooth bead appearance and low sensitivity of blow-hole. It is able to obtain the weld metal with good wear resistance under wide range of welding parameter owing to its high hardness of weld metal and low penetration. It is suitable for hardfacing of bulldozer blade, bucket lip, tipper teeth, the parts of impeller subjected to severe soil abrasion.

Notes on usage: and slowly cooled to room

1.The required pre-heat and inter-pass temperature should be kept over 300 temperature after welding.

Typical chemical composition (wt%): C

0.41

2.5

0.6

7.5

0.5

Typical weld metal hardness (on mild steel): Layer

5th layer

Hardness (HRC)

57-59

Suggested welding parameter (DC<+>): Diameter (mm)

1.2mm

1.6mm

Voltage (Volt)

25-34

Current (Amp)

150-280

200-350

Parameters

Flow rate of shield gas (l/min.)

CO2,15-25

1103

TWH-61Nb-G Characteristics and Applications: TWH-61Nb-G is a metal-cored wire for CO2 welding with the welding properties of stable arc and little slag. With deposit efficiency of 93%, the weld metal contains carbide forming elements such as Cr, Nb. it offers excellent resistance to severe abrasion wear. It is suitable for hardfacing of hopper liner for steel mill, roll crusher for crushing raw cement material, roll mill for crushing coal and table liner.

Notes on usage: 1. For hardfacing the high carbon steel or the low-alloy steel, the welding consumables of the austenite stainless steel could be welded as buffer layer. 2. “Don’t weld too many layers” is recommended to avoid crack. In need of welding many layers, the bead of rib or waffle pattern should be applied.

Typical chemical composition (wt%): C 4.7

Si 1.6

Mn 0.6

Cr 22.2

Nb 3.0

Typical weld metal hardness (on mild steel): Layer

5th layer

Hardness (HRC)

60-62

Suggested welding parameter DC(+): Diameter (mm)

1.2

1.6

2.0

Voltage (Volt)

25-34

23-34

Current (Amp)

150-280

200-350

300-450

Parameters

Flow rate of shield gas (l/min.)

CO2,15-25

1103

TWH-61P-O Characteristics and Applications: TWH-61P-O is a self-shielded flux-cored wire that deposits a primary carbide surfacing alloy with excellent wear resistance and high hardness. The hardness of weld metal can be easily over HRC 60 and can be used on components subjected to severe abrasion with low or moderate impact. It is suitable for the reclamations of coal pulverizer, bucket, dipper teeth and other parts subjected to severe wear.

Notes on usage: 1. The DC(+) polarity is recommended. 2. Preheat above 200 for the base metal is cast iron, low alloy steel and medium carbon steel. 3. The weld metal can not be machined by flame cutting except grinding with sand wheel.

Typical chemical composition of weld metal (wt%): C

5.4

0.2

1.3

28.5

Range of all-weld-metal hardness (On Mild Steel): Testing Condition Self-shield

Rockwellâ&#x20AC;&#x2122;s Hardness (HRC) 1st layer

2nd layer

50-56

55-61

Suggested welding parameter( DC<+>): Diameter (mm) Parameters

2.8

Volt

28-35

Amps

400-650

Stick out (mm)

50-60

1103

TWH-62-G Characteristics and Applications: TWH-62-G is a flux-cored wire for CO2 welding with the properties of stable arc, smooth bead appearance and low sensitivity of blow-hole. It is able to obtain the weld metal with good resistance to wear under wide range of welding parameter owing to its high hardness of weld metal and low penetration. It is suitable for hardfacing of bulldozer blade, bucket lip, tipper teeth, the parts of impeller subjected to severe soil abrasion.

Notes on usage: 1.The pre-heat and inter-pass temperature should be kept over 300 temperature after welding.

and should be slowly cooled to room

Typical chemical composition (wt%): C

0.70

0.7

1.1

8.0

0.4

Typical weld metal hardness (on mild steel): Layer

5th layer

Hardness (HRC)

61-64

Suggested welding parameter DC(+): Diameter (mm)

1.2

1.6

Voltage (Volt)

25-34

Current (Amp)

150-280

200-350

Parameters

Flow rate of shield gas (l/min.)

CO2,15-25

1103

TWH-63B-G Characteristics and Applications: TWH-63B-G is a metal-cored wire for CO2 welding with the properties of stable arc and little slag. With deposit efficiency of 93%, the weld metal contains carbide forming elements such as Cr., B. it offers excellent resistance to severe abrasion wear. It is suitable for hardfacing of hopper liner for steel mill, roll crusher for crushing raw cement material, roll mill for crushing coal and table liner.

Notes on usage: 1. For hardfacing the high carbon steel or the low alloy steel, the welding consumables of the austenite stainless steel could be welded as buffer layer. 2. “Don’t weld too many layers” is recommended to avoid crack. In need of welding many layers, the bead of rib or waffle pattern should be applied.

Typical chemical composition (wt%): C

3.5

1.2

0.6

27.9

0.4

Typical weld metal hardness (on mild steel): Layer Hardness (HRC)

5th layer 62-64

Suggested welding parameter DC(+): Diameter (mm)

1.6mm

2.0mm

Voltage (Volt)

25-35

23-35

Current (Amp)

200-400

300-500

Parameters

Flow rate of shield gas (l/min.)

CO2,15-25

1103

TWH-65-O Characteristics and Applications: TWH-65-O is a self-shielded flux cored wire to produce weld metal which is resistant to extreme abrasive wear even at high temperature. The deposits can not be flame cut, heat-treated, machined or forged. It is used for blast furnace bell, sugar cane industry, bucket teeth and coke oven screen etc.

Notes on usage: 1.The recommended deposit is two layers.

Typical chemical composition of weld metal (wt%): C

5.1

0.6

0.9

22.5

5.0

1.2

5.5

1.1

Range of weld metal hardness (HRC): Room temp.

63-65

600

50-52

Suggested welding parameter (DC<+>) : Diameter (mm)

2.8

3.2

Volt

25-32

28-36

Amps

300-450

300-650

Stickout (mm)

50-60

50-70

Parameters

1103

TWH-65W-G Characteristics and Applications: TWH-65W-G is a metal-cored wire for CO2 welding with the properties of stable arc and little slag. With deposit efficiency of 93%, the weld metal contains carbide forming elements such as Cr, Nb, Mo, W, V which offers excellent resistance to severe abrasion wear. It is designed for hardfacing of hopper liner for steel mill, roll crusher for crushing raw cement material, roll mill for crushing coal and table liner.

Notes on usage: 1. For hardfacing the high-carbon steel or the low-alloy steel, the welding consumables of the austenitic stainless steel could be welded as buffer layer. 2. “Don’t weld too many layers” is recommended to avoid crack. In need of welding many layers, the bead of rib or waffle pattern should be applied.

Typical chemical composition (wt%): C

5.2

1.9

0.5

21.5

3.7

0.6

0.5

3.0

Typical weld metal hardness (on mild steel): Layer

5th layer

Hardness (HRC)

65-69

Suggested welding parameter (DC<+>): Diameter (mm)

1.2

1.6

2.0

Voltage (Volt)

25-34

23-34

Current (Amp)

150-280

200-350

300-450

Parameters

Flow rate of shield gas (l/min.)

CO2,15-25

1103

TWH-67-O Characteristics and Applications: TWH-67-O is a self-shielded flux-cored wire developing a ledeburitic structure with a great amount of embedded Chromium Carbides and super-hard Metalborides. The alloy is specifically designed for extreme abrasive wear at high temperatures. The deposits canâ&#x20AC;&#x2122;t be flame out, heat-treated, machined or forged except grinding. It is used for blast furnace bell, sugar cane industry, bucket teeth and coke oven screen etc.

Notes on usage: 1. For hardfacing the high-carbon steel or the low-alloy steel, the welding consumables of the austenite stainless steel could be welded as buffer layer. 2. Too many layers might cause crack. In need of welding many layers, the bead of rib or waffle pattern should be applied.

Typical chemical composition (wt%): C

5.1

0.5

0.8

1.5

Typical weld metal hardness (on mild steel): Hardness (HRC)

63-67

Suggested welding parameter (DC<+>): Diameter (mm)

2.8

3.2

Voltage (Volt)

26-32

28-36

Current (Amp)

250-450

300-650

Stickout (mm)

50-60

Parameters

1103

TWH-68NM-G Characteristics and Applications: TWH-68NM-G is a metal-cored wire for CO2 welding with the properties of stable arc and little slag. With deposit efficiency around 93%, the weld metal contains carbide forming elements such as Cr, Mo, Nb and offers excellent resistance to severe abrasion wear. It is suitable for hardfacing of hopper liner for steel mill, roll crusher for crushing raw cement material, roll mill for crushing coal and table liner.

Notes on usage: 1. For hardfacing high-carbon steel or low-alloy steel, the welding consumables of the austenite stainless steel could be welded as buffer layer. 2. “Don’t weld too many layers” is recommended to avoid crack. In need of welding many layers, the bead of rib or waffle pattern should be applied.

Typical chemical composition (wt%): C

6.5

2.2

0.3

23.2

1.8

3.5

Typical weld metal hardness (on mild steel): Layer

5th Layer 67

Hardness (HRC)

Suggested welding parameter (DC<+>): Diameter (mm) 1.6

2.0

Voltage (Volt)

25-34

23-34

Current (Amp)

200-350

300-450

Parameters

Flow rate of shield gas (l/min.)

CO2,15-25

1103

TWS-420Mo-G Characteristics and Applications: TWS-420Mo-G is a flux-cored wire for CO2 welding, which weld metal contains 13%Cr-1%Mo. It is suitable for application of resistance to soil abrasion and corrosion wear such as hardfacing of shovel, press model, the parts of bulldozer, valve seat, agitator propeller, turbine fan, conveyer screw.

Notes on usage: 1.The pre-heat and inter-pass temperature should be kept over 200 temperature after welding.

and slowly cooled to room

Typical chemical composition (wt%): C 0.22

Si 0.4

Mn 0.4

Cr 12.7

Mo 0.8

Typical weld metal hardness (on mild steel): Layer

5th Layer

Hardness (HRC)

49-53

Suggested welding parameter (DC<+>): Diameter (mm) Parameters Voltage (Volt) Current (Amp) Flow rate of shield gas (l/min.)

1.2

1.6

25-34 150-280

25-34 200-350 CO2,15-25

1103

TWS-420-S /TF-81 Characteristics and Applications: TWS-420-S is a submerged arc flux-cored wire that matches with TF-81 neutral flux to produce the weld metal of AISI 420 martensitic stainless steel. It offers excellent resistance to fire cracking, corrosion and unlimited deposition thickness. It is used for workpieces such as continuous casting rolls and steel mill rolls for high temperature service.

Notes on usage: 1. When the carbon content of the carbon steel workpiece is over 0.8 wt% or that of low alloy steel workpiece is over 0.35wt%, a buffer layer using mild steel filler metal (root-pass welding by TWH-31-S or TWH-34-O with around 300~400 pre-heat treatment) is helpful for further hardfacing. 2. The pre-heat and inter-pass temperatures between 200-420 should be kept for massive workpieces, heavy cylinders and highly stressed workpieces to prevent weld cracking.

Typical chemical composition (wt%): C

0.21

1.3

0.6

13.7

Typical hardness of weld metal (on mild steel): Hardness (HRC)

46-51

Suggested welding parameter (DC<+>): Diameter (mm) Parameters Volt Amps Stickout(mm)

3.2 25-32 300-450 30-40

1103